A kind of chromium-free passivation solution and passivation process for electro-galvanizing
A chromium-free passivation and electro-galvanizing technology, which is applied in the coating process of metal materials, can solve the problems of poor corrosion resistance, poor weather resistance and stability of passivation film, etc., to improve corrosion resistance, realize clean production, The effect of extending the service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0029] Embodiment 1 A kind of chromium-free passivation solution and passivation process thereof for electrogalvanizing
[0030] The chromium-free passivation solution for electrogalvanizing is composed of the following components and parts by weight: 10 parts of ammonium molybdate, 5 parts of sodium phosphate, 1 part of cerium nitrate, 15 parts of nitric acid with a mass concentration of 60%, tartaric acid 3 parts of sodium, 1.5 parts of complexing agent, 2 parts of film-forming adjuvant, and 40 parts of deionized water.
[0031] The complexing agent is composed of sodium alginate, polyacrylic acid and triethanolamine in a weight ratio of 1:10:15.
[0032] The film-forming auxiliary is composed of phytic acid, calcium silicate and linoleic acid in a weight ratio of 10:9:5.
[0033] The pH value of the passivation solution is 4.0, and the pH is adjusted with phosphoric acid.
[0034] The method for preparing a chromium-free passivation solution for electro-galvanizing includ...
Embodiment 2
[0038] Embodiment 2 A kind of chromium-free passivation solution and passivation process thereof for electrogalvanizing
[0039] The chromium-free passivation solution for electrogalvanizing is composed of the following components and parts by weight: 23 parts of ammonium molybdate, 12 parts of sodium phosphate, 3 parts of cerium nitrate, 25 parts of nitric acid with a mass concentration of 70%, tartaric acid 9 parts of sodium, 2.5 parts of complexing agent, 5 parts of film-forming adjuvant, and 55 parts of deionized water.
[0040] The complexing agent is composed of sodium alginate, polyacrylic acid and triethanolamine in a weight ratio of 2:8:13.
[0041] The film-forming auxiliary is composed of phytic acid, calcium silicate and linoleic acid in a weight ratio of 13:7:4.
[0042] The pH value of the passivation solution is 4.5, and the pH is adjusted with ammonia water.
[0043] The method for preparing a chromium-free passivation solution for electrogalvanizing includes...
Embodiment 3
[0047] Embodiment 3 A kind of chromium-free passivation solution and passivation process thereof for electrogalvanizing
[0048] The chromium-free passivation solution for electro-galvanizing is composed of the following components and parts by weight: 28 parts of ammonium molybdate, 15 parts of sodium phosphate, 5 parts of cerium nitrate, 30 parts of nitric acid with a mass concentration of 75%, tartaric acid 15 parts of sodium, 3.5 parts of complexing agent, 9 parts of film-forming adjuvant, and 70 parts of deionized water.
[0049] The complexing agent is composed of sodium alginate, polyacrylic acid and triethanolamine in a weight ratio of 4:6:8.
[0050] The film-forming auxiliary is composed of phytic acid, calcium silicate and linoleic acid in a weight ratio of 15:6:2.
[0051] The pH value of the passivation solution is 5.0, and the pH is adjusted with phosphoric acid.
[0052] The method for preparing a chromium-free passivation solution for electrogalvanizing inclu...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap