Polyvinyl chloride elastomer electroosmosis electrode composite material and preparation method thereof

A polyvinyl chloride and composite material technology is applied in the field of electroosmotic electrode materials, which can solve the problems of unstable resistivity and easy attenuation, and achieve the effects of no resistivity attenuation, convenient preparation and strong practicability.

Inactive Publication Date: 2020-04-03
陕西易莱德新材料科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing electroosmotic electrodes often have defects such as unstable resistivity and easy attenuation in the application process of sewage purification and drainage treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] The present invention also provides a method for preparing the above-mentioned polyvinyl chloride elastomer electroosmotic electrode composite material, comprising the following steps:

[0021] Step 1: Weigh the polyvinyl chloride elastomer 31-35%, phenoxy resin 6-10%, epoxy resin 6-10%, cosolvent 6-10%, curing agent 1-3%, coupling agent 1-3%, the balance is conductive carbon black, and the sum of the mass percentages of the above components is 100%;

[0022] Step 2: Add the conductive carbon black weighed in step 1 into the mixer, control the temperature to be 90-110°C, stir for 40-60min, add polyvinyl chloride elastomer, phenoxy resin, epoxy resin, cosolvent, cure agent and coupling agent, continue to stir for 40-60min and then discharge;

[0023] Step 3: Cool the material obtained in step 2 to 20-40 °C for discharging, and then put it into a granulator for granulation, and then get it.

[0024] Through the above method, the preparation method of the polyvinyl chlor...

Embodiment 1

[0026] Weigh 31% of polyvinyl chloride elastomer, 6% of phenoxy resin, 6% of epoxy resin, 6% of cosolvent, 1% of curing agent, 1% of coupling agent, and the balance of conductive carbon black by mass percentage. The sum of the mass percentages is 100%; add the weighed conductive carbon black into the mixer, control the temperature to 90 ° C, and add polyvinyl chloride elastomer, phenoxy resin, epoxy resin, cosolvent, curing after stirring for 40 minutes. agent and coupling agent, continue to stir for 40min and then discharge the material; cool the material to 20 ℃ to discharge the material, and then put it into a granulator for granulation, that is, it is obtained.

Embodiment 2

[0028] Weigh 32% of polyvinyl chloride elastomer, 7% of phenoxy resin, 7% of epoxy resin, 7% of cosolvent, 1.5% of curing agent, 1.5% of coupling agent, and the balance of conductive carbon black by mass percentage. The sum of the mass percentages is 100%; add the weighed conductive carbon black to the mixer, control the temperature to 95°C, add polyvinyl chloride elastomer, phenoxy resin, epoxy resin, cosolvent, curing after stirring for 45min agent and coupling agent, continue to stir for 45min and then discharge the material; cool the material to 25 °C for discharge, and then put it into a granulator for granulation.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polyvinyl chloride elastomer electroosmosis electrode composite material. The polyvinyl chloride elastomer electroosmosis electrode composite material is prepared from the following components in percentage by mass: 31 to 35 percent of a polyvinyl chloride elastomer, 6 to 10 percent of a phenoxy resin, 6 to 10 percent of an epoxy resin, 6 to 10 percent of a cosolvent, 1 to 3 percent of a curing agent, 1 to 3 percent of a coupling agent and the balance of conductive carbon black. The invention also discloses a preparation method of the polyvinyl chloride elastomer electroosmosis electrode composite material. The polyvinyl chloride elastomer electroosmosis electrode composite material disclosed by the invention has good mechanical properties such as flexibility, adhesion and the like, meanwhile, due to the addition of the cosolvent, the conductivity is excellent when the polyvinyl chloride elastomer electroosmosis electrode composite material is used for an electroosmosis electrode, the resistivity of a product is not attenuated after long-time energization, and the stability is high. The preparation method of the polyvinyl chloride elastomer electroosmosiselectrode composite material is basically the same as that of a common polymer material in processing and forming, so that the preparation is convenient, the practicability is high and the market prospect is wide.

Description

technical field [0001] The invention belongs to the technical field of electroosmotic electrode materials, in particular to a polyvinyl chloride elastomer electroosmotic electrode composite material, and the invention also relates to a preparation method of the above-mentioned polyvinyl chloride elastomer electroosmotic electrode composite material. Background technique [0002] According to the difference of structure and preparation method, conductive polymer materials can be divided into two categories: structural conductive polymer materials and composite conductive polymer materials. Structural conductive polymer materials refer to conjugated polymers whose molecular structure itself can conduct electricity or have a conductive function after doping treatment, such as polyethylene fast, polyaniline, polypyrrole, polyphene, polyfuran, etc. Composite conductive polymer material refers to the polymer as the matrix, by adding various conductive fillers (such as carbon black...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L71/12C08L63/00C08K13/02C08K3/04C08K5/098C08K5/17
CPCC08K2201/001C08L27/06C08L2205/03C08L71/12C08L63/00C08K13/02C08K3/04C08K5/098C08K5/175
Inventor 成伟
Owner 陕西易莱德新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap