Mixing device for potassium-based battery and supercapacitor and preparation method thereof

A technology of supercapacitors and hybrid devices, applied in the manufacture of hybrid/electric double layer capacitors, etc., can solve the problems of low energy density of supercapacitors, poor cycle stability power density, etc., and achieve low cost, high power density and low price. Effect

Inactive Publication Date: 2019-10-29
XIFENG 2D FUJIAN MATERIAL TECH CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the poor cycle stability and limited power density of current potassium-ion full batteries, and the low energy density of exis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mixing device for potassium-based battery and supercapacitor and preparation method thereof
  • Mixing device for potassium-based battery and supercapacitor and preparation method thereof
  • Mixing device for potassium-based battery and supercapacitor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0040] Soft carbon is used as the negative electrode material, activated carbon is used as the positive electrode material, 3M KFSI is the electrolyte solution (solvent is DME), and glass fiber is the full battery of the potassium-based battery supercapacitor hybrid device assembled by the diaphragm. Such as figure 2 The TEM and HRTEM images of soft carbon can observe a large number of cross-linked black skeletons, which can effectively accelerate electron transport and adapt to the volume change of the material during charge / discharge, and the cross-linked stripes are conducive to the penetration of electrolytes, thereby Improve the electrochemical performance of the battery. Such as image 3 The transmission electron microscope (TEM and HRTEM) images of the shown activated carbon positive electrode material show that the material has a porous structure, and the specific preparation process is as follows:

[0041] Firstly, activated carbon, carbon black and PVDF were mixed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a mixing device for a potassium-based battery and a supercapacitor and a preparation method thereof. The method includes the following steps: preparing a negative electrode: namely a step of mixing and dissolving a negative electrode carbon material with carbon black and CMC in a certain weight ratio in a mixed solution of water and ethanol, stirring uniformly and then applying slurry to current collector copper foil, and performing annealing treatment in a vacuum environment at 60 DEG C-90 DEG C for 15-20 h; preparation a positive electrode: namely a step of mixing anddissolving a positive electrode carbon material with the carbon black and PVDF in a certain weight ratio in NMP, stirring uniformly and then applying the slurry to current collector aluminum foil, and performing the annealing treatment in a vacuum atmosphere at 60 DEG C-90 DEG C for 15-20 h; and preparing an electrolyte: namely a step of allowing the electrolyte to be a potassium-based salt electrolyte, and enabling positive ions in the electrolyte to be embedded in the negative electrode carbon material when the negative electrode is charged, and to be removed from the negative electrode carbon material during discharging; and enabling negative ions in the electrolyte to perform underpotential deposition when the positive electrode is charged, and enabling the negative ions to be adsorbed in the positive electrode carbon material and to be desorbed from the positive electrode carbon material during discharging.

Description

technical field [0001] The invention relates to the technical fields of potassium ion batteries and supercapacitors, in particular to a potassium-based battery supercapacitor mixing device and a preparation method thereof. Background technique [0002] Clean energy has led to the rapid development of large-scale energy storage devices with the advantages of low cost, environmental protection and abundance. Due to the high cost and the depletion of lithium resources, the further development of lithium-ion batteries is seriously hindered; therefore, various metal-ion batteries such as sodium-ion batteries (SIB), potassium-ion batteries (PIB), aluminum-ion batteries (AIB), magnesium-ion batteries (MIB), and supercapacitors (SCs) have been fully explored as alternatives to lithium-ion batteries (LIBs), according to the standard electrode potentials Li (-3.04V vs E0), Na (-2.71V vs E0), K (-2.93 V vs. E0), Al (-1.66V vs. E0) and Mg (-2.37V vs. E0), compared with SIB, AIB and MIB...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01G11/84
CPCH01G11/84Y02E60/13
Inventor 林楷睿
Owner XIFENG 2D FUJIAN MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap