Preparation method of imitated natural granite ceramic tile

A technology of imitating natural and ceramic tiles, applied in the field of preparation of imitation natural granite tiles, can solve the problems of time-consuming grinding and engraving, can not be reused, waste of natural resources, etc. effect of numbers

Active Publication Date: 2020-12-22
GUANGDONG OVERLAND CERAMICS CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, as a natural material, natural granite has a long formation period, high cost in processing and shaping, time-consuming grinding and engraving, and low efficiency; it is easy to break and break when dropped or hit hard, and cannot be reused. A great waste of natural resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of imitated natural granite ceramic tile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A preparation method for imitating natural granite tiles, comprising the following steps:

[0037] (1) Preparation of black particles;

[0038] (2) Preparation of red frit particles;

[0039] (3) Preparation of ceramic tile base material;

[0040] (4) Add 30 parts of tile base material, 5 parts of black granules, and 5 parts of red frit granules into the mixer by weight and mix evenly;

[0041] (5) Compress the product obtained in (4) with a molding machine at 55 MPa to obtain a dry billet;

[0042] (6) Sinter the dry blank at 1280°C for 140 minutes, cool it to room temperature, and grind the edges to obtain imitation natural granite tiles.

[0043] In the present embodiment, the preparation method of the black particles is:

[0044] S1: Weigh the following raw materials according to the ratio: 24 parts of kaolin, 10 parts of quartz, 7 parts of porcelain sand, 5 parts of talc, 2 parts of diyttrium trioxide, 2 parts of strontium oxide, 2 parts of ammonium bicarbonate...

Embodiment 2

[0058] A preparation method for imitating natural granite tiles, comprising the following steps:

[0059] (1) Preparation of black particles;

[0060] (2) Preparation of red frit particles;

[0061] (3) Preparation of ceramic tile base material;

[0062] (4) Add 30 parts of tile base material, 5 parts of black granules, and 5 parts of red frit granules into the mixer by weight and mix evenly;

[0063] (5) Compress the product obtained in (4) with a molding machine at 55 MPa to obtain a dry billet;

[0064] (6) Sinter the dry blank at 1280°C for 140 minutes, cool it to room temperature, and grind the edges to obtain imitation natural granite tiles.

[0065] In the present embodiment, the preparation method of the black particles is:

[0066] S1: Weigh the following raw materials according to the ratio: 24 parts of kaolin, 10 parts of quartz, 7 parts of porcelain sand, 5 parts of talc, 2 parts of diyttrium trioxide, 2 parts of strontium oxide, 2 parts of ammonium bicarbonate...

Embodiment 3

[0080] A preparation method for imitating natural granite tiles, comprising the following steps:

[0081] (1) Preparation of black particles;

[0082] (2) Preparation of red frit particles;

[0083] (3) Preparation of ceramic tile base material;

[0084] (4) Add 30 parts of tile base material, 5 parts of black granules, and 5 parts of red frit granules into the mixer by weight and mix evenly;

[0085] (5) Compress the product obtained in (4) with a molding machine at 55 MPa to obtain a dry billet;

[0086] (6) Sinter the dry blank at 1280°C for 140 minutes, cool it to room temperature, and grind the edges to obtain imitation natural granite tiles.

[0087] In the present embodiment, the preparation method of the black particles is:

[0088] S1: Weigh the following raw materials according to the ratio: 24 parts of kaolin, 10 parts of quartz, 7 parts of porcelain sand, 5 parts of talc, 2 parts of diyttrium trioxide, 2 parts of strontium oxide, 2 parts of ammonium bicarbonate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an imitated natural granite ceramic tile. The preparation method comprises the following steps of (1) preparing black particles, (2) preparing red fritparticles, (3) preparing a ceramic tile base material, (4) adding 25-40 parts by weight of the ceramic tile base material, 3-8 parts by weight of the black particles and 3-8 parts by weight of the redfrit particles into a mixer, and uniformly mixing, (5) carrying out compression molding on the product obtained in the step (4) by using a molding machine under 50-70 MPa to obtain a dry blank, and (6) sintering the dry blank at 1200-1300 DEG C for 120-180 minutes, cooling to room temperature, and edging to obtain the imitated natural granite ceramic tile. The imitated natural granite ceramic tile is composed of the black particles, the red frit particles and the ceramic tile base material, the imitated natural granite effect can be achieved through the black particles and the red frit particles, and the effect is vivid.

Description

technical field [0001] The invention relates to the technical field of tiles, in particular to a method for preparing imitation natural granite tiles. Background technique [0002] Granite is a kind of granite, the surface is pockmarked, mostly black and white spots, red and black spots, etc. Granite is a kind of granite with relatively high density and hard texture. It is often used for architectural decoration, sculpture sculpture, stone grinding Wait. In recent years, natural granite is very decorative and has the decorative effect of returning to nature. The texture spots of natural marble are very popular among sellers. They can cater to the development of architectural decoration that pursues health and environmental protection and advocates the new concept of natural consumption. Therefore, it is frequently used In the architectural decoration industry, more and more people are favored. However, as a natural material, natural granite has a long formation period, hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/195C01B32/168C04B35/622
CPCC04B35/195C04B35/622C04B2235/3213C04B2235/3225C04B2235/3272C04B2235/3284C04B2235/34C04B2235/3409C04B2235/3418C04B2235/349C04B2235/40C04B2235/447C04B2235/5276C04B2235/5288C04B2235/9607C04B2235/9661C01B32/168
Inventor 麦文英汪加武叶建明王礼熊红炎卢佩玉
Owner GUANGDONG OVERLAND CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More