Antibacterial HDPE plastic chair suitable for outdoor use and preparation method thereof

A plastic and outdoor technology, applied in the field of plastic chairs, can solve the problems of high human toxicity, poor temperature resistance, environmental pollution, etc., and achieve the effect of good processing performance, good stability and dispersion, and simple molding process

Pending Publication Date: 2020-08-18
陈志益
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the preparation method of HDPE antibacterial plastics is mainly made by adding a small amount of antibacterial agents, blending and compounding, and its active ingredients are antibacterial agents. These antibacterial agents include inorganic antibacterial agents and organic antibacterial agents. Plastic thermoforming proce

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial HDPE plastic chair suitable for outdoor use and preparation method thereof
  • Antibacterial HDPE plastic chair suitable for outdoor use and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An antibacterial HDPE plastic chair suitable for outdoor use, its raw materials include: high-density polyethylene 100kg, polypropylene 15kg, ethylene-vinyl acetate copolymer 6kg, carboxylated polypropylene 1kg, cedar oil 2kg, epoxy soybean oil 0.5kg , sodium stearate 1kg, magnesium oxide 1kg, highly stable antibacterial agent 4kg, vinyl succinic anhydride grafted polypropylene 1kg, diphenylamine 2kg, phenyl o-hydroxybenzoate 1kg.

[0027] The melt flow rate (230°C / 2.16kg) of polypropylene is 90g / 10min, and the density is 0.88g / cm 3 .

[0028] The highly stable antibacterial agent is prepared by the following process: 30kg of attapulgite is sent into a drying furnace, roasted at a temperature of 500°C, cooled to obtain calcined attapulgite with a density of 0.74g / cm3, crushed through a 100-mesh sieve, and sent into a 100kg In a hydrochloric acid solution with a concentration of 5mol / L, stir at a temperature of 80°C for 1h, filter, wash, dry, and send it into an ethanol...

Embodiment 2

[0034] An antibacterial HDPE plastic chair suitable for outdoor use, its raw materials include: high-density polyethylene 100kg, polypropylene 25kg, ethylene-vinyl acetate copolymer 2kg, carboxylated polypropylene 2kg, cedar oil 1kg, epoxy soybean oil 1.2kg , sodium stearate 0.2kg, magnesium oxide 2kg, highly stable antibacterial agent 2kg, acrylic acid grafted polypropylene 2kg, p-phenylenediamine 1kg, 2-hydroxy-4-methoxybenzophenone 2kg.

[0035] The melt flow rate (230°C / 2.16kg) of polypropylene is 96g / 10min, and the density is 0.85g / cm 3 .

[0036] The highly stable antibacterial agent is prepared by the following process: 20kg of attapulgite is sent into a drying furnace, roasted at a temperature of 600°C, cooled to obtain calcined attapulgite with a density of 0.7g / cm3, crushed through a 200-mesh sieve, and sent into a 50kg In a hydrochloric acid solution with a concentration of 5.6mol / L, stir at a temperature of 70°C for 2h, filter, wash, dry, and send it into a soluti...

Embodiment 3

[0042] An antibacterial HDPE plastic chair suitable for outdoor use, its raw materials include: high-density polyethylene 100kg, polypropylene 18kg, ethylene-vinyl acetate copolymer 5kg, carboxylated polypropylene 1.3kg, cedar oil 1.8kg, epoxy soybean oil 0.6kg, sodium stearate 0.8kg, magnesium oxide 1.3kg, highly stable antibacterial agent 3.5kg, citraconic anhydride grafted polypropylene 1.2kg, N-isopropyl-N'-phenyl-p-phenylenediamine 1.7kg, Phenyl o-hydroxybenzoate 1.2kg.

[0043] The melt flow rate (230°C / 2.16kg) of polypropylene is 92g / 10min, and the density is 0.87g / cm 3 .

[0044] The highly stable antibacterial agent is prepared by the following process: 26kg of attapulgite is sent into a drying furnace, roasted at a temperature of 530°C, cooled to obtain calcined attapulgite with a density of 0.73g / cm3, crushed through a 140-mesh sieve, and sent into 80kg In a hydrochloric acid solution with a concentration of 5.2mol / L, stir at a temperature of 77°C for 1.3h, filter...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melt flow rateaaaaaaaaaa
Densityaaaaaaaaaa
Melt flow rateaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antibacterial HDPE plastic chair suitable for outdoor use. The plastic chair comprises the following components in parts by weight: 100 parts of high density polyethylene, 15-25 parts of polypropylene, 2-6 parts of an ethylene-vinyl acetate copolymer, 1-2 parts of carboxylated polypropylene, 1-2 parts of cedar oil, 0.5-1.2 parts of epoxidized soybean oil, 0.2-1 part of sodium stearate, 1-2 parts of magnesium oxide, 2-4 parts of a high-stability antibacterial agent, 1-2 parts of a compatilizer, 1-2 parts of an antioxidant and 1-2 parts of a light stabilizer; wherein the high-stability antibacterial agent is obtained by acidolysis of calcined attapulgite and combination with 8-hydroxyquinoline; the compatilizer is a graft of polypropylene and unsaturated acid or agraft of polypropylene and anhydride; the unsaturated acid is acrylic acid or methacrylic acid, and the anhydride is maleic anhydride, fumaric acid, itaconic acid, citraconic acid, citraconic anhydride or vinyl succinic anhydride. The invention further discloses a preparation method of the antibacterial HDPE plastic chair suitable for outdoor use.

Description

technical field [0001] The invention relates to the technical field of plastic chairs, in particular to an antibacterial HDPE plastic chair suitable for outdoor use and a preparation method thereof. Background technique [0002] High-density polyethylene (HDPE) has good mechanical properties, and its initial relative elongation is as high as 500-600%. HDPE is widely used in packaging materials, daily necessities, office supplies, medical supplies, gas transmission, water supply, sewage, Agricultural irrigation, oil field, chemical industry, mining, post and telecommunications and other fields. In the daily necessities industry, plastic tables and chairs made of HDPE are used outdoors in high-humidity, high-salt atmosphere environments such as beaches, and are better than tables and chairs made of other materials in terms of chemical stability, water resistance and service life. Has incomparable advantages. [0003] With the improvement of people's living standards, people ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L23/12C08L23/08C08L23/26C08L91/00C08L51/06C08K13/06C08K9/02C08K7/26C08K3/22C08K5/098C08K5/3437C08K5/18C08K5/134C08K5/132C08K5/5399
CPCC08L23/06C08L2205/035C08L2201/08C08L2207/062C08K2003/222C08L23/12C08L23/0853C08L23/26C08L91/00C08L51/06C08K13/06C08K9/02C08K7/26C08K3/22C08K5/098C08K5/3437C08K5/18C08K5/1345C08K5/132C08K5/5399
Inventor 胡森川杨曦罗万象陈志益
Owner 陈志益
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap