Manufacturing process of bamboo charcoal fiber fabrics
A bamboo charcoal fiber and production process technology, applied in the field of fabric processing, can solve the problems of insufficient comfort, complex production process, poor hand feel, etc., and achieve the effects of soft hand feel, simple production process and fine appearance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0024] A kind of manufacture craft of bamboo charcoal fiber cloth, concrete manufacture method step is as follows:
[0025] Step 1: take an appropriate amount of aged bamboo over 5 years and dry it so that the moisture content of the bamboo reaches 20-25%.
[0026] Step 2: put the pre-dried bamboo in step 1 into an externally heated vertical retort, and burn it for 48-72 hours to obtain bamboo charcoal.
[0027] Step 3: Grinding the bamboo charcoal obtained in step 2 into nano-scale particles with a nano-grinding machine, adding nano-scale bamboo charcoal and nano-scale titanium dioxide into the viscose spinning solution, and spinning out bamboo charcoal fibers.
[0028] Step 4: The yarn obtained by blending the bamboo charcoal fiber and cotton fiber obtained in step 3 is used as the base yarn.
[0029] Step five: using cotton fiber and regenerated cellulose fiber to blend to obtain yarn as a veil.
[0030] Step 6: Weave the bottom yarn and veil obtained in Step 4 and Step 5...
Embodiment 2
[0039] A kind of manufacture craft of bamboo charcoal fiber cloth, concrete manufacture method step is as follows:
[0040] Step 1: take an appropriate amount of aged bamboo over 5 years and dry it so that the moisture content of the bamboo reaches 20-25%.
[0041] Step 2: put the pre-dried bamboo in step 1 into an externally heated vertical retort, and burn it for 48-72 hours to obtain bamboo charcoal.
[0042] Step 3: Grinding the bamboo charcoal obtained in step 2 into nano-scale particles with a nano-grinding machine, adding nano-scale bamboo charcoal and nano-scale titanium dioxide into the viscose spinning solution, and spinning out bamboo charcoal fibers.
[0043] Step 4: The yarn obtained by blending the bamboo charcoal fiber and cotton fiber obtained in step 3 is used as the base yarn.
[0044] Step five: using cotton fiber and regenerated cellulose fiber to blend to obtain yarn as a veil.
[0045] Step 6: Weave the bottom yarn and veil obtained in Step 4 and Step 5...
Embodiment 3
[0054] A kind of manufacture craft of bamboo charcoal fiber cloth, concrete manufacture method step is as follows:
[0055] Step 1: take an appropriate amount of aged bamboo over 5 years and dry it so that the moisture content of the bamboo reaches 20-25%.
[0056] Step 2: put the pre-dried bamboo in step 1 into an externally heated vertical retort, and burn it for 48-72 hours to obtain bamboo charcoal.
[0057] Step 3: Grinding the bamboo charcoal obtained in step 2 into nano-scale particles with a nano-grinding machine, adding nano-scale bamboo charcoal and nano-scale titanium dioxide into the viscose spinning solution, and spinning out bamboo charcoal fibers.
[0058] Step 4: The yarn obtained by blending the bamboo charcoal fiber and cotton fiber obtained in step 3 is used as the base yarn.
[0059] Step five: using cotton fiber and regenerated cellulose fiber to blend to obtain yarn as a veil.
[0060] Step 6: Weave the bottom yarn and veil obtained in Step 4 and Step 5...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com