Steel fiber quick-hardening template frame and preparation method thereof

A formwork frame and steel fiber technology, which is applied to clay preparation devices, chemical instruments and methods, manufacturing tools, etc., can solve the problems of thick formwork material, occupy a lot of building area, and take a long time to remove the formwork, so as to avoid brittle failure, The effect of saving turnover materials and saving on-site labor

Inactive Publication Date: 2021-01-29
CHINA RAILWAY CONSTR CORP LTD +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] As a kind of permanent formwork, rapid-hardening formwork needs to be able to be rapidly formed to meet special construction requirements. For the rapid-hardening formwork currently on the market, first, the thickness of the formwork material is relatively thick, and it occupies a large building area. 1. The distance between the connecting parts is small, resulting in many connecting parts and high cost. Third, the formwork contains glass fiber mesh cloth or steel wire mesh, which leads to a long time for form removal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel fiber quick-hardening template frame and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0025] see figure 1 , a steel fiber rapid-hardening type formwork frame, including a formwork 1; the formwork 1 is respectively arranged on both sides of a steel bar 2, the height between the two formworks 1 is the height of the wall, and the formwork 1 is passed through Pull connector 3 to connect.

[0026] The materials of the template 1 include cement, natural sand, steel fiber, silica fume, retarder, polycarboxylate superplasticizer powder, defoamer, rubb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a steel fiber quick-hardening template frame and a preparation method thereof. The steel fiber quick-hardening template frame comprises a template, reinforcing steel bars and opposite-pull connecting pieces, and template materials comprise cement, natural sand, steel fibers, silica fume, a retarder, polycarboxylate superplasticizer powder, a defoaming agent, rubber powder and an accelerator. The frame has the beneficial effects that the thickness of the formwork is 20 mm, the formwork has higher strength, the distance between the opposite-pull connecting pieces can be set to be 40 cm, the number of the connecting pieces can be reduced to a large extent, the cost of the opposite-pull connecting pieces is reduced, the compressive strength and breaking strength of formwork materials can be improved to a large extent by arranging the steel fibers, and meanwhile brittle failure of the formwork materials can be avoided. The produced template material is high in fluidity and can be self-leveled, vibration is not needed during template forming, the requirements of building industrialization are met in the aspects of saving on-site labor, saving turnover materials and the like, and the production efficiency of components can be greatly improved.

Description

technical field [0001] The invention relates to a support-free permanent formwork, in particular to a steel fiber rapid-hardening formwork frame and a preparation method thereof, belonging to the technical field of building materials. Background technique [0002] Permanent formwork means that when making reinforced concrete structural members, the forming formwork used is one-time. After the concrete is formed, the formwork and concrete become one. [0003] As a kind of permanent formwork, rapid-hardening formwork needs to be able to be rapidly formed to meet special construction requirements. For the rapid-hardening formwork currently on the market, first, the thickness of the formwork material is relatively thick, and it occupies a large building area. 1. The distance between the connecting parts is small, resulting in many connecting parts and high cost. Thirdly, the formwork contains glass fiber mesh cloth or steel wire mesh, which leads to a long time for formwork remo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00B28B7/00B28B23/02B28C5/40
CPCB28B7/00B28B23/02B28C5/402C04B28/00C04B14/06C04B14/48C04B18/146C04B24/24C04B2103/10C04B2103/302C04B2103/50C04B2103/22
Inventor 史乐贤周大兴方宏伟钱增志董磊张红伟
Owner CHINA RAILWAY CONSTR CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com