A Nixing pottery and pottery clay technology, applied in the field of Nixing pottery pottery clay partial pressure compaction process, can solve the problems of single material, low efficiency, inability to improve product output efficiency, etc., to reduce shrinkage, improve strength, The effect of improving product output efficiency

Pending Publication Date: 2020-11-24
广西钦州市古朝坭兴陶制作有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in the existing Nixing pottery clay partial pressure compacting process, in the raw material allocation of clay, the materials used are relatively single, and a large amount of manpower is still used in the process of processing and grinding, resulting in low production efficiency. At the same time, the compaction process of ceramic clay often adopts a single manual rolling and pressing process, which makes it impossible to improve the product output efficiency. Therefore, a Nixing ceramic clay partial pressure compaction process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nixing pottery clay partial pressure type pressing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] see figure 1 , the present invention provides a technical solution: a Nixing pottery mud partial pressure compaction process, comprising the following steps:

[0030] S1. Clay raw material preparation: 3 parts of purple clay, 3 parts of white clay, 1 part of mineral powder, 1 part of clay mineral, 1 part of feldspar and 0.5 part of metal oxide. After mixing the above ingredients, enter the next step;

[0031] S2. Making pottery clay: use a finely processed ball mill, place silicon balls and pottery clay raw materials in the ball mill, use the machine to roll to make the silica balls and mud rub against each other, grind the pottery mud raw materials, and put them into a uniform After mixing and sieving in the softener, enter the next step;

[0032] S3. Clay clay partial pressure compaction; place the mud material in the die groove in the compaction device, wherein the pressure film groove is divided into three levels, and the mud material is divided in turn through the...

Embodiment 2

[0044] see figure 1 , the present invention provides a technical solution: a Nixing pottery mud partial pressure compaction process, comprising the following steps:

[0045] S1. Clay raw material preparation: 7 parts of purple clay, 7 parts of white clay, 3 parts of mineral powder, 3 parts of clay mineral, 3 parts of feldspar and 0.1 part of metal oxide. After mixing the above ingredients, enter the next step;

[0046] S2. Making pottery clay: use a finely processed ball mill, place silicon balls and pottery clay raw materials in the ball mill, use the machine to roll to make the silica balls and mud rub against each other, grind the pottery mud raw materials, and put them into a uniform After mixing and sieving in the softener, enter the next step;

[0047] S3. Clay clay partial pressure compaction; place the mud material in the die groove in the compaction device, wherein the pressure film groove is divided into three levels, and the mud material is divided in turn through ...

Embodiment 3

[0059] see figure 1 , the present invention provides a technical solution: a Nixing pottery mud partial pressure compaction process, comprising the following steps:

[0060] S1. Clay raw material preparation: 5 parts of purple red mud, 5 parts of white clay, 2 parts of mineral powder, 2 parts of clay mineral, 2 parts of feldspar and 0.8 part of metal oxide. After mixing the above ingredients, enter the next step;

[0061] S2. Making pottery clay: use a finely processed ball mill, place silicon balls and pottery clay raw materials in the ball mill, use the machine to roll to make the silica balls and mud rub against each other, grind the pottery mud raw materials, and put them into a uniform After mixing and sieving in the softener, enter the next step;

[0062] S3. Clay clay partial pressure compaction; place the mud material in the die groove in the compaction device, wherein the pressure film groove is divided into three levels, and the mud material is divided in turn throu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nixing pottery clay partial pressure type pressing process. The nixing pottery clay partial pressure type pressing process comprises the following steps that S1, pottery clayraw materials are prepared, specifically, 3-7 parts of purple red clay, 3-7 parts of white clay, 1-3 parts of mineral powder, 1-3 parts of clay minerals, 1-3 parts of feldspar and 0.5-1 part of metaloxide are mixed, and after the ingredients are mixed, and the next step is carried out; and S2, pottery clay materials are manufactured, specifically, a ball mill which is processed and finely groundis used, silicon balls and the pottery clay raw materials are placed in the ball mill, the silicon balls and the clay materials are rubbed with each other by utilizing the rolling of a machine, and after the pottery clay raw materials are finely ground, the prepared pottery clay raw materials are finely ground by using the ball mill which is processed and finely ground, the clay materials are placed into a homogenizer to be mixed and sieved, then the clay materials are placed in a three-stage pressing die groove in a pressing device for partial pressure pressing, and leftover materials overflowing from a die after partial pressure are subjected to edge cutting by using a cutter, so that the integrity of the pottery clay is guaranteed. By means of the method, the subsequent forming, cooling and shaping efficiency of the pottery clay can be greatly improved.

Description

technical field [0001] The invention relates to the technical field of Nixing pottery clay technology, in particular to a Nixing pottery clay partial pressure compacting process. Background technique [0002] As we all know, Qinzhou Nixing pottery, referred to as Nixing pottery, uses the unique purple red pottery clay on the east and west banks of the Qinjiang River in Qinzhou City, Guangxi as raw material. Disperse, dissolve, oxidize, and reach a weathered state, and then crush the soil and mix it at a ratio of 4:6 to make pottery blanks. Nixing pottery uses the unique purple red clay on both sides of the Qinjiang River as raw material. The hard is the bone, mixed according to the soft six hard four, and the flesh and bone can support each other to be the top grade. Because it is hidden deep in the mountain hinterland. Natural clean, fine mud. It is green and environmentally friendly, and contains more than a dozen rich minerals beneficial to the human body, such as iron...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B28B3/02B28B17/02B28B11/12C04B33/04C04B33/13
CPCB28B3/02B28B11/12B28B17/026C04B33/04C04B33/13C04B33/131C04B2235/602
Inventor 李雨芬罗家华
Owner 广西钦州市古朝坭兴陶制作有限公司