HRB600 high-strength hot-rolling ribbed reinforcing bars with added ferro-silicon nitride and manufacturing method thereof

A technology of hot-rolling ribbed steel bars and adding ferrosilicon nitride, which is applied in the field of steel manufacturing, can solve the problems of high cost and large usage, and achieve a simple production process, a lot of cost savings, and a finer and more uniform grain size Effect

Inactive Publication Date: 2019-10-08
WUHAN IRON & STEEL GRP ECHENG IRON & STEEL CO LTD
View PDF8 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the invention is to propose a HRB600 high-strength hot-rolled ribbed steel bar with ferrosilicon nitride added and a manufacturing method thereof, so as to solve the problems of large usage and high cost of the existing high-strength hot-rolled ribbed steel bar vanadium-nitrogen alloy, The specification of th

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • HRB600 high-strength hot-rolling ribbed reinforcing bars with added ferro-silicon nitride and manufacturing method thereof
  • HRB600 high-strength hot-rolling ribbed reinforcing bars with added ferro-silicon nitride and manufacturing method thereof
  • HRB600 high-strength hot-rolling ribbed reinforcing bars with added ferro-silicon nitride and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] It should be noted that, as used herein, the term "comprises", "comprises" or any other variation thereof is intended to cover a non-exclusive inclusion such that a process, method, article or system comprising a set of elements includes not only those elements, It also includes other elements not expressly listed, or elements inherent in the process, method, article, or system. Without further limitations, an element defined by the phrase "comprising a..." does not preclude the presence of additional identical elements in the process, method, article or system comprising that element.

[0032] The serial numbers of the following embodiments of the present invention are only for description, and do not represent the advantages and disadvantages of the embodiments.

[0033]In this document, the use of the words first, second, and third etc. does not indicate any order. These words can be interpreted as names.

[0034] It should be understood that the specific embodimen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an HRB600 high-strength hot-rolling ribbed reinforcing bars with added ferro-silicon nitride and a manufacturing method thereof. Components of the reinforcing bars comprise C,Si, Mn, P, S, Nb, V and the balance of Fe and impurities; the contents of the component elements simultaneously meet the condition that the carbon equivalent Ceq equaling to C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15 is less than or equal to 0.58 percent. The manufacturing method comprises the following steps: performing treatment on the added ferro-silicon nitride on an argon station and performing alloying,wherein the added ferro-silicon nitride is more easily bonded with N in steel because the affinity of V and N is greater than the affinity of V and C, so that VN is formed; and after the ferro-siliconnitride is added, a large quantity of V is separated out, so that VN and VC alloys are formed, and thus, precipitation and strengthening effects of the V and a crystal grain thinning effect are improved. According to the hot-rolling ribbed reinforcing bars provided by the invention, the ferro-silicon nitride is added in molten steel, and the VN alloy is replaced by a part of the ferro-silicon nitride, so that the use of the VN (Vanadium-Nitrogen) alloy is reduced, the cost is reduced a lot, the production processes are simple, and batch production is easily realized.

Description

technical field [0001] The invention relates to the technical field of steel manufacture, in particular to a HRB600 high-strength hot-rolled ribbed steel bar added with ferrosilicon nitride and a manufacturing method thereof. Background technique [0002] Hot-rolled ribbed steel bars are the main reinforcement materials for reinforced concrete building structures, which carry various loads such as tensile and compressive stresses and strains, rebar reprocessing effects (welding, mechanical connection, bending or straightening) and other loads in the structure, and are widely used. With the emergence of high-rise, long-span, earthquake-resistant, low-temperature-resistant, and fire-resistant building structures, users not only require steel bars to have high strength, but also require high toughness and good welding performance. [0003] With the sustained and stable economic development, a large number of hot-rolled ribbed steel bars for reinforced concrete need to be produc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/12C22C33/06C21D8/08
CPCC21D8/065C21D8/08C21D2211/005C21D2211/009C22C33/06C22C38/001C22C38/02C22C38/04C22C38/12
Inventor 杨文博姜明芳王小燕李相付
Owner WUHAN IRON & STEEL GRP ECHENG IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap