A composite process method for preparing vascular stent

A vascular stent and composite process technology, which is applied in the directions of prosthesis, filament/wire forming, fiber processing, etc., can solve the problems of high price of allogeneic decellularization technology, difficult to meet the performance requirements of vascular stent, and limited source of autologous blood vessels. Achieve the effect of accelerating endothelialization, favorable adsorption and good biocompatibility

Active Publication Date: 2021-08-06
SHANGHAI UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, large-diameter artificial blood vessels (>6mm) made of metal, nylon, polytetrafluoroethylene and other materials have achieved extensive success in the field of repairing large and medium-sized artery defects. However, there is no suitable artificial blood vessel (<6mm) for small-diameter blood vessels. Solution, now the main treatment is blood vessel transplantation, but due to the limited source of autologous blood vessels and the high price of allogeneic decellularization technology, a large number of artificial blood vessels are clinically needed as transplant substitutes
[0003] With the extensive research on vascular stents in recent years, it is found that the best way to prepare vascular stents is to imitate the three-layer structure of natural blood vessels to achieve the purpose of vascular transplantation. The performance requirements of the bracket

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A composite process method for preparing vascular stent
  • A composite process method for preparing vascular stent
  • A composite process method for preparing vascular stent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A composite process method for preparing vascular stents, comprising the following steps:

[0039] a. Dissolve PLCL and PEG in a mixed solution of calcium chloride and N,N-dimethylformamide with a volume ratio of 1:1 according to the mass ratio of 5:1, and prepare a 150 mg / mL solution as the oil phase, and add The endothelial growth factor trimethylated chitosan is used as the water phase, the oil phase and the water phase are fully mixed at a ratio of 10:1, and stirred until a stable water-emulsion solution is prepared.

[0040] b. Load the water-emulsion solution in a into the cylinder for electrospinning, such as figure 1 As shown, a 316L stainless steel solid electrode rod with a diameter of 2.5 cm is used as a receiving rod to collect electrospinning, and the receiving range length of the receiving rod to receive electrospinning on the shaft is 7 mm, wherein the distance between the receiving rod and the needle The voltage was 10kv, the injection speed was 0.8mL / h...

Embodiment 2

[0046] This embodiment is basically the same as Embodiment 1, a composite process method for preparing a vascular stent, comprising the following steps:

[0047] a. Dissolve PLCL and PEG in a mixed solution of calcium chloride and N,N-dimethylformamide with a volume ratio of 1:1 according to the mass ratio of 7:1, and prepare a 250mg / mL solution as the oil phase, and add Endothelial growth factor trimethylated chitosan is used as the water phase, the oil phase and the water phase are fully mixed at a ratio of 15:1, and stirred until a stable water-emulsion solution is prepared.

[0048] b. Load the water-emulsion solution in a into the barrel for electrospinning, use a 316L stainless steel solid electrode rod with a diameter of 2.5cm as the receiving rod to collect the electrospinning, and control the receiving rod to receive the electrospinning on the shaft The length of the receiving range is 8mm, the voltage between the receiving rod and the needle is 10kv, the injection sp...

Embodiment 3

[0054] This embodiment is basically the same as Embodiment 1, a composite process method for preparing a vascular stent, comprising the following steps:

[0055] a. Dissolve PLCL and PEG in a mixed solution of calcium chloride and N,N-dimethylformamide with a volume ratio of 1:1 according to the mass ratio of 10:1, and prepare a 350 mg / mL solution as the oil phase. The endothelial growth factor trimethylated chitosan is used as the water phase, the oil phase and the water phase are fully mixed at a ratio of 20:1, and stirred until a stable water-emulsion solution is prepared.

[0056] b. Load the water-emulsion solution in a into the barrel for electrospinning, use a 3cm diameter 316L stainless steel solid electrode rod as a receiving rod to collect the electrospinning, and control the receiving rod to receive the electrospinning on the shaft The length of the receiving range is 9mm, the voltage between the receiving rod and the needle is 15kv, the injection speed is 1.2mL / h, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a composite process method for preparing a vascular stent. Two different processes are used to prepare a three-layer vascular stent structure. The inner layer material is PLCL, PEG and endothelial growth factor. Electrospinning is used to form an axially ordered structure. Spinning; the middle layer is collagen, and the prepared collagen layer is more solid than collagen hydrogel by electrochemical method; the outermost layer is electrospun, and the material is PLCL, and the spinning is collected into a circumferential order. The blood vessel stent prepared by the invention well simulates the three-layer structure of the natural blood vessel, and has broad prospects in clinical application.

Description

technical field [0001] The invention relates to a composite process method for preparing a vascular stent, which is applied in the fields of biomanufacturing technology and tissue repair. Background technique [0002] Cardiovascular disease has become one of the main causes of death in the world. The main causes of cardiovascular disease are intimal hyperplasia and thrombosis, which lead to vascular occlusion. Once vascular occlusion occurs, it will lead to tissue ischemia far from the heart. make it lose its original organizational function. At present, large-diameter artificial blood vessels (>6mm) made of metal, nylon, polytetrafluoroethylene and other materials have achieved extensive success in the field of repairing large and medium-sized artery defects. However, there is no suitable artificial blood vessel (<6mm) for small-diameter blood vessels. Solution, now the main treatment method is blood vessel transplantation, but due to the limited source of autologous...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/40A61L27/50A61L27/24A61L27/18A61L27/54A61L27/22D01D5/00
CPCA61L27/18A61L27/227A61L27/24A61L27/50A61L27/507A61L27/54A61L2300/414A61L2430/22D01D5/003D01D5/0076C08L67/04
Inventor 胡庆夕沈志鹏张海光刘随红
Owner SHANGHAI UNIV