Production method of cinerary casket storage rack with antibacterial function

A production method and urn technology, which is applied in the field of funeral supplies, can solve the problems of mildew spots on urn storage racks, reduce the service life of urns, and have no sterilization effect, and achieve beautiful surface, high toughness, and compact structure Effect

Inactive Publication Date: 2021-03-12
江西钰石实业有限公司
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the field of making urn storage racks, in the existing manufacturing methods of urn storage racks, most of the urn storage racks do not have a sterilization effect, resulting in a large number of microorganisms growing on the urn storage racks, resulting in mold spots on the urn storage racks , affect the appearance, and make the stored urn easily corroded, reducing the service life of the urn, so we propose a production method for the urn storage rack with antibacterial function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of cinerary casket storage rack with antibacterial function
  • Production method of cinerary casket storage rack with antibacterial function
  • Production method of cinerary casket storage rack with antibacterial function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A method for producing an urn storage rack with an antibacterial function, comprising the following steps:

[0032] S1: Selection of raw materials. The raw material of the urn storage rack with antibacterial function is selected as the basic raw material for preparation. The weight percentage of the raw material of the urn storage rack with antibacterial function is chitin: 0.6%, titanium dioxide: 0.6%, cinnamon essential oil: 0.3%, Horseradish Essential Oil: 1%, Diethyl Phthalate: 1%, Zinc Borate: 2.5%, Cypress Oil: 0.6%, Polyimide: 0.6%, Antibacterial Additive: 1%, and Polyethylene 91.8 %;

[0033] S2: Mixing, adding the raw materials selected in step S1 into the smelting furnace in turn, and mechanically stirring at the same time, ensuring that the smelting temperature of the smelting furnace is 195°C during stirring, melting into molten materials, and setting aside;

[0034] S3: Forming, solid-dissolving the material kneaded in step S2 at 100° C. for 1 hour, and th...

Embodiment 2

[0043] A method for producing an urn storage rack with an antibacterial function, comprising the following steps:

[0044] S1: Raw material selection, select the raw material of the urn storage rack with antibacterial function as the basic raw material for preparation, the weight percentage of the raw material of the urn storage rack with antibacterial function is chitin: 0.8%, titanium dioxide: 0.7%, cinnamon essential oil: 0.5%, Horseradish Essential Oil: 1.2%, Diethyl Phthalate: 1.2%, Zinc Borate: 3%, Cypress Oil: 0.8%, Polyimide: 0.8%, Antibacterial Additive: 1.3%, Polyethylene 89.7 %;

[0045] S2: Mixing, adding the raw materials selected in step S1 into the smelting furnace in turn, and mechanically stirring at the same time, ensuring that the smelting temperature of the smelting furnace is 203°C during stirring, smelting into molten materials, and setting aside;

[0046]S3: Molding, solid-dissolving the material kneaded in step S2 at 110° C. for 1.5 hours, and then mak...

Embodiment 3

[0055] A method for producing an urn storage rack with an antibacterial function, comprising the following steps:

[0056] S1: Raw material selection, select the urn storage rack material with antibacterial function as the basic raw material for preparation, the weight percentage of raw materials for the urn storage rack with antibacterial function is chitin: 1%, titanium dioxide: 0.8%, cinnamon essential oil: 0.7%, Horseradish Essential Oil: 1.4%, Diethyl Phthalate: 1.4%, Zinc Borate: 3.5%, Cedarwood Oil: 1%, Polyimide: 1%, Antimicrobial Additive: 1.5%, and Polyethylene 87.7%;

[0057] S2: Mixing, adding the raw materials selected in step S1 into the smelting furnace in turn, and mechanically stirring at the same time, ensuring that the smelting temperature of the smelting furnace is 210°C during stirring, smelting into molten materials, and setting aside;

[0058] S3: Forming, solid-dissolving the material kneaded in step S2 at 120° C. for 2 hours, and then making the solid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method of a cinerary casket storage rack with an antibacterial function. The production method comprises the following steps: S1, selecting raw materials; s2, carrying out mixing; s3, carrying out forming; s4, carrying out cooling; s5, carrying out mechanical finishing; s6, carrying out surface treatment; s7, carrying out machining and finishing; s8, carrying out welding and assembling; and S9: carrying out welding treatment. The cinerary casket storage rack is made of plastic, an antibacterial agent is added into the manufacturing plastic for manufacturingthe cinerary casket storage rack, the plastic material is convenient to weld, and the cinerary casket storage rack is compact in structure, high in toughness, non-conductive and not prone to corrosion, microorganisms cannot be generated on the surface of the cinerary casket storage rack, and mildew spots cannot be generated on the surface of the cinerary casket storage rack, therefore, appearanceof cinerary casket storage rack is greatly improved. Compared with a cinerary casket storage rack manufactured through an existing cinerary casket storage rack manufacturing method, the cinerary casket storage rack is stable in structure, the surface of the cinerary casket storage rack is still attractive after the cinerary casket storage rack is used for a long time, mildew spots cannot be generated due to environmental problems, a casket body cannot be corroded due to bacterium breeding, and the service life of a cinerary casket is prolonged.

Description

technical field [0001] The invention relates to the technical field of making funeral supplies, in particular to a production method for an urn storage rack with an antibacterial function. Background technique [0002] Funeral supplies and equipment include coffin materials, refrigeration equipment, ashes storage racks, cremation machinery, production equipment and raw materials. [0003] In the field of making urn storage racks, in the existing manufacturing methods of urn storage racks, most of the urn storage racks do not have a sterilization effect, resulting in the breeding of a large number of microorganisms on the urn storage racks, resulting in mold spots on the urn storage racks , affect the appearance, and make the stored urn easily corroded, reducing the service life of the urn, so we propose a production method for the urn storage rack with antibacterial function. Contents of the invention [0004] The object of the present invention is to provide a method for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/06C08L79/08C08L91/00C08L5/08C08K3/22C08K5/12C08K3/38C08K5/00C08K3/34C08K3/36C08K13/02C08K7/10C08K13/04
CPCC08L23/06C08K2003/2241C08K2003/387C08L2201/08C08L2205/035C08L79/08C08L91/00C08L5/08C08K3/22C08K5/12C08K3/38C08K5/0058C08K3/346C08K3/36C08K13/02C08K7/10C08K13/04
Inventor 李和平
Owner 江西钰石实业有限公司