Preparation method of bamboo pulp, bamboo pulp and fibers

A technology of bamboo pulp and bamboo fiber, which is applied in the processing of fiber raw materials, pulping of cellulose raw materials, post-processing of cellulose pulp, etc., can solve the problems of poor fiber quality and low bamboo pulp quality, and achieve better fiber quality. , high whiteness, high quality effect

Active Publication Date: 2020-12-01
HEBEI JIGAO CHEM FIBER
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to overcome the deficiencies in the prior art, provide a preparation method of bamboo pulp, bamboo pulp and fiber, to solve the problem that the existing bamboo pulp has low quality and the quality of the obtained fiber is poor technical issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of bamboo pulp, bamboo pulp and fibers
  • Preparation method of bamboo pulp, bamboo pulp and fibers
  • Preparation method of bamboo pulp, bamboo pulp and fibers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Preparation Process:

[0028] (1) material preparation: get an appropriate amount of bamboo for subsequent use;

[0029] (2) material cutting: adopt the mode of oblique cutting to cut the bamboo of step (1), length is controlled at 20mm;

[0030] (3) Cooking: adding the bamboo material of step (2) into the container for cooking, the cooking liquid is a sodium hydroxide solution with a concentration of 15%, the cooking pressure is 0.7MPa, the cooking temperature is 168°C, and the cooking time is 130min;

[0031] (4) bleaching: the product of step (3) is bleached, the bleaching solution is a hydrogen peroxide solution with a concentration of 1.5%, the bleaching temperature is 65°C, and the bleaching time is 100min;

[0032] (5) classification: utilize classification sieve to screen out the bamboo fiber of 0.5mm from the product of step (4);

[0033] (6) copying: the bamboo fiber of step (5) is copied into bamboo pulp.

[0034] Product performance:

[0035] In the bamb...

Embodiment 2

[0038] Preparation Process:

[0039] (1) material preparation: get an appropriate amount of bamboo for subsequent use;

[0040] (2) material cutting: adopt the mode of oblique cutting to cut the bamboo of step (1), length is controlled at 25mm;

[0041](3) Cooking: adding the bamboo material of step (2) into the container for cooking, the cooking liquid is a sodium hydroxide solution with a concentration of 15%, the cooking pressure is 0.75MPa, the cooking temperature is 169°C, and the cooking time is 130min;

[0042] (4) bleaching: the product of step (3) is bleached, the bleaching solution is a hydrogen peroxide solution with a concentration of 1.5%, the bleaching temperature is 65°C, and the bleaching time is 100min;

[0043] (5) classification: utilize classification sieve to screen out the bamboo fiber of 1.5mm from the product of step (4);

[0044] (6) copying: the bamboo fiber of step (5) is copied into bamboo pulp.

[0045] Product performance:

[0046] In the bamb...

Embodiment 3

[0049] Preparation Process:

[0050] (1) material preparation: get an appropriate amount of bamboo for subsequent use;

[0051] (2) material cutting: adopt the mode of oblique cutting to cut the bamboo of step (1), length is controlled at 25mm;

[0052] (3) Cooking: adding the bamboo material of step (2) into the container for cooking, the cooking liquid is a sodium hydroxide solution with a concentration of 15%, the cooking pressure is 0.7MPa, the cooking temperature is 165°C, and the cooking time is 130min;

[0053] (4) Bleaching: the product of step (3) is bleached, the bleaching solution is a hydrogen peroxide solution with a concentration of 1.5%, the bleaching temperature is 70°C, and the bleaching time is 100min;

[0054] (5) classification: utilize classification sieve to screen out the bamboo fiber of 3.0mm from the product of step (4);

[0055] (6) copying: the bamboo fiber of step (5) is copied into bamboo pulp.

[0056] Product performance:

[0057] In the bamb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of bamboo pulp, the bamboo pulp and fibers. The preparation method comprises material preparation, material cutting, cooking and papermaking, the preparation method further comprises grading after cooking and before papermaking, and in the grading process, the bamboo fibers of 0.5-3.0 mm are selected out for papermaking. According to the method, the grading process is added after cooking and before papermaking so that the length distribution proportion of cellulose is guaranteed, the quality of the prepared bamboo pulp is higher, and the quality offibers prepared from the bamboo pulp is better.

Description

technical field [0001] The invention belongs to the textile field, and in particular relates to a preparation method of bamboo pulp, bamboo pulp and fiber. Background technique [0002] my country is the world's largest producer of textiles and raw materials. In recent years, due to the development of urbanization, the improvement of people's living standards, the change of consumption concepts and the strengthening of health and environmental protection awareness, there are great risks in the sustainable development of my country's related industries. Conducive to the healthy and stable development of related industries. However, the production of wood and cotton linters in my country is limited due to factors such as planting area, growth cycle, ecological balance and cost, and most of the existing wood is imported. Therefore, solving the problem of raw materials has become the most important thing to promote the development of my country's textile raw materials. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21C3/02D21C3/22D21C9/16D21H11/12
CPCD21C3/02D21C3/222D21C9/163D21H11/12
Inventor 徐佳威李振峰张焕志范梅欣董战超吴兴乐刘会兵
Owner HEBEI JIGAO CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap