A metal powder and atomized powder technology, which is applied in the field of combined atomization to prepare spherical metal powder, can solve the problems of general powder production efficiency, coarse powder, and high cost of powder production, and achieve high controllability of laser energy and directionality, Wide application prospects and high production efficiency

Pending Publication Date: 2020-03-20
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF9 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the melting process of this method is non-contact, effectively avoiding the introduction of impurities, and the prepared powder has a high degree of sphericity, but the prepared powder is relatively coarse, the composition uniformity of the powder is uncontrollable, and the rotation speed of the electrode rod is relatively high. The electrode and transmission requirements of the equipment are relatively high, the preparation process is not easy to control, and the powder production efficiency is average. It is necessary to prepare alloy bars first, and the cost of powder production is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method and device for preparing spherical metal powder through combined atomization
  • Method and device for preparing spherical metal powder through combined atomization

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be further described in detail below in conjunction with the accompanying drawings and specific embodiments.

[0019] like figure 1 As shown, a combined atomization device for preparing spherical metal powder provided by the present invention includes a metal melting system, a water atomization system, a powder drying system, a laser spheroidization system, a powder collection system, a gas circulation system, Control System.

[0020]The metal melting system includes a melting chamber 1, a crucible 2, a heater 3, a metal raw material 4, and a molten metal 5 for providing molten metal 5 for water atomization; the metal raw material 4 is placed in the crucible 2 Inside; the crucible 2 is placed in the melting chamber 1, and both the crucible 2 and the bottom of the melting chamber 1 have small openings; the heater 3 is installed around the crucible 2 for heating and melting the metal raw material 4 to form a molten metal 5 ;

[0021] The wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method and device for preparing spherical metal powder through combined atomization, and belongs to the technical field of metal powder preparation. The device comprises a metal melting system, a water atomizing system, a powder drying system, a laser spheroidizing system, a powder collecting system, a gas circulating system and a control system. A water atomization method has the characteristics of low cost, high production efficiency and small granularity but the prepared powder is uneven in morphology and high in oxygen content; a laser spheroidizing method is highin laser energy and directivity controllability and can spheroidize irregular powder; and the two methods are combined so that advantages can be combined and disadvantages can be overcome, and the combined method is suitable for preparing spherical metal powder. The method and device have good application prospects in actual production of advanced manufacturing technologies such as 3D printing.

Description

Technical field: [0001] The invention belongs to the technical field of metal powder preparation, and in particular relates to a combined atomization method and device for preparing spherical metal powder. Background technique: [0002] With the rapid development of science and technology, the application of metal powder is more and more extensive, so the preparation of metal powder is also very important. Among the prepared metal powders, compared with irregular powders, spherical powders have superior properties such as good fluidity, good sinterability and controllable reaction, and are increasingly widely used in mass production and scientific research. Spherical metal powder is the raw material for advanced manufacturing technologies such as 3D printing (additive manufacturing) and metal injection molding. Among them, 3D printing technology is an emerging technology that is rapidly developing in the field of manufacturing. , home appliances, biomedicine and other fiel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/08B22F9/02
CPCB22F9/082B22F9/02B22F2009/0828B22F2009/0872B22F2009/0844B22F2999/00B22F2202/11
Inventor 张兴权陈涛钱健清刘侠马群双隋凤利杨恒基纪啸天
Owner ANHUI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap