Wear-resistant bacteriostatic bamboo-fiber rib fabric and processing method thereof

A processing method and bamboo fiber technology, applied in knitting, fiber processing, weft knitting and other directions, can solve the problems of poor dimensional stability and solidity, knitted garments that are not stiff in shape, physical discomfort, etc., to improve hygroscopicity and stability. properties, excellent antibacterial and deodorant effects, and enhanced hydrophilic and hydrophobic properties

Inactive Publication Date: 2020-01-21
苏州神马织针器材有限公司
View PDF9 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Rib knitted fabric is a knitted fabric in which a yarn is sequentially formed into a wale on the front and back. In a dry environment, ribbed cloth still generates static electricity due to friction, which makes the human body constantly feel the electric shock, causing physical discomfort
[0004] The characteristics of knitted fabrics are that they can extend in all directions and have good elasticity. The reason is that they are woven from hole-shaped coils, which have great air permeability and soft hand feeling; knitted fabrics are soft and comfortable, but their dimensional stability and solidity are relatively low. Poor; this feature of knitted fabrics makes the shape of knitted garments not crisp; woven garments are easy to cut out of shape, generally speaking, they have better solidity and are not easy to deform. This feature makes garments made of woven fabrics crisp, The functional characteristics of shaping and beautifying the body are very obvious, but the wearer will feel "board, hard and uncomfortable", and will feel tired after wearing for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1: Bamboo fiber wear-resistant and antibacterial type rib knitted fabric is made of the following components by weight (kg): cotton fiber 38, bamboo fiber 45, flax fiber 20, antibacterial and deodorant fiber 12, polyimide fiber 8. Seaweed carbon fiber 6. Modal fiber 4.

[0022] The processing method of bamboo fiber wear-resistant and antibacterial rib knitted fabric specifically includes the following contents:

[0023] (1) Take each raw material by weight of the raw materials, first soak cotton fiber, bamboo fiber and flax fiber in 28°C warm water, and add a compound enzyme whose quality is 5.0% of the total fiber mass, and heat up to 32°C , and ultrasonically stirred for 45 minutes, sealed with argon gas for 8 minutes, and irradiated with 60Co-γ rays for 20 minutes at 45 ° C; the irradiated cotton fibers, bamboo fibers, and flax fibers were taken out and cleaned with absolute ethanol for 5 minutes. times, dry in an oven for later use;

[0024] (2) Weigh t...

Embodiment 2

[0028] Embodiment 2: Bamboo fiber wear-resistant and antibacterial type rib knitted fabric is made of the following weight (kg): cotton fiber 40, bamboo fiber 48, flax fiber 22, antibacterial and deodorant fiber 13, polyimide fiber 10 , Seaweed carbon fiber 8, Modal fiber 6.

[0029] The processing method of bamboo fiber wear-resistant and antibacterial rib knitted fabric specifically includes the following contents:

[0030] (1) Take each raw material according to the weight portion of the raw material, first soak cotton fiber, bamboo fiber, and flax fiber in 25°C warm water, and add a compound enzyme whose quality is 5.0% of the total fiber mass, and heat up to 32°C , and ultrasonically stirred for 45 minutes, and sealed with inert gas mixed with argon and helium for 10 minutes, and irradiated with 60Co-γ rays for 15 minutes at 45°C; take out the irradiated cotton fibers, bamboo fibers, and flax fibers for Wash with absolute ethanol for 5 times, and dry in an oven for later...

Embodiment 3

[0036] Embodiment 3: Bamboo fiber wear-resistant and antibacterial type rib knitted fabric is made of the following weight (kg): cotton fiber 44, bamboo fiber 50, flax fiber 25, antibacterial and deodorant fiber 15, polyimide fiber 10 , Seaweed carbon fiber 8, Modal fiber 8.

[0037] The processing method of bamboo fiber wear-resistant and antibacterial rib knitted fabric specifically includes the following contents:

[0038] (1) Take each raw material by weight of the raw materials, first soak cotton fiber, bamboo fiber, and flax fiber in 30°C warm water, and add a compound enzyme whose quality is 5.5% of the total fiber mass, and heat up to 35°C , and ultrasonically stirred for 45 minutes, sealed with a hernia inert gas for 10 minutes, and irradiated with 60Co-γ rays at 45°C for 20 minutes; take out the irradiated cotton fibers, bamboo fibers, and flax fibers and wash them with absolute ethanol for 4 -6 times, dry in the oven for later use;

[0039] (2) Weigh the seaweed c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant bacteriostatic bamboo-fiber rib fabric and a processing method thereof. The rib fabric is prepared from, by weight, 38-44 parts of cotton fiber, 45-50 parts ofbamboo fiber, 20-25 parts of flax fiber, 12-15 parts of bacteriostatic anti-odor fiber, 8-10 parts of polyimide fiber, 6-8 parts of algae carbon fibre, and 4-8 parts of modal fiber. The rib fabric isprepared from various fibers, the bamboo fiber has good breathability, water absorptivity, high wear resistance, good dying property and the like, and has functions such as natural antibacterial property, bacteriostat, mite controlling, deodorizing and ultraviolet resistance; particularly, the average bacteriostasis rate of the bacteriostatic anti-odor fiber to staphylococcus aureus, candida sporogenes and colibacillus is equal to or higher than 99%, and thus excellent antibacterial and deodorizing effect can be achieved.

Description

technical field [0001] The invention relates to a wear-resistant and antibacterial rib knitted fabric of bamboo fiber and a processing method thereof, and relates to the technical field of textiles. Background technique [0002] A wide range of raw materials can be used for weaving knitted fabrics, including cotton, wool, silk, hemp, chemical fibers and their blended yarns or interlaced yarns; With greater extensibility and elasticity, it is suitable for making underwear, tights and sportswear, etc. Knitted fabrics can also be used as outerwear, mattresses, etc. after changing the structure and improving dimensional stability. [0003] Rib knitted fabric is a knitted fabric in which a yarn is sequentially formed into a wale on the front and back. In a dry environment, ribbed cloth still generates static electricity due to friction, which makes the human body feel the electric shock continuously, causing physical discomfort. [0004] The characteristics of knitted fabrics a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/14D04B1/16D06B3/02D06B13/00D06M16/00D06M10/00D06M101/06
CPCD04B1/14D04B1/16D06B3/02D06B13/00D06M10/008D06M16/00D06M16/003D06M2101/06D10B2201/02D10B2201/04D10B2201/10D10B2201/22D10B2401/13
Inventor 刘金华刘金才顾斌宾
Owner 苏州神马织针器材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com