Wood-plastic line and preparation method thereof

A wood-plastic and line technology, applied to window/door frames, etc., can solve the problems of non-moisture-proof solid wood lines, undurable mud lines, and increased deforestation, so as to achieve low refractive index, protect the environment, and reduce deforestation. Effect

Pending Publication Date: 2020-04-21
宋恩明
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of people's living standards, there are better requirements for the living environment. A comfortable and beautiful living place can make people feel more happy. Nowadays, when installing doors and windows, the edges of the walls often use solid wood lines, mud lines and density boards. Lines are used for decoration, but the use of solid wood lines increases the felling of forests, which is not conducive to environmental protection. At the same time, solid wood lines are not moisture-proof, easy to deform, and termite-proof. Mud lines are solid wood, waste wood and multi-layer wood. Glue is pressed together with chemical raw materials such as gypsum powder. The mud-coated lines are not durable, easy to be deformed by moisture and easy to age. At the same time, they contain formaldehyde, which is not environmentally friendly and has a certain impact on health. MDF lines are made by pressing wood powder and glue. It is also not durable, easily deformed by moisture, and contains formaldehyde

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A wood-plastic line, made of the following raw materials in parts by weight: 25 parts of wood powder, 80 parts of PVC resin, 90 parts of heavy calcium, 0.3 parts of calcium stearate, 0.9 parts of stearic acid, 6 parts of foam regulator, AC foaming agent 0.2 parts, NC foaming agent 1.3 parts, plastic steel 20 parts, PVC foaming 20 parts.

[0027] Preferably, recycled materials are used for the plastic steel and PVC foam.

[0028] Preferably, the wood-plastic line includes a wood core and wood plastic, and the wood plastic wraps the wood core.

[0029] Preferably, the wood core is recycled waste wood.

[0030] Preferably, the wood-plastic line and its preparation method include the following steps:

[0031] Step 1: Grind plastic steel and PVC foam recycled materials into granules.

[0032] Step 2: Put the plastic steel and PVC foaming recycled materials that are ground into granules, wood powder, PVC resin, heavy calcium, and calcium stearate into the mixer in proporti...

Embodiment 2

[0040] A wood-plastic line, made of the following raw materials in parts by weight: 30 parts of wood powder, 85 parts of PVC resin, 100 parts of heavy calcium, 0.4 parts of calcium stearate, 1.1 parts of stearic acid, 7.5 parts of foam regulator, 0.29 parts of AC foaming agent, 1.6 parts of NC foaming agent, 25 parts of plastic steel, and 25 parts of PVC foaming.

[0041] Preferably, recycled materials are used for the plastic steel and PVC foam.

[0042] Preferably, the wood-plastic line includes a wood core and wood plastic, and the wood plastic wraps the wood core.

[0043] Preferably, the wood core is recycled waste wood.

[0044] Preferably, the wood-plastic line and its preparation method include the following steps:

[0045] Step 1: Grind plastic steel and PVC foam recycled materials into granules.

[0046] Step 2: Put the plastic steel and PVC foaming recycled materials that are ground into granules, wood powder, PVC resin, heavy calcium, and calcium stearate into t...

Embodiment 3

[0054] A wood-plastic line, made of the following raw materials in parts by weight: 35 parts of wood powder, 100 parts of PVC resin, 110 parts of heavy calcium, 0.5 parts of calcium stearate, 1.3 parts of stearic acid, 9 parts of foam regulator, 0.38 parts of AC foaming agent, 1.9 parts of NC foaming agent, 30 parts of plastic steel, 30 parts of PVC foaming.

[0055] Preferably, recycled materials are used for the plastic steel and PVC foam.

[0056] Preferably, the wood-plastic line includes a wood core and wood plastic, and the wood plastic wraps the wood core.

[0057] Preferably, the wood core is recycled waste wood.

[0058] Preferably, the wood-plastic line and its preparation method include the following steps:

[0059] Step 1: Grind plastic steel and PVC foam recycled materials into granules.

[0060] Step 2: Put the plastic steel and PVC foaming recycled materials that are ground into granules, wood powder, PVC resin, heavy calcium, and calcium stearate into the mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wood-plastic line and a preparation method thereof, and relates to the technical field of material preparation. The wood-plastic line is prepared from the following raw materials in parts by weight: 25-35 parts of wood powder, 80-100 parts of PVC resin, 90-110 parts of coarse whiting, 0.3-0.5 part of calcium stearate, 0.9-1.3 parts of stearic acid, 6-9 parts of a foamingregulator, 0.2-0.38 part of an AC foaming agent, 1.3-1.9 parts of an NC foaming agent, 20-30 parts of plastic steel and 20-30 parts of PVC foam. According to the wood-plastic line, a wood core in thewood-plastic line is made of waste wood so that resource waste is avoided, forest felling is reduced, resources are reasonably utilized, and the environment is protected; the wood-plastic raw materials are filled with the plastic steel and PVC recycled materials, so that the manufactured wood-plastic line has the effects of no deformation and durability; the wood core is wrapped by the wood-plastic raw materials, so that the wood-plastic line has moisture-proof, termite-proof and anti-aging effects on the whole; the wood-plastic raw materials and additives have the characteristics of no toxicity, no odor, no odor and zero formaldehyde, the whole processing and manufacturing process of the wood-plastic line is convenient, the quality of the wood-plastic line is stable, and the size is accurate.

Description

technical field [0001] The invention relates to the technical field of material preparation, in particular to a wood-plastic line and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, there are better requirements for the living environment. A comfortable and beautiful living place can make people feel more happy. Nowadays, when installing doors and windows, the edges of the walls often use solid wood lines, mud lines and density boards. Lines are used for decoration, but the use of solid wood lines increases the felling of forests, which is not conducive to environmental protection. At the same time, solid wood lines are not moisture-proof, easy to deform, and termite-proof. Mud lines are solid wood, waste wood and multi-layer wood. Glue is pressed together with chemical raw materials such as gypsum powder. The mud-coated lines are not durable, easy to be deformed by moisture and easy to age. At the same time, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08K3/26C08K5/098C08K5/09C08J9/10C08J9/08C08J9/04B29C45/14E06B1/34
CPCB29C45/14C08J9/04C08J9/08C08J9/103C08J2203/02C08J2203/04C08J2203/20C08J2327/06C08J2497/02C08K5/09C08K5/098C08K2003/265E06B1/34
Inventor 宋恩明
Owner 宋恩明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products