A kind of high-hardness high-entropy alloy coating and its preparation method and application

A high-entropy alloy, high-hardness technology, applied in the field of high-entropy alloys, can solve the problems of low strength and hardness, great influence on wear performance, poor wear resistance, etc., and achieve the effect of good high temperature wear resistance.

Active Publication Date: 2022-04-05
NANJING INST OF TECH +2
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After research, it was found that CoCrFeMnNi high-entropy alloy with FCC solid solution structure has excellent thermal stability and corrosion resistance, but its strength and hardness are low, and its wear resistance is poor, especially the friction temperature on the wear performance of CoCrFeMnNi high-entropy alloy coating. Greater impact

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-hardness high-entropy alloy coating and its preparation method and application
  • A kind of high-hardness high-entropy alloy coating and its preparation method and application
  • A kind of high-hardness high-entropy alloy coating and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A high-hardness high-entropy alloy coating, the composition and atomic ratio are as follows: CoCrFeMnNiTi x V y , wherein x=0.3~1, y=0.1~1. Preferably, x:y=(0.5˜1):1. Further preferably, x:y=1:1. That is, the composition of the high-entropy alloy coating in this embodiment is: CoCrFeMnNiTiV.

[0041] The CoCrFeMnNi high-entropy alloy powder is spherical, the particle size of the spherical powder is 53-150 μm, and the purity is greater than 99.5wt.%; the Ti powder is spherical or elliptical, the particle size is 19-80 μm, and the purity is greater than 99.9wt.%. Irregular rhombus, the particle size is 5-30 μm, and the purity is greater than 99.9wt.%.

[0042] A method for preparing a high-hardness high-entropy alloy coating, comprising the following steps,

[0043] S01, powder mixing: put the prepared CoCrFeMnNiTiV alloy powder in a mixer for at least 4 hours, and the mixing frequency is 50-100 Hz;

[0044] S02, drying: place the mixed alloy powder in a drying oven...

Embodiment 2

[0072] The difference between this embodiment and embodiment 1 is only:

[0073] A high-hardness high-entropy alloy coating, the composition and atomic ratio are as follows: CoCrFeMnNiTi 0.3 V 0.6 .

[0074] The parameters of the plasma cladding technology are: working current: 130A; working voltage: 25V; plasma arc forward speed: 75mm / min; plasma arc swing speed: 900mm / min; powder feeding rate: 5g / min; ion gas rate: 1.2L / min; powder feeding gas rate: 1.5L / min; protective gas rate: 6L / min; ion gas, powder feeding gas and protective gas are all argon.

Embodiment 3

[0076] The difference between this embodiment and embodiment 1 is only:

[0077] A high-hardness high-entropy alloy coating, the composition and atomic ratio are as follows: CoCrFeMnNiTi 0.6 V.

[0078] The parameters of the plasma cladding technology are: working current: 190A; working voltage: 40V; plasma arc forward speed: 130mm / min; plasma arc swing speed: 1500mm / min; powder feeding rate: 20g / min; ion gas rate: 3.5L / min; powder feeding gas rate: 4.2L / min; protective gas rate: 12L / min; ion gas, powder feeding gas and protective gas are all argon.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-hardness high-entropy alloy coating and its preparation method and application. The composition and atomic ratio of the high-entropy alloy coating are as follows: CoCrFeMnNiTi x V y , wherein x=0.3~1, y=0.1~1. The high-entropy alloy coating can be applied to high-temperature friction and wear materials, especially can be applied to milling cutter coating, high-temperature rotating shaft coating or high-temperature friction disc coating. The preparation method of the high-entropy alloy coating includes powder mixing, drying, pretreatment of base material and cladding coating. The plasma cladding CoCrFeMnNiTiV high-entropy alloy coating prepared by the invention is composed of a V-rich BCC1 phase and a Ti-rich BCC2 phase, and its solidification structure is a cellular dendrite structure. The average hardness of CoCrFeMnNiTiV high-entropy alloy coating reached 942.8HV 0.3 , 7.5 times that of the base Q235 steel.

Description

technical field [0001] The invention relates to a high-hardness high-entropy alloy coating and a preparation method and application thereof, belonging to the technical field of high-entropy alloys. Background technique [0002] The mechanical properties (strength, hardness, thermal stability, corrosion resistance, low-temperature mechanical properties, etc.) and physical properties (magnetic properties) of equiatomic ratio CoCrFeMnNi high-entropy alloys have been studied in depth. After research, it was found that CoCrFeMnNi high-entropy alloy with FCC solid solution structure has excellent thermal stability and corrosion resistance, but its strength and hardness are low, and its wear resistance is poor, especially the friction temperature on the wear performance of CoCrFeMnNi high-entropy alloy coating. Greater impact. [0003] Wear is one of the main causes of component failure. It is of great significance to study the wear law of materials and improve their wear resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C24/10C22C30/00
CPCC23C24/106C22C30/00
Inventor 张保森张显程程江波王章忠朱帅帅俞亚秋张志佳陆雯婷沈天瀛
Owner NANJING INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products