Formula for preparing high-transparency glass

A technology with high transparency and formula, which is applied in the field of glass formula, can solve the problems of different glass transparency, gloss and quenching temperature difference, glass transparency can not meet the requirements, etc., and achieve moderate quenching temperature difference, reduce bubbles, and reduce bubbles.

Inactive Publication Date: 2019-12-13
徐州宏华玻璃科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of the times, more and more glass is used in our life, and people's requirements for glass are getting higher and higher. In the existing technology, when some high transparency is required, the transparency of the current glass cannot To meet the requirements, in the process of glass preparation, the selection of different raw materials will lead to differences in the transparency, gloss and quenching temperature difference of the glass.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0007] A formula for preparing high-transparency glass. The raw materials in the formula are composed by weight percentage: 0.5% calcite, 10% feldspar, 1% cullet or quartz sand, 1% cerium-based composite clarifier, 1% barium carbonate , 5% colorant, 10% cobalt powder and Yuanming powder, 30% catalyst, at this time, the quenching temperature difference of the glass is not enough, and there are some bubbles.

Embodiment 2

[0009] A formula for preparing high-transparency glass. The raw materials in the formula are composed by weight percentage: 6% calcite, 35% feldspar, 10% cullet or quartz sand, 3% cerium-based composite clarifier, 2.5% barium carbonate , 20% coloring agent, 20% cobalt powder and Yuan Ming powder, 60% catalyst, the production cost of glass is higher at this moment, and the lightness of glass is insufficient.

Embodiment 3

[0011] A formula for preparing high-transparency glass. The raw materials in the formula are composed by weight percentage: 4% calcite, 23% feldspar, 5% cullet or quartz sand, 1.5% cerium-based composite clarifier, 1.25% barium carbonate , 13% coloring agent, 15% cobalt powder and sodium sulfate, 45% catalyst, at this time, the primer-free wrapping of glass can save production cost, improve production efficiency, and the temperature difference of quenching is moderate, and the gloss is good; and, flat view Colorless and transparent, few and small bubbles, no obvious black spots, high lightness.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a formula for preparing high-transparency glass. The formula contains an additive and a carrier, and comprises the following raw materials in percentage by weight: 0.5 to 6% of calcite, 10 to 35% of feldspar, 1 to 10% of cullet or quartz sand, 0 to 3% of cerium-based composite clarifying agent, 0 to 2.5% of barium carbonate, 5 to 20% of a coloring agent, 10 to 20% of cobalt powder and anhydrous sodium sulphate, and 30 to 60 % of a catalyst. Products prepared base on the formula possess moderate quenching temperature different, are excellent in gloss, and are colorlessand transparent in eye level; bubbles are few and small; no obvious black spot is generated; the transparency is high; bubbles in glass bottles are reduced and shrinked; glass bottle transparency is improved further; and glass bottle raw material cost is reduced with ensured glass bottle transparency.

Description

technical field [0001] The invention discloses a formula for preparing high-transparency glass. Background technique [0002] With the development of the times, more and more glass is used in our life, and people's requirements for glass are getting higher and higher. In the existing technology, when some high transparency is required, the transparency of the current glass cannot To meet the requirements, in the process of glass preparation, the selection of different raw materials will lead to differences in the transparency, gloss and quenching temperature difference of the glass. Contents of the invention [0003] Aiming at the problems existing in the above-mentioned prior art, the present invention provides a formula for preparing high-transparency glass, which has moderate quenching temperature difference and good gloss; moreover, it is colorless and transparent when viewed from above, with few and small bubbles, no obvious black spots, high lightness, and less Mini...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C6/04C03C6/02C03C1/00C03C1/04
CPCC03C1/00C03C1/004C03C1/04
Inventor 谢秉翰
Owner 徐州宏华玻璃科技有限公司