Silane-alumina wear-resistant coating on surface of willow handicrafts

A technology for wood handicrafts and wear-resistant coatings, applied in the field of handicrafts, can solve the problems of inability to protect wood handicrafts, poor wear resistance, coating peeling, etc., and achieves increased water solubility and hydration properties, high wear resistance, and improved The effect of adhesion

Inactive Publication Date: 2020-07-03
阜阳文鼎工艺品有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention is environmentally friendly, has good water resistance and enhances the surface hardness of the material; however, it mainly uses linseed oil as a binder, and its wear resistance is poor. Good protection for wooden crafts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] A silane-alumina wear-resistant coating on the surface of willow handicrafts, treated with vinyltrimethoxysilane and mixed with 2-acrylamido-2-methylpropanesulfonic acid / epoxy resin solution to obtain a composite solution;

[0061] Under the action of a catalyst, the composite liquid is modified with 2-methyl-2-acrylic acid-2-isocyanatoethyl ester to obtain a composite material, and the preparation method of vinyltrimethoxysilane-treated alumina is as follows:

[0062] First, evenly disperse the nano-alumina particles into the ethanol solution, then add vinyltrimethoxysilane, heat to 50°C, stir for 20min, then add graphene, continue stirring for 1 hour, then perform suction filtration and wash with water , dried to constant weight, that is. The average particle diameter of the nano-alumina particles is 100nm; the mass fraction of the ethanol solution is 20%; the mixing ratio of the nano-alumina particles and the ethanol solution is 80g:400mL. The mass ratio of the viny...

Embodiment 2

[0070] A silane-alumina wear-resistant coating on the surface of willow handicrafts, treated with vinyltrimethoxysilane and mixed with 2-acrylamido-2-methylpropanesulfonic acid / epoxy resin solution to obtain a composite solution;

[0071] Under the action of a catalyst, the composite liquid is modified with 2-methyl-2-acrylic acid-2-isocyanatoethyl ester to obtain a composite material, and the preparation method of vinyltrimethoxysilane-treated alumina is as follows:

[0072] First, evenly disperse the nano-alumina particles into the ethanol solution, then add vinyltrimethoxysilane, heat to 55°C, stir for 20min, then add graphene, continue stirring for 1 hour, then perform suction filtration and wash with water , dried to constant weight, that is. The average particle diameter of the nano-alumina particles is 100nm; the mass fraction of the ethanol solution is 20%; the mixing ratio of the nano-alumina particles and the ethanol solution is 80g:450mL. The mass ratio of the viny...

Embodiment 3

[0079] A silane-alumina wear-resistant coating on the surface of willow handicrafts, treated with vinyltrimethoxysilane and mixed with 2-acrylamido-2-methylpropanesulfonic acid / epoxy resin solution to obtain a composite solution;

[0080] Under the action of a catalyst, the composite liquid is modified with 2-methyl-2-acrylic acid-2-isocyanatoethyl ester to obtain a composite material, and the preparation method of vinyltrimethoxysilane-treated alumina is as follows:

[0081] First, evenly disperse the nano-alumina particles into the ethanol solution, then add vinyltrimethoxysilane, heat to 52°C, stir for 20min, then add graphene, continue stirring for 1 hour, then perform suction filtration and wash with water , dried to constant weight, that is. The average particle diameter of the nano-alumina particles is 100nm; the mass fraction of the ethanol solution is 20%; the mixing ratio of the nano-alumina particles and the ethanol solution is 80g:410mL. The mass ratio of the viny...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a silane-alumina wear-resistant coating on the surface of willow handicrafts, and relates to the technical field of handicrafts. The preparation method comprises the followingsteps: mixing alumina treated by vinyl trimethoxysilane with a 2-acrylamide-2-methylpropanesulfonic acid/epoxy resin solution to obtain a composite solution; under the action of a catalyst, modifyingthe composite solution by 2-methyl-2-acrylic acid-2-isocyanatoethyl ester to obtain a composite material; brushing the composite material on the surface of a willow handicraft; placing the brushed willow artware in a drying chamber, and drying to form a wear-resistant coating on the surface of the willow artware. The wear-resistant coating formed on the surface of the willow handicraft has a lowerfriction coefficient, and better wear resistance.

Description

technical field [0001] The invention belongs to the technical field of handicrafts, in particular to a silane-alumina wear-resistant coating on the surface of willow handicrafts. Background technique [0002] There are many shapes and patterns of wooden handicrafts, beautiful and generous, light in weight, can be placed or hung at will, and the cost is low, so it is more and more popular with consumers. However, due to the wood material of handicrafts, it is easy to absorb water, deform, and get moldy due to moisture. , Breeding bacteria, seriously affecting the consumer experience and limiting the development of wooden handicrafts. [0003] Therefore, in the prior art, various protective treatments are carried out on the surface of wooden handicrafts to improve their surface properties. Among them, coating paint on the surface of wooden handicrafts is one of the more commonly used treatment methods, for example: CN 109536021 A, disclosed in the present invention A wood sur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D4/02C09D7/62B05D7/06B05D7/24
CPCB05D7/06B05D7/24C09D4/06C09D7/62
Inventor 余秀芳
Owner 阜阳文鼎工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap