6005A aluminum alloy for automobiles and crash box processing method

A processing method and technology of aluminum alloy, which are applied in the processing field of 6005A aluminum alloy for automobiles and energy-absorbing boxes, can solve the problems of crushing and cracking, and achieve the effect of uniform deformation and no cracking.

Pending Publication Date: 2020-04-21
山东友升铝业有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current energy-absorbing box products produced by the 6005A alloy meet the conditions of Rm≥280MPa, RP0.2≥260MPa, and A≥10%, and the crushing cracks; after adjusting the aging process, the crushing cracking still exists

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 6005A aluminum alloy for automobiles and crash box processing method
  • 6005A aluminum alloy for automobiles and crash box processing method
  • 6005A aluminum alloy for automobiles and crash box processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only a part of the embodiments of the present invention, rather than all the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by those of ordinary skill in the art without creative work shall fall within the protection scope of the present invention.

[0033] 1. During the smelting process of 6005A aluminum rods, magnesium is added with magnesium ingots with a magnesium content of 99.9%, and silicon is added with aluminum-silicon alloys with a silicon content of 21%; the temperature of the aluminum liquid is 745℃ when adding; 1 Debug the components of each embodiment)

[0034] Table 1

[0035]

[0036] 2. The aluminum liquid adopts two-stage filtration, and the number of filter plates is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a 6005A aluminum alloy for automobiles and a crash box processing method. The 6005A aluminum alloy for automobiles comprises the following components in percentage by weight: 0.75-0.80% of Si, 0.15-0.20% of Fe, less than or equal to 0.10% of Cu, 0.28-0.30% of Mn, 0.63-0.68% of Mg, 0.06-0.10% of Cr, less than or equal to 0.10% of Zn, less than or equal to 0.10% of Ti and thebalance of Al. The crash box processing method adopts the aluminum alloy. the aluminum alloy is capable of weakening the segregation, at crystal boundaries, of surplus Si, so that embrittlement is not easy to cause and alloy materials are not easy to craze during compression degeneration. The 6005A aluminum alloy crash box prepared by the process satisfies the conditions that the tensile strengthRm is greater than or equal to 280 MPa, the yield strength RP0.2 is greater than or equal to 260 MPa and the elongation percentage A is greater than or equal to 10%; and the crash box is symmetric, uniform in deformation and free of craze at folds during compression degeneration.

Description

Technical field [0001] The invention relates to a method for processing 6005A aluminum alloy and an energy-absorbing box for automobiles. Background technique [0002] The energy absorbing box is a safety component of the car body that absorbs the energy transmitted by the anti-collision beam through deformation when a collision accident occurs, and reduces the impact force. Therefore, the energy absorbing box needs to meet the crushing characteristics, energy absorbing characteristics and collision stability. The current energy-absorbing box products produced by 6005A alloy will collapse and crack when Rm≥280MPa, RP0.2≥260MPa, and A≥10%; after adjusting the aging process, crushing cracking still exists. Summary of the invention [0003] The technical problem to be solved by the present invention is to provide a 6005A aluminum alloy for automobiles suitable for automobile energy absorbing boxes, and also provide a 6005A aluminum alloy energy absorbing box for automobiles that sat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/02C22C1/03B22D11/04C22F1/043
CPCB22D11/003B22D11/04C22C1/026C22C1/03C22C21/02C22F1/002C22F1/043
Inventor 罗世兵卓振
Owner 山东友升铝业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com