Natural bamboo fiber bed core plate and preparation method thereof
A technology of bamboo raw fiber and manufacturing method, applied in the field of bamboo raw fiber bed core board and its preparation, can solve the problems of low content of low-melting fiber, loose mattress, slag falling, etc., achieve high air permeability and flexibility, and ensure comfort , Guarantee the effect of using strength and life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0035] Such as figure 1 Shown, a kind of bamboo fiber bed core board comprises the first hard cotton fiber layer 1, core layer 2, the second hard cotton fiber layer 3, and described first hard cotton fiber layer 1 is positioned at described bamboo fiber bed The uppermost layer of the core board, the second hard cotton fiber layer 3 is located at the bottom of the bamboo fiber bed core board, and the core layer 2 is arranged on the first hard cotton fiber layer 1 and the second hard cotton fiber layer 3. Between the cotton fiber layers 3, the core layer 2 contains bamboo fibers and low melting point fibers,
[0036] The thickness of the first hard cotton fiber layer 1 is 1 mm, the thickness of the core layer 2 is 10 mm, and the thickness of the second hard cotton fiber layer 3 is 1 mm;
[0037] The core layer is a composite layer composed of the following components by weight percentage: 92% bamboo fiber, 5% low-melting fiber;
[0038] The surface of the bamboo fiber is provi...
Embodiment 2
[0052] A bamboo fiber bed core board, the thickness of the first hard cotton fiber layer is 3 millimeters, the thickness of the core layer is 120 millimeters, and the thickness of the second hard cotton fiber layer is 3 millimeters;
[0053] The core layer is a composite layer composed of the following components by weight percentage: 95% bamboo fiber, 8% low-melting fiber;
[0054] The bamboo fiber is long and thin, and the length of a single filamentous bamboo fiber is 40 millimeters, and the diameter is 0.5 millimeters;
[0055] There are through holes in the cross section of the bamboo raw fiber, and the diameter of the through hole in the cross section of the bamboo raw fiber is 0.18 mm.
[0056] A method for manufacturing a bamboo fiber bed core board, said method comprising:
[0057] Step 1: preparing bamboo fiber, specifically including:
[0058] Cut the bamboo into a specified length, and then cut it into bamboo slices; soak the bamboo slices in an alkaline water so...
Embodiment 3
[0066] A bamboo fiber bed core board, the thickness of the first hard cotton fiber layer is 2 millimeters, the thickness of the core layer is 60 millimeters, and the thickness of the second hard cotton fiber layer is 2 millimeters;
[0067] The core layer is a composite layer composed of the following components by weight percentage: 94% bamboo fiber, 6% low-melting fiber;
[0068] The bamboo fiber is long and thin, and the length of a single filamentous bamboo fiber is 30 millimeters, and the diameter is 0.3 millimeters;
[0069] There are through holes in the cross section of the bamboo raw fiber, and the diameter of the through hole in the cross section of the bamboo raw fiber is 0.1 mm.
[0070] A method for manufacturing a bamboo fiber bed core board, said method comprising:
[0071] Step 1: preparing bamboo fiber, specifically including:
[0072] Cut the bamboo into a specified length, and then cut it into bamboo slices; soak the bamboo slices in an alkaline water soft...
PUM
| Property | Measurement | Unit |
|---|---|---|
| Thickness | aaaaa | aaaaa |
| Thickness | aaaaa | aaaaa |
| Length | aaaaa | aaaaa |