Preparation method for preparing bionic intelligent metal material surface through 3D printing

A 3D printing, metal material technology, applied in the directions of additive manufacturing, additive processing, energy efficiency improvement, etc., can solve the problem that the control of surface chemical composition is not easy to achieve, the construction method of metal surface microscopic topography is complicated, and it is difficult to realize the microscopic topography of metal surface. Effective control, etc.

Inactive Publication Date: 2019-11-12
GUANGZHOU PANYU POLYTECHNIC
View PDF10 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Prior art methods regulate its surface chemical composition on the basis of metal surface microscopic topography or build its surface topography on the basis of a certain surface chemical composition or use both methods simultaneously; but the construction method of metal surface microscopic topography is relatively Complex, difficult to achieve effective control of metal surface micro-morphology
In addition, with the change of the microscopic morphology of the metal surface, it is not easy to control the chemical composition of the surface.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for preparing bionic intelligent metal material surface through 3D printing
  • Preparation method for preparing bionic intelligent metal material surface through 3D printing
  • Preparation method for preparing bionic intelligent metal material surface through 3D printing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Copper-based material with triangular arrangement on the surface of embodiment 1

[0032] The first step is to use 3D modeling software and CAD (Computer-Aided Design, computer-aided design) workstation to create a 3D model of a triangular arrangement on the copper-based surface with a triangular surface micro-topography, and obtain the 3D data and 3D printing of the model Process file: First, convert the data format from the software into the STL data format suitable for 3D printing process file generation; secondly, check and analyze the STL data; then, pre-set the amount of printing consumables and sample size according to the requirements of the metal sample Finally, edit the STL file to obtain the 3D printing process file. Choose 3D metal laser sintering printing equipment to complete the preparation of metal materials with triangular arrangement on the copper-based surface.

[0033] In the second step, the copper-based surface obtained in the first step is placed...

Embodiment 2

[0037] The silver-based material of embodiment 2 surface quadrilateral arrangement

[0038] The first step is to use 3D modeling software and CAD (Computer-Aided Design, computer-aided design) workstation to create a 3D model of a quadrilateral arrangement on the silver-based surface with different surface microscopic topography, obtain the model 3D data and 3D printing process files, select 3D metal laser sintering printing equipment completes the preparation of metal materials with quadrilateral arrangement on the silver-based surface.

[0039] In the second step, the silver-based surface obtained in the first step is placed in acetone and ethanol respectively, soaked and cleaned for 10 minutes in turn, for a total of 20 minutes, to obtain a clean silver-based surface;

[0040] In the third step, the concentration is 5 grams of 0.1mol / L potassium hydroxide solution, 2 grams of 0.01mol / L sodium persulfate solution and 10 grams of distilled water are mixed, and stirred at a sp...

Embodiment 3

[0043] The gold base material of embodiment 3 surface pentagon arrangement

[0044]The first step is to use 3D modeling software and CAD (Computer-Aided Design, computer-aided design) workstation to create a 3D model of pentagonal arrangement on the gold-based surface with different surface microscopic topography, and obtain the 3D model data and 3D printing process files , choose 3D metal laser sintering printing equipment to complete the preparation of metal materials with pentagonal arrangement on the gold-based surface.

[0045] In the second step, the gold-based surface obtained in the first step is placed in ethanol and distilled water, respectively, soaked and cleaned for 12 minutes, a total of 24 minutes, to obtain a clean gold-based surface;

[0046] In the third step, after the concentration is 4 grams of 3 mol / L potassium hydroxide solution and 9 grams of 5 mol / L sodium bicarbonate solution, 3.5 grams of 4 mol / L potassium persulfate solution and 27 grams of distille...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method for preparing a bionic intelligent metal material surface through 3D printing. The method comprises the following steps of: S1, preparing metal surfaces with different micro-morphologies by a 3D metal laser sintering technology; and S2, the metal surfaces with different micro-morphologies are processed by a surface chemical reaction treatment technologyto obtain the metal functional surfaces with different surface chemical compositions and surface roughness. The metal functional surfaces are prepared by the 3D metal laser sintering technology and the surface chemical reaction treatment technology together, so that the metal surfaces with different surface chemical compositions, surface roughness and surface geometric appearances are obtained. Inaddition, the chemical compositions, the surface roughness and the surface geometric appearances of the metal surfaces are continuously and monotonously changed, and the surface contact angles are ingradient change within the range of 150 degrees + / -15 degrees - 10 degrees + / -5 degrees.

Description

technical field [0001] The invention belongs to the technical surface treatment technology, and in particular relates to a method for preparing the surface of a bionic intelligent metal material by 3D printing. Background technique [0002] Biomimetic intelligent materials are new materials with perception, response and special functional capabilities, which are prepared through structural bionics and functional bionics by imitating various characteristics or characteristics of organisms based on the principles of bionics. As an important functional material, metals are widely used in various engineering fields. The preparation of multi-scale ordered metal surfaces with molecular, nano, and micro structures is an inherent requirement for the realization of biomimetic smart metal material surfaces. At present, the surface of biomimetic smart metal materials is mainly prepared by adjusting the chemical composition of the metal surface and constructing the microscopic morpholog...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B22F3/105B33Y10/00B33Y50/02B33Y80/00
CPCB33Y10/00B33Y50/02B33Y80/00B22F10/00B22F10/34B22F10/28B22F10/62B22F10/60B22F10/68Y02P10/25
Inventor 张勇
Owner GUANGZHOU PANYU POLYTECHNIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com