Film-coated metal plate

A technology of metal plate and film coating, which is applied in the field of building materials, can solve the problems of high cost of construction personnel, decrease of connection strength, corrosion of rivets, etc., and achieve the effects of saving timeliness, providing service life of materials, and saving construction period

Active Publication Date: 2020-06-05
苏州凯伦高分子新材料科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For the above-mentioned alternative, the cost of construction personnel is relatively high, and the price of materials should not be underestimated
[0004] In addition, since the color steel plates on the roof are connected by rivets, and the rivets are exposed, the rivets will be corroded as the use time increases, resulting in a decrease in the connection strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Film-coated metal plate
  • Film-coated metal plate
  • Film-coated metal plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0045] The technical solutions of the present invention will be clearly and completely described below in conjunction with the accompanying drawings. Apparently, the described embodiments are some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0046] Such as figure 1 and figure 2 As shown, the coated metal plate of the present application includes a metal plate 1, a polymer adhesive film layer 2 on the metal plate 1 and a TPO layer 3 on the polymer adhesive film layer 2;

[0047] TPO layer 3 includes the following components:

[0048] 20-100 parts by weight of ethylene-olefin copolymer;

[0049] 10-40 parts by weight of polypropylene;

[0050] 5-30 parts by weight of titanium dioxide;

[0051] 0-40 parts by weight of filler;

[0052] 0.1-2 pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a film-coated metal plate which comprises a metal plate body, a macromolecule adhesive film layer on the metal plate body and a TPO layer on the macromolecule adhesive film layer. The TPO layer comprises the following components: 20-100 parts of an ethylene-olefin copolymer; 10 to 40 parts of polypropylene; 5-30 parts of titanium dioxide; 0-40 parts of a filler; 0.1 to 2 parts of an antioxidant; and 0.1 to 2 parts of an anti-ultraviolet agent. The TPO layer and the metal plate are connected into a whole through the macromolecule adhesive film layer, the production process is simple, one-time forming is achieved, construction is convenient, operation is flexible, the construction period is effectively shortened, and the macromolecule adhesive film layer effectivelyavoids the environmental protection problem related to a traditional adhesive. A metal roofing board adopting the TPO layer can be designed with a durable life, and the conventional durable life is guaranteed for 10 years. The TPO layers of the adjacent steel plates are connected in a welded mode, and the problem that rivets are exposed outside and are prone to corrosion, so that the connecting strength is reduced is solved.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a film-coated metal plate. Background technique [0002] At present, the basic structure of light steel roof: metal plate, vapor barrier layer, rock wool or extruded board, non-woven fabric, PVC or TPO waterproof membrane, and the wind resistance strength of the roof should be tested and stipulated in the construction design. The material construction method should be constructed in sequence according to the above-mentioned structural levels, and no structural material can be missing, and the cost of construction personnel is relatively high. [0003] At present, there are two main schemes for roof maintenance: one is to directly replace the damaged color steel plate; the other is to repair the color steel plate with full-stick PVC or TPO waterproof membrane after polishing and derusting the color steel plate. For the above-mentioned alternative, the cost of construction person...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/085B32B15/18B32B15/20B32B7/12B32B27/12B32B27/18B32B27/20B32B27/32C08L23/08C08L23/12C08K3/22C08K3/34C08K5/13C08K13/02C09J123/08C09J123/02C09J123/06C09J153/02C09J151/06E04D3/35
CPCB32B15/085B32B15/18B32B15/20B32B7/12B32B27/12B32B27/18B32B27/20B32B27/32C08L23/0815C09J123/08C09J123/02C09J123/06C09J153/02C09J151/06C09J11/00E04D3/351B32B2264/102B32B2264/104B32B2270/00B32B2307/712B32B2307/7265B32B2419/06C08K2003/2241C08L2205/035C08L23/12C08K3/22C08K3/34C08K5/13C08K13/02C08L23/02C08L23/06C08L53/02C08L51/06
Inventor 李伟李忠人沈梦婷
Owner 苏州凯伦高分子新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products