A kind of multifunctional thermal insulation and antibacterial elastic silk and stockings

一种多功能、弹性丝的技术，应用在导电/抗静长丝制造、袜、连裤袜等方向，能够解决脱落、结合力弱等问题，达到弹性提高、提高抗拉伸强度的效果

Active Publication Date: 2022-04-15
HUNAN YANTUO NEW MATERIAL TECH CO LTD
View PDF19 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the functional substance is embedded in the fiber, it can overcome the binding force between it and the stocking fiber, but most functional substances can play a relevant role on the surface of the stocking fiber. For example, silver nanoparticles must be in contact with bacteria on the fiber surface to be able to Antibacterial is achieved, but the functional substance embedded on the surface is relatively weaker than the functional substance embedded in the interior due to a part of the exposed fiber, which still has the risk of falling off during washing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of multifunctional thermal insulation and antibacterial elastic silk and stockings

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1) Preparation of silver nanowires by solvothermal method:

[0031] In step 1), polyvinylpyrrolidone is uniformly dispersed in ethylene glycol by magnetic stirring to form a solution with a mass fraction of 4%, and ferric chloride and silver nitrate are dispersed in ethylene glycol respectively to form a mass fraction of 0.8% solution, quickly add 10mL ferric chloride and silver nitrate solutions to 150mL polyvinylpyrrolidone solution and stir evenly to form a dispersion, with an interval of no more than 1 minute; transfer the dispersion to a polytetrafluoroethylene reactor In 100°C, the reaction was incubated at 100° C. for 8 h, cooled at room temperature, centrifuged, and the supernatant liquid was discarded, washed three times with deionized water and ethanol to obtain silver nanowires. The silver nanowires have an average diameter of 112 nanometers and an average length of 1.2 microns.

[0032] 2) Preparation of silver nanowire airgel composite powder:

[0033] In...

Embodiment 2

[0037] The silver nanowire airgel composite powder prepared in Example 1 is used for spinning:

[0038] The thermoplastic polyurethane is dried and sliced, and then sent into a screw extruder with silver nanowire airgel composite powder and silane coupling agent KH550 to form a polyurethane melt at 220°C, and then added toluene diisocyanate trimer to obtain Mixed melt; wherein, the mass ratio of thermoplastic polyurethane, silver nanowire airgel composite powder, KH550, and toluene diisocyanate trimer is 100:0.5:1:5; the mixed melt is extruded by a screw extruder and Transport to the spinning position of the spinning box; use the spinning pump to quantitatively and evenly press the mixed melt to the spinneret with a pore size of 100 microns, and the fine stream of the mixed melt is extruded from the small hole of the spinneret, and the mixture melts at room temperature in the tunnel. Cooling makes multifunctional thermal insulation and antibacterial elastic yarn.

Embodiment 3

[0040] The silver nanowire airgel composite powder prepared in Example 1 is used for spinning:

[0041] After the thermoplastic polyurethane is dried, it is sliced, and then it is sent into the Screw extruder, forming polyurethane melt at 220°C, and then adding toluene diisocyanate trimer to obtain a mixed melt; among them, thermoplastic polyurethane, silver nanowire airgel composite powder, KH550, toluene diisocyanate trimer, The mass ratio of the plasticizer is 100:0.1:5:10:0.5; the mixed melt is extruded by the screw extruder and transported to the spinning position of the spinning box; the mixed melt is quantitatively and evenly pressed by the spinning pump To the spinneret with a hole diameter of 100 microns, the fine stream of mixed melt is extruded from the small hole of the spinneret, and cooled at room temperature in the tunnel to make a multifunctional thermal insulation antibacterial elastic yarn.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a multifunctional thermal insulation and antibacterial elastic silk and silk stockings. The elastic silk is prepared through the following steps: preparing silver nanowires by solvothermal method; preparing SiO 2 In the process of airgel, silver nanowires are added to prepare silver nanowire airgel composite powder; silver nanowire airgel composite powder, silane coupling agent, and small molecule polyisocyanate prepolymer are added as additives to molten thermoplastic polyurethane Among them, the multifunctional thermal insulation and antibacterial elastic yarn is obtained through spinning. The silane coupling agent of the present invention can make the composite powder and polyurethane further bonded firmly, so as to maintain heat preservation and antibacterial functions for a long time; a small molecule polyisocyanate prepolymer is added in the thermoplastic polyurethane spinning process to make it react with the broken substance The linear structure of the polyurethane is changed into a three-dimensional structure, thereby improving the elasticity.

Description

technical field [0001] The invention relates to a multifunctional heat-preserving and antibacterial elastic silk and silk stockings, in particular to an elastic silk and silk stockings which adopt airgel, silver nanowires and small molecule polyisocyanate prepolymers to realize heat preservation, antibacterial and elasticity improvement. Background technique [0002] Silk stockings generally refer to nylon thin socks, which can modify the feet and legs and increase the aesthetic feeling, so they are favored by consumers. As the market demand increases year by year, stockings with various functions also begin to appear on the market. In addition to retaining the original modification function, according to different occasions, different objects and different environments, stockings also have heat preservation, antibacterial, and antibacterial properties. Odor and high elasticity and other functions. [0003] Chinese patent CN103704890A discloses a sock with thermal insulatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/94D01F1/10D01F1/09D01F1/07A41B11/00A41B17/00
CPCD01F6/94D01F1/103D01F1/10D01F1/09D01F1/07A41B11/00A41B17/00A41B2400/34
Inventor 张丁日杜华军
Owner HUNAN YANTUO NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com