A kind of preparation method of glass fiber wall cloth base cloth

A glass fiber wall and glass fiber cloth technology, which is applied in fiber processing, textile, liquid/gas/steam textile material processing, etc., can solve the problems that water cannot be volatilized normally, affects the fastness and beauty, and wall cloth foams, etc., and achieves Improves moisture evaporation efficiency, maintains appearance, and prevents blistering and mildew

Active Publication Date: 2021-02-19
富仕德新材料制造(淮安)有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is a serious problem in the use and construction of sea-based cloth at present: after being glued to the wall for a period of time, due to the hydrophobicity of the glass fiber itself, the water cannot be volatilized normally, resulting in foaming and even mildew of the wall cloth, which affects the fastness and appearance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] This embodiment discloses a method for preparing a glass fiber wall cloth base cloth, which includes the following steps:

[0023] Step 1: preparing glass fiber cloth;

[0024] Step 2: Dip the glass fiber cloth into the resin solution;

[0025] Step 3: Sand the glass fiber cloth.

[0026] In step 1, the preparation method of glass fiber cloth is as follows: the crucible wire drawing method is to first melt the glass raw material at high temperature into glass balls, then melt the glass balls twice, and draw them at high speed to make glass fiber filaments; the hydrophilic fibers are used as raw materials in turn. After opening and cleaning, carding, drawing, and roving to make hydrophilic filaments; then use part of the glass fiber filaments and hydrophilic filaments as raw materials to make composite yarns through spun yarn; heat-setting the composite yarns; finally The composite yarn and the remaining glass fiber filaments are used as raw materials to make glass fib...

Embodiment 2

[0034] This embodiment discloses a method for preparing a glass fiber wall cloth base cloth, which includes the following steps:

[0035] Step 1: preparing glass fiber cloth;

[0036] Step 2: Dip the glass fiber cloth into the resin solution;

[0037] Step 3: Sand the glass fiber cloth.

[0038] In step 1, the preparation method of glass fiber cloth is as follows: the pool kiln wire drawing method is to melt pyrophyllite and other raw materials in the kiln to form a glass solution, remove the air bubbles and transport it to the porous bushing plate through a channel, and draw it into glass fiber filaments at high speed; Using hydrophilic fiber as raw material to make hydrophilic filament through opening and cleaning, carding, drawing, and roving in sequence; then using part of glass fiber filament and hydrophilic filament as raw material to make composite yarn through spinning; Line heat setting treatment; finally, the composite yarn and the remaining glass fiber filaments a...

Embodiment 3

[0046] This embodiment discloses a method for preparing a glass fiber wall cloth base cloth, which includes the following steps:

[0047] Step 1: preparing glass fiber cloth;

[0048] Step 2: Dip the glass fiber cloth into the resin solution;

[0049] Step 3: Sand the glass fiber cloth.

[0050] In step 1, the preparation method of glass fiber cloth is as follows: the crucible wire drawing method is to first melt the glass raw material at high temperature into glass balls, then melt the glass balls twice, and draw them at high speed to make glass fiber filaments; the hydrophilic fibers are used as raw materials in turn. After opening and cleaning, carding, drawing, and roving to make hydrophilic filaments; then use part of the glass fiber filaments and hydrophilic filaments as raw materials to make composite yarns through spun yarn; heat-setting the composite yarns; finally The composite yarn and the remaining glass fiber filaments are used as raw materials to make glass fib...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for preparing a glass fiber wall cloth base cloth, comprising the following steps: step 1: preparing glass fiber cloth; step 2: dipping the glass fiber cloth into a resin solution; step 3: sanding the glass fiber cloth . In the preparation method of the glass fiber wall cloth base cloth provided by the present invention, the glass fiber cloth is sanded to form countless ultrafine fibers on the surface of the glass fiber cloth, and the glass fiber cloth and The moisture between the walls can be discharged to prevent foaming and mildew, and to maintain the appearance. In addition, by introducing a small amount of hydrophilic groups into the glass fiber cloth, the glass fiber cloth can quickly transport water and improve the performance of the glass fiber cloth. The moisture volatilization efficiency between the wall and the wall does not affect other properties of the glass fiber cloth.

Description

technical field [0001] The invention relates to the field of glass fiber technology, in particular to a method for preparing a glass fiber wall cloth base cloth. Background technique [0002] Cracking of the wall after home decoration is a common problem. As people's requirements for interior decoration increase, more attention is paid to the decorative effect of the wall surface. People will paste wallpaper or brush latex paint on the wall to achieve a beautiful effect. For wallpaper, it is more about the decorative effect, and there are not many functional improvements. For example, the air in the south of my country is relatively humid, and there is often a return to moisture. Ordinary wallpapers are prone to warping, wrinkles, or even Falling off and other situations, the durability is poor, and it cannot meet the needs of use, especially in fire prevention, flame retardancy, and environmental protection. For latex paint, free formaldehyde will be released, which can in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/00D03D15/267D03D15/47D03D15/217D03D15/233D03D15/225D02G3/04D02G3/18D06B3/10D06C11/00D06M15/263D06M15/333D06M15/356
CPCD02G3/04D02G3/18D03D15/00D06B3/10D06C11/00D06M15/263D06M15/333D06M15/3568D10B2101/06D10B2201/01D10B2201/02D10B2201/24D10B2211/02D10B2211/04D03D15/267E04F13/002
Inventor 王少伟邵亚国梁开仁
Owner 富仕德新材料制造(淮安)有限公司