Composite coating pot, surface treatment method of pot, and electromagnetic heating appliance

A technology for composite coating and cookware, applied in the fields of electromagnetic heating utensils and composite coating cookware, can solve the problems of inability to achieve rapid heating, high thermal inertia, low energy efficiency value, etc., and achieve excellent adhesion and improved scratch resistance. Effect

Pending Publication Date: 2019-12-13
SHANGHAI CHUNMI ELECTRONICS TECH CO LTD
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the past, electromagnetic heating appliances, such as IH rice cookers or induction cookers, were generally made of iron or iron-aluminum composite boards as heating appliances. However, due to the poor thermal conductivity and high thermal inertia of iron materials, the effect of rapid heating cannot be achieved. Energy efficiency is not high
However, pots using carbon-based composite materials cannot be directly used as pots because of the porous material structure of carbon-based composite materials, strong adsorption, fragile materials, and single surface appearance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite coating pot, surface treatment method of pot, and electromagnetic heating appliance
  • Composite coating pot, surface treatment method of pot, and electromagnetic heating appliance
  • Composite coating pot, surface treatment method of pot, and electromagnetic heating appliance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A composite coating cookware, the cookware 1 includes a bottom wall and a side wall connected to the bottom wall, the cookware 1 also includes a composite coating formed on the surface of the cookware 1, the composite coating There are at least two layers, including at least one base layer 3 and at least one surface layer 2 sprayed in sequence. Wherein, the cookware 1 is a cookware made of carbon-based composite material or carbon fiber material, and the carbon-based composite material of the cookware 1 is a carbon / carbon composite material containing glassy carbon material.

[0035] How it works: as Figure 1-2 As shown, in this technical solution, the cookware 1 is a cookware made of carbon-based composite materials or carbon fiber materials, wherein the carbon-based composite materials have low density (<2.0g / cm3), high specific modulus, high Magnetic conductivity, high thermal conductivity, low expansion coefficient, good thermal shock resistance, and high dimensio...

Embodiment 2

[0042] A surface treatment method for a composite coating pot, comprising the following steps:

[0043] Step 1: Plasma treatment is performed on the inner and outer surfaces of the cookware for 3 to 15 minutes;

[0044] Step 2: spray at least one base layer on the inner and outer surfaces of the cookware after plasma treatment, the spraying distance is 10~60mm, more preferably 50~60mm, the spraying angle is 40~80 degrees, and more preferably 45~60mm 55 degrees, the base layer is a resin film coating with good compatibility with carbon-based composite materials, the thickness of the base layer is about 10-40 μm, and it is naturally dried for 2-4 hours;

[0045] Step 3: After the base layer is dried, a transition layer is sprayed on the inner and outer surfaces of the cookware. The transition layer is a primer mixed with 10% to 50% of uncured resin. The components of the uncured resin in the transition layer The composition of the base layer is the same, and it is naturally dri...

Embodiment 3

[0049] An electromagnetic heating appliance includes an appliance body 4, an upper cover 5 connected to the appliance body 4 and fastened to the open end of the appliance body 4, and the interior of the appliance body 4 is equipped with the above-mentioned composite coating cookware. The appliance body 4 has the characteristics of high power, fast heating speed and high energy efficiency, and has good cooking effect.

[0050] Further, in this embodiment, it can be considered that the appliance body 4 includes an outer pot 6 and an assembly area between the appliance body 4 and the outer pot 6, and the bottom or bottom and side walls of the outer pot 6 are provided for The coil disc 7 that generates electromagnetic, the bottom of the outer pot 6 is provided with a thermostat 8, the inner surface of the assembly area is provided with a circuit board 9, the thermostat 8 and the coil disc 7 are integrated into the circuit through wires on board 9.

[0051] Furthermore, in this em...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a composite coating pot, a surface treatment method of the pot, and an electromagnetic heating appliance. The pot comprises a bottom wall and a side wall connected with the bottom wall, wherein the pot further comprises the composite coating formed on the surface of the pot; the composite coating comprises at least two layers and comprises at least one base layer and at least one surface layer which are sequentially sprayed; the electromagnetic heating appliance comprises an appliance body, and an upper cover which is connected with the appliance body and is buckled atthe open end of the appliance body; and the interior of the appliance body is equipped with the composite coating pot. The invention provides the composite coating pot with excellent adhesion betweencoatings, weather resistance, salt fog resistance, non-sticking property, wear resistance and the like which all satisfy requirements, the surface treatment method of the pot, and the electromagneticheating appliance.

Description

technical field [0001] The invention belongs to the technical field of kitchen cooking appliances, and in particular relates to a composite-coated cookware, a surface treatment method for the cookware, and an electromagnetic heating appliance. Background technique [0002] In the past, electromagnetic heating appliances, such as IH rice cookers or induction cookers, were generally made of iron or iron-aluminum composite plates as heating appliances. However, due to the poor thermal conductivity and high thermal inertia of iron, the effect of rapid heating cannot be achieved. The energy efficiency value is not high. The cookware using carbon-based composite materials cannot be directly used as cookware due to the porous material structure of carbon-based composite materials, strong adsorption, fragile materials, and single surface appearance. [0003] Therefore, based on these problems, there is provided a composite coating cookware and a surface treatment method for the coo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A47J27/00A47J36/02A47J36/24
CPCA47J27/002A47J36/025A47J36/2483
Inventor 杨华郑秀谦龚圆杰陈春恒
Owner SHANGHAI CHUNMI ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap