The preparation method of a bamboo pulp meal, bamboo pulp meal and fiber

A bamboo pulp and bamboo fiber technology, which is applied in fiber raw material processing, cellulose raw material pulping, cellulose pulp post-processing and other directions, can solve the problems of low bamboo pulp quality and poor fiber quality, and achieve better fiber quality. , Good spinnability and good physical index

Active Publication Date: 2022-08-05
HEBEI JIGAO CHEM FIBER
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to overcome the deficiencies in the prior art, provide a preparation method of bamboo pulp, bamboo pulp and fiber, to solve the problem that the existing bamboo pulp has low quality and the quality of the obtained fiber is poor technical issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • The preparation method of a bamboo pulp meal, bamboo pulp meal and fiber
  • The preparation method of a bamboo pulp meal, bamboo pulp meal and fiber
  • The preparation method of a bamboo pulp meal, bamboo pulp meal and fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Preparation Process:

[0028] (1) Material preparation: take an appropriate amount of bamboo for use;

[0029] (2) cutting material: adopt the mode of oblique cutting to cut the bamboo of step (1), and the length is controlled at 20mm;

[0030] (3) cooking: the bamboo material of step (2) is added in the container to cook, and cooking liquid is the sodium hydroxide solution that concentration is 15%, and cooking pressure is 0.7MPa, and cooking temperature is 168 ℃, and cooking time is 130min;

[0031] (4) bleaching: the product of step (3) is bleached, and the bleaching solution is a hydrogen peroxide solution with a concentration of 1.5%, the bleaching temperature is 65°C, and the bleaching time is 100min;

[0032] (5) classification: utilize classification sieve to screen out the bamboo fiber of 0.5mm from the product of step (4);

[0033] (6) Papermaking: the bamboo fiber of step (5) is copied into bamboo pulp.

[0034] Product performance:

[0035] The methyl fi...

Embodiment 2

[0038] Preparation Process:

[0039] (1) Material preparation: take an appropriate amount of bamboo for use;

[0040] (2) cutting material: adopt the mode of oblique cutting to cut the bamboo of step (1), and the length is controlled at 25mm;

[0041] (3) cooking: the bamboo material of step (2) is added in the container to cook, and the cooking liquid is the sodium hydroxide solution that concentration is 15%, and the cooking pressure is 0.75MPa, and the cooking temperature is 169 ℃, and the cooking time is 130min;

[0042] (4) bleaching: the product of step (3) is bleached, and the bleaching solution is a hydrogen peroxide solution with a concentration of 1.5%, the bleaching temperature is 65°C, and the bleaching time is 100min;

[0043] (5) classification: utilize classification sieve to screen out the bamboo fiber of 1.5mm from the product of step (4);

[0044] (6) Papermaking: the bamboo fiber of step (5) is copied into bamboo pulp.

[0045] Product performance:

[0046...

Embodiment 3

[0049] Preparation Process:

[0050] (1) Material preparation: take an appropriate amount of bamboo for use;

[0051] (2) cutting material: adopt the mode of oblique cutting to cut the bamboo of step (1), and the length is controlled at 25mm;

[0052] (3) cooking: the bamboo material of step (2) is added in the container to cook, and cooking liquid is the sodium hydroxide solution that concentration is 15%, and cooking pressure is 0.7MPa, and cooking temperature is 165 ℃, and cooking time is 130min;

[0053] (4) bleaching: the product of step (3) is bleached, and the bleaching solution is a hydrogen peroxide solution with a concentration of 1.5%, and the bleaching temperature is 70°C, and the bleaching time is 100min;

[0054] (5) classification: utilize classification sieve to screen out the bamboo fiber of 3.0mm from the product of step (4);

[0055] (6) Papermaking: the bamboo fiber of step (5) is copied into bamboo pulp.

[0056] Product performance:

[0057] The methy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
whitenessaaaaaaaaaa
Ash contentaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of bamboo pulp, bamboo pulp and fiber, wherein the preparation method includes material preparation, material cutting, cooking and papermaking, and the preparation method also includes grading after the cooking and before the papermaking. , screened out 0.5-3.0mm bamboo fiber for papermaking. The invention ensures the cellulose length distribution ratio by increasing the grading process after cooking and before papermaking, so that the quality of the obtained bamboo pulp is higher, and the quality of the fibers obtained from the obtained bamboo pulp is better.

Description

technical field [0001] The invention belongs to the field of textiles, and in particular relates to a preparation method of bamboo pulp, bamboo pulp and fibers. Background technique [0002] my country is the world's largest producer of textiles and raw materials. In recent years, due to the development of urbanization, the improvement of people's living standards, the change of consumption concepts and the strengthening of health and environmental protection awareness, there are great risks in the sustainable development of related industries in my country. Conducive to the healthy and stable development of related industries. However, the production of wood and cotton linter in my country is limited due to the constraints of planting area, growth cycle, ecological balance and cost, and the existing wood is mostly imported. Therefore, solving the problem of raw materials has become the top priority of promoting the development of textile raw materials in my country. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D21C3/02D21C3/22D21C9/16D21H11/12
CPCD21C3/02D21C3/222D21C9/163D21H11/12
Inventor 徐佳威李振峰张焕志范梅欣董战超吴兴乐刘会兵
Owner HEBEI JIGAO CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka