Flame-retarding PP and preparation method thereof

A composite flame retardant and copolymer resin technology, applied in the field of flame retardant materials, can solve the problems of low notched impact resistance, easy aging, poor fluidity, etc., and achieve excellent notched impact strength, excellent low temperature resistance, and environmental friendliness

Pending Publication Date: 2020-03-10
厦门颜盛塑化科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the oxygen index of polypropylene is low, only 17.4. It is easy to burn, has a fast burning rate, and has a large calorific value. When burning, it is accompanied by melt dripping, which is easy to cause fire and has unsafe factors, which limits its application in many fields. application
[0003] In order to enhance the flame retardancy of polypropylene products, only flame retardants can be added, but the addition of flame retardants will often reduce the mechanical properties of the products, making these products prone to stress, cracking, and impact resistance to notches. Low strength, poor wear resistance, poor fluidity, easy aging and other shortcomings, the product reliability is insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retarding PP and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An embodiment of the flame-retardant PP of the present invention, the flame-retardant PP described in this embodiment includes the following components by weight: 75 parts of PP copolymer resin, 15 parts of environmentally friendly bromine-antimony composite flame retardant, and 7 parts of compatibilizer , 2 parts of antioxidant, 1 part of heat-resistant stabilizer.

[0024] The environment-friendly bromine-antimony composite flame retardant described in this embodiment is a compound of octabromoether and antimony trioxide, the mass ratio is 3:1, the compatibilizer is maleic anhydride grafted PP, and the antimony The oxygen agent is a compound of antioxidant 1010 and antioxidant 168, the mass ratio is 1:1, and the heat-resistant stabilizer is N,N-4,4-diphenylmethane bismaleimide.

[0025] The preparation method of the flame-retardant PP described in this example includes the following steps: the PP copolymer resin is first placed in a blast oven and dried at 80°C for 4 ...

Embodiment 2

[0027] An embodiment of the flame-retardant PP of the present invention, the flame-retardant PP described in this embodiment includes the following components in parts by weight: 80 parts of PP copolymer resin, 18 parts of environmentally friendly bromine-antimony composite flame retardant, and 10 parts of compatibilizer , 4 parts of antioxidant, 2 parts of heat-resistant stabilizer.

[0028] The environment-friendly bromine-antimony composite flame retardant described in this embodiment is a compound of octabromo-S ether and antimony trioxide, the mass ratio is 4:1, the compatibilizer is maleic anhydride grafted PP, and the The antioxidant is a compound of antioxidant 1010 and antioxidant 168, the mass ratio is 1:1, and the heat-resistant stabilizer is N,N-4,4-diphenylmethane bismaleimide.

[0029] The preparation method of the flame-retardant PP described in this example includes the following steps: first place the PP copolymer resin in a blast oven and dry it at a temperat...

Embodiment 3

[0031] An embodiment of the flame-retardant PP of the present invention, the flame-retardant PP described in this embodiment includes the following components by weight: 60 parts of PP copolymer resin, 12 parts of environment-friendly bromine-antimony composite flame retardant, and 6 parts of compatibilizer , 1 part of antioxidant, 0.5 part of heat-resistant stabilizer.

[0032] The environment-friendly bromine-antimony composite flame retardant described in this embodiment is a compound of octabromoether and antimony trioxide, the mass ratio is 3.5:1, the compatibilizer is maleic anhydride grafted PP, and the antimony The oxygen agent is a compound of antioxidant 1010 and antioxidant 168, the mass ratio is 1:1, and the heat-resistant stabilizer is N,N-4,4-diphenylmethane bismaleimide.

[0033] The preparation method of the flame-retardant PP described in this example includes the following steps: first place the PP copolymer resin in a blast oven and dry it at a temperature o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses flame-retarding PP including, by weight, 60-80 parts of PP copolymerized resin, 12-18 parts of environment-friendly bromine / antimony composite flame-retarding agent, 6-10 partsof a compatibilizer, 1-4 parts of an antioxidant, and 0.5-2 parts of a heat-resistant stabilizer. The invention also discloses a preparation method of the flame-retarding PP. In the invention, the flame retarding effect of the flame-retarding PP is significantly improved, and the flame-retarding PP is improved in impact toughness and low temperature resistance at the same time. The flame-retarding PP can be applied to the field, with high requirements, such as home appliances, machinery, automobiles, etc.

Description

technical field [0001] The invention relates to the field of flame-retardant materials, in particular to a flame-retardant PP and a preparation method thereof. Background technique [0002] Polypropylene (PP) is widely used in automobiles, home appliances, textiles, construction and other industries due to its excellent mechanical properties, good electrical insulation, chemical corrosion resistance, and light weight. However, the oxygen index of polypropylene is low, only 17.4. It is easy to burn, has a fast burning rate, and has a large calorific value. When burning, it is accompanied by melt dripping, which is easy to cause fire and has unsafe factors, which limits its application in many fields. application. [0003] In order to enhance the flame retardancy of polypropylene products, only flame retardants can be added, but the addition of flame retardants will often reduce the mechanical properties of the products, making these products prone to stress, cracking, and im...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/14C08L51/06C08K13/02C08K3/22C08K5/06C08K5/134C08K5/526C08K5/3415
CPCC08L23/14C08L2201/02C08L2205/08C08L51/06C08K13/02C08K3/2279C08K5/06C08K5/1345C08K5/526C08K5/3415
Inventor 周桂林朱孙庆
Owner 厦门颜盛塑化科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap