Waterborne environment-friendly polyurethane modified emulsified asphalt cold-mixed material and preparation method thereof

A technology of polyurethane modification and water-based polyurethane, which is applied in the field of asphalt manufacturing, can solve the problems of easy cracking of materials, poor anti-rutting performance, cumbersome production of materials, etc., and achieve the effects of improving construction conditions, reducing emissions, and simple and diverse processing

Inactive Publication Date: 2021-04-30
南通福伦利新材料有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] (1), in the cold winter, the material is prone to brittle cracks, reducing the service life;
[0004] (2), the hardness of the material itself is not enough, the anti-rutting performance is poor, and the service life is short;
[0005] (3), cumbersome material production, excessive energy consumption during production, time-consuming and labor-intensive, inconvenient construction and other defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne environment-friendly polyurethane modified emulsified asphalt cold-mixed material and preparation method thereof
  • Waterborne environment-friendly polyurethane modified emulsified asphalt cold-mixed material and preparation method thereof
  • Waterborne environment-friendly polyurethane modified emulsified asphalt cold-mixed material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] In order to make the technical solutions of the present invention clearer and clearer to those skilled in the art, the present invention will be further described in detail below in conjunction with the examples and accompanying drawings, but the embodiments of the present invention are not limited thereto.

[0037] The water-based environmentally friendly polyurethane modified emulsified asphalt cold mix of the present invention comprises the following components and the parts by weight of each component are:

[0038] Polyurethane modified room temperature composite emulsion: 11-12 parts;

[0039] Aggregate: 100 parts;

[0040] High stiffness mixed additives: 2 parts;

[0041] Water: 2 parts;

[0042] Water-based polyurethane: 2-3 parts,

[0043] Described polyurethane modified room temperature composite emulsion comprises the following components and the parts by weight of each component are:

[0044] Base emulsified asphalt: 100 parts;

[0045] Emulsified asphal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterborne environment-friendly polyurethane modified emulsified asphalt cold-mixed material and a preparation method thereof. The preparation method comprises the steps of: compositely modifying matrix emulsified asphalt: an emulsified asphalt modifier is slowly added into the matrix emulsified asphalt, the stirring time is 5 min, the stirring rotating speed is 400-500 r / min till the color is uniform and no white floating exists on the surface, and a pre-finished product A is formed; slowly adding waterborne polyurethane into the pre-finished product A while stirring for 10 minutes at the stirring speed of 600-700 r / min to form a polyurethane modified normal-temperature composite emulsion B; mixing and stirring the high-stiffness mixed additive and the aggregate for 20 seconds, adding purified water, and stirring for 20 seconds to form a pre-finished product C; and uniformly spraying the polyurethane modified normal-temperature composite emulsion B onto the pre-finished product C, and stirring for 30 seconds to obtain the water-based environment-friendly polyurethane modified emulsified asphalt cold-mixed material, which has the advantages of high adhesive force, wear resistance, no peeling, balanced rigidity and toughness, simple and diversified processing and high cost performance compared with the traditional modified emulsified asphalt.

Description

technical field [0001] The invention relates to the technical field of asphalt production, in particular to a water-based environmentally friendly polyurethane modified emulsified asphalt cold mix and a preparation method thereof. Background technique [0002] With the rapid development of the road network, the demand for road protection and repair is also increasing. At present, more and more quantities are required for road preventive materials and repairing cold patch materials. However, the current material suffers from the following problems: [0003] (1), in the cold winter, the material is prone to brittle cracks, reducing the service life; [0004] (2), the hardness of the material itself is not enough, the anti-rutting performance is poor, and the service life is short; [0005] (3) The production of materials is cumbersome, excessive energy consumption during production, time-consuming and labor-intensive, and inconvenient construction. [0006] Therefore, how ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B24/28C04B24/36C04B24/42C04B24/04C04B111/72
CPCC04B28/06C04B24/282C04B24/36C04B24/42C04B24/04C04B2111/00017C04B2111/72C04B2111/0075C04B2103/0045C04B2103/0068
Inventor 蔡海军吴新峰顾健键吴瑞琪高亮苏适
Owner 南通福伦利新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products