A spray wood paint for uv-led curing

A UV-LED, wood paint technology, applied in coatings, polyester coatings, polyurea/polyurethane coatings, etc., can solve problems such as low color repair efficiency and paint waste

Active Publication Date: 2022-06-28
上海展辰涂料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a spray wood paint for UV-LED curing, to solve the problems of low color correction efficiency and serious paint waste caused by manual painting in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A spray wood paint for uv-led curing
  • A spray wood paint for uv-led curing
  • A spray wood paint for uv-led curing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～6

[0026] A kind of sprayed wood lacquer suitable for UV-LED curing, the mass fractions of the raw materials in Examples 1 to 6 are listed in Table 2.

Embodiment 1

[0027] In Example 1, the weight ratio of the modified polyester acrylate resin and the hexafunctional aliphatic urethane acrylic resin is a mixture of 2.5:1; among the photoinitiators, photoinitiator TPO: photoinitiator ITX=2.0:1; active dilution The agent is HDDA and DPGDA=1:3.4; the weight ratio of BYK-405 and AEROSIL R972 in the anti-settling agent is 1:3.

Embodiment 2

[0028] In Example 2, the weight ratio of the mixture of the modified polyester acrylate resin and the hexafunctional aliphatic urethane acrylic resin is = 2.9:1; the photoinitiator TPO in the photoinitiator: the photoinitiator ITX = 2.5:1; the active The diluents are all DPGDA; the weight ratio of BYK-405 and AEROSIL R 972 in the anti-settling agent is 1:3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A spray wood paint for UV-LED curing of the present invention comprises the following raw materials in mass fraction: acrylic resin: 30%-45%, photoinitiator: 5%-8%, talcum powder: 10%-20% , dispersant: 0.1% to 2%, reactive diluent: 36% to 46%; the weight ratio of the acrylic resin to modified polyester acrylate resin and hexafunctional aliphatic polyurethane acrylic resin is (2.0 to 3.5): 1 mixture. The invention uses a reciprocating automatic spraying machine for fast coating, infrared leveling lines for leveling, and LED curing equipment for curing, which not only sprays more evenly, saves time and space to be dried, and reduces energy consumption; it does not contain volatile organic compounds , greatly reducing environmental pollution; reducing man-made instability; less paint waste, saving paint and labor costs, and improving the market competitiveness of products.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a sprayed wood paint for UV-LED curing. Background technique [0002] The first patent for ultraviolet (UV) curing coatings was born in 1947. After more than half a century of development, UV curing coatings have become a relatively mature technology, especially with the improvement of people's awareness of environmental protection, production and researchers pay more attention Development and application of UV-curable coatings. [0003] UV light-curing coating is a kind of high-efficiency, environmental protection, energy-saving and high-quality light-curing material. UV-curing coating is a kind of green and environment-friendly coating, which fully conforms to the "4E" principle. Generally, the energy consumption of UV curing is 1 / 5 of that of thermal curing. , and the UV-curable coating contains less volatile components and less pollution, which can reduce the co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/06C09D175/14C09D7/61C09D7/45C09D7/47
CPCC09D167/06C09D7/61C09D7/45C09D7/47C08L2205/035C08L2201/08C08L75/14C08L77/00C08L33/00C08K3/34C08K3/36
Inventor 胡晗周琼辉胡石成
Owner 上海展辰涂料有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com