A kind of chitosan modified nanofiber sustained-release antibacterial film and preparation method thereof

A chitosan modification and nanofiber technology, which is applied in fiber treatment, fiber chemical characteristics, rayon manufacturing, etc., can solve the problem of poor binding fastness between antibacterial agents and fibers, limiting the durability of antibacterial effects, swelling and disintegration, etc. problem, to achieve the effect of lasting effect, promoting dissolution and increasing content

Active Publication Date: 2021-11-16
广州大鱼创福科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, chitosan and polyethylene oxide have certain water solubility, and after forming the material, they will swell and disintegrate, which will also cause a burst release effect in the later stage of release.
In addition, the existing antibacterial fibers have limited the durability of their antibacterial effects due to the poor combination of antibacterial agents and fibers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of chitosan modified nanofiber sustained-release antibacterial film and preparation method thereof
  • A kind of chitosan modified nanofiber sustained-release antibacterial film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preparation method of chitosan modified nanofiber sustained-release antibacterial film, comprising the steps of:

[0027] 1. Add 0.7g of soybean lecithin, 0.2g of cholesterol and 0.4ml of terpinen-4-ol into 20ml of chloroform, stir well to dissolve it completely, remove the chloroform by rotary evaporation at room temperature, and then use a syringe at a rate of 5ml / min Inject it into 6 times the volume of water containing 3g / L Tween 80, then homogenize at a speed of 11000r / min, dialyze and concentrate to 1 / 6 volume with 15g / L polyvinyl alcohol 6000 solution to obtain pine oil En-4-ol liposomes;

[0028] 2. Add 1g of chitosan powder with a relative molecular weight of 30kDa and a deacetylation degree of 90%, 1.5g of benzenesulfonyl chloride, 1.5g of sodium hydroxide, 0.2g of 15-crown ether-5 and 0.15g of DMAP into 60ml of dichloromethane React at 50°C for 8 hours, then wash the reactant with a sodium hydroxide solution with a concentration of 8g / L, and collect the pr...

Embodiment 2

[0031] A preparation method of chitosan modified nanofiber sustained-release antibacterial film, comprising the steps of:

[0032] 1. Add 0.5g of soybean lecithin, 0.1g of cholesterol and 0.2ml of terpinen-4-ol into 20ml of chloroform, stir well to dissolve it completely, remove the chloroform by rotary evaporation at room temperature, and then use a syringe at a rate of 3ml / min Inject it into 5 times the volume of water containing 2g / L Tween 20, then homogenize at a speed of 10000r / min, dialyze and concentrate to 1 / 5 volume with 10g / L polyvinyl alcohol 6000 solution to obtain pine oil En-4-ol liposomes;

[0033] 2, 1g relative molecular weight is 20kDa, and deacetylation degree is 80% chitosan powder, 1g benzenesulfonyl chloride, 1g sodium hydroxide, 0.1g 15-crown ether-5 and 0.1g DMAP add 50ml dichloromethane at 40 React at ℃ for 6 hours, then wash the reactant with a sodium hydroxide solution with a concentration of 5g / L, and collect the precipitate by centrifugation;

[...

Embodiment 3

[0036] A preparation method of chitosan modified nanofiber sustained-release antibacterial film, comprising the steps of:

[0037] 1. Add 0.8g of soybean lecithin, 0.3g of cholesterol and 0.5ml of terpinen-4-ol into 20ml of chloroform, stir well to dissolve it completely, remove the chloroform by rotary evaporation at room temperature, and then use a syringe at a rate of 7ml / min. Inject it into 8 times the volume of water containing 5g / L Span 80, then homogenize at a speed of 12000r / min, dialyze and concentrate to 1 / 8 volume with 20g / L polyvinyl alcohol 6000 solution to obtain pine oil En-4-ol liposomes;

[0038] 2, 1g relative molecular weight is 50kDa, and deacetylation degree is 100% chitosan powder, 2g benzenesulfonyl chloride, 1.8g sodium hydroxide, 0.3g 18-crown ether-6 and 0.2g DMAP add 75ml dichloromethane in React at 60°C for 10 hours, then wash the reactant with a sodium hydroxide solution with a concentration of 10g / L, and collect the precipitate by centrifugation;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of textile material processing, and discloses a chitosan-modified nanofiber sustained-release antibacterial film and a preparation method thereof. The preparation method comprises: preparing terpinene-4-alcohol liposome; adding chitosan powder, benzenesulfonyl chloride, sodium hydroxide, crown ether and DMAP to dichloromethane for reaction, and washing the reactant with sodium hydroxide solution Collect the precipitate; dissolve the precipitate and polyethylene oxide in 90% acetic acid solution, stir well, add terpinene-4-alcohol liposome, and electrospin to form chitosan-modified nanofiber slow-release antibacterial film. The release of terpinene-4-alcohol in the nanofiber slow-release antibacterial film prepared by the invention is longer and its antibacterial effect is better.

Description

technical field [0001] The invention relates to the technical field of textile material processing, in particular to a chitosan modified nanofiber slow-release antibacterial film and a preparation method thereof. Background technique [0002] Chitosan is the second most abundant polysaccharide in nature—the deacetylation product of chitin, which is insoluble in water and alkaline solution, but soluble in most dilute acids, and exists in the shells and shells of crustaceans and arthropods. In the cell walls of lower plants such as fungi and algae. Chitosan is rich in resources and has the advantages of good biocompatibility, biodegradability, adhesion, antibacterial, moisture retention, non-toxic and non-polluting properties. The chemical structure of chitosan is similar to that of cellulose. They have good adsorption and compatibility. The hydroxyl groups of chitosan and some of the amino groups form many intermolecular hydrogen bonds with the hydroxyl groups of fibers, whi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04H3/005D04H3/033D01D5/00C08B37/08D01F9/00D01F1/10
CPCC08B37/003D01D5/003D01D5/0092D01F1/10D01F1/103D01F9/00D04H3/005D04H3/033
Inventor 葛彦汤佳鹏付译鋆谢雅婷陈苹谢浩月
Owner 广州大鱼创福科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com