A continuous casting method for aluminum-containing peritectic high-strength automobile steel

An automotive steel, high-strength technology, applied in the field of continuous casting of aluminum-containing peritectic high-strength automotive steel, can solve the problems of slab cracks, unsteady pouring, water plugging, etc., to improve lubrication, solve continuous casting problems, and improve lubrication. Effect

Active Publication Date: 2021-07-23
SHOUGANG CORPORATION
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a continuous casting method of aluminum-containing peritectic high-strength automobile steel to solve or partly solve the problem that the high-strength automobile steel containing more aluminum peritectic is prone to cracks and water blocking during continuous casting, and cannot be poured stably technical problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A continuous casting method for aluminum-containing peritectic high-strength automobile steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] In order to enable those skilled in the technical field to which the application belongs to understand the application more clearly, the technical solutions of the application will be described in detail below through specific embodiments in conjunction with the accompanying drawings.

[0029] During slab continuous casting, the tundish receives the molten steel transferred from the ladle, and then distributes it to each crystallizer through the tundish nozzle; the molten steel forms a certain thickness in the crystallizer through the cooling process control of the cooling water in the crystallizer. The casting slab of the primary slab shell; then the slab is stably pulled out from the crystallizer according to a certain pulling speed, and the slab is further cooled when passing through the secondary cooling section of the continuous casting machine to solidify the inside of the slab; then it is drawn and straightened , cutting, and finally obtain the finished slab.

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a continuous casting method of aluminum-containing peritectic high-strength automobile steel, which comprises: opening a stopper rod, an upper nozzle and three channels between plates in a tundish during the molten steel pouring process of aluminum-containing peritectic high-strength automobile steel Argon blowing; mold flux is used for protective pouring, and the chemical composition of mold flux includes: Al 2 o 3 : 1.2%~1.6%, CaO: 35%~45%, SiO 2 : 30%~35%, F: 8%~12%, Na 2 O+K 2 O: 1.0% to 2.0%, MgO: 0.8% to 1.0%, C: 4% to 6%. The process is used to control the heat flux density of the meniscus region of the crystallizer to 1.0-2.0MW·m ‑2 ; The continuous casting machine adopts the preset casting speed to pull out the billet of aluminum-containing peritectic high-strength automobile steel; the second cooling section of the continuous casting adopts the second preset weak cooling process. Through the above scheme, the surface cracks and bonding defects of the slab are significantly reduced.

Description

technical field [0001] The application relates to the technical field of high-strength automobile steel smelting, in particular to a continuous casting method for aluminum-containing peritectic high-strength automobile steel. Background technique [0002] The development trend of modern automobiles is light weight, energy saving, anti-corrosion, safety and comfort. Reducing energy consumption, reducing environmental pollution and saving limited resources is a very important and urgent problem that people are facing today. Reducing the weight of automobiles is one of the important measures to improve the fuel economy and save energy consumption of automobiles. Data show that for every 10% reduction in vehicle mass, fuel consumption will drop by 6-8%, and emissions will drop by 4%. Aluminum-containing peritectic high-strength automotive steel is based on the traditional dual-phase steel ferrite plus martensite dual-phase structure, introducing a certain amount of retained aus...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/111B22D11/117B22D11/053B22D11/055B22D11/07B22D11/22
CPCB22D11/053B22D11/055B22D11/07B22D11/111B22D11/117B22D11/22B22D11/225
Inventor 罗衍昭季晨曦何文远关顺宽张志敏杨晓山王胜东刘延强杨敬铭王宝动杨春宝曾智安泽秋赵长亮
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com