Preparation method of environment-friendly high-temperature leveling agent for fabric

A high-temperature leveling agent and environment-friendly technology, applied in the field of fine chemicals, can solve the problems of poor dye migration of high-temperature leveling agents, and achieve the effects of simple production conditions, favorable production and excellent migration performance.

Active Publication Date: 2021-04-30
江苏文理新材料科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although its raw materials are environmentally friendly products, and the prepared high-temperature leveling agent has poor dye migration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] 1) Under the catalysis of 1g arginine and 10g ethylene oxide under the catalysis of 20mg tetramethylammonium hydroxide, conduct ultrasonic reaction at 180-190°C for 1-2h, after the reaction, use acetic acid to adjust the pH to 6.2 -7.0 gets leveling agent mother liquor;

[0019] 2) Mix all the leveling agent masterbatch obtained in step 1) with urea (2-5% of the weight of the leveling agent masterbatch), 1.1g sulfamic acid, stir evenly and heat up to 140-150°C for 6-8h, and adjust pH to neutral, filtered after cooling to obtain an environment-friendly high-temperature leveling agent for fabrics.

Embodiment 2

[0021] 1) Use 3g of arginine and 10g of ethylene oxide under the catalysis of 30mg of tetramethylammonium hydroxide, conduct ultrasonic reaction at 180-190°C for 1-2h, adjust the pH to 6.2 with acetic acid after the reaction -7.0 gets leveling agent mother liquor;

[0022] 2) Mix all the leveling agent masterbatch obtained in step 1) with urea (2-5% of the weight of the leveling agent masterbatch), 1.1g sulfamic acid, stir evenly and heat up to 140-150°C for 6-8h, and adjust pH to neutral, filtered after cooling to obtain an environment-friendly high-temperature leveling agent for fabrics.

Embodiment 3

[0024] 1) Use 2g of arginine and 10g of ethylene oxide under the catalysis of 30mg of tetramethylammonium hydroxide, conduct ultrasonic reaction at 180-190°C for 1-2h, adjust the pH to 6.2 with acetic acid after the reaction -7.0 gets leveling agent mother liquor;

[0025] 2) Mix all the leveling agent masterbatch obtained in step 1) with urea (2-5% of the weight of the leveling agent masterbatch), 1.18g sulfamic acid, stir evenly and heat up to 140-150°C for 6-8h heat preservation reaction, adjust pH to neutral, filtered after cooling to obtain an environment-friendly high-temperature leveling agent for fabrics.

[0026] For performance testing, the environment-friendly high-temperature leveling agents prepared in Examples 1-3 were tested for leveling effect, and the results showed that the environment-friendly high-temperature leveling agents prepared in Examples 1-3 all had excellent leveling properties. However, the environment-friendly high-temperature leveling agent pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of fine chemicals, and particularly relates to a preparation method of an environment-friendly high-temperature leveling agent for fabric. Arginine and ethylene oxide are polymerized to prepare leveling agent mother liquor for the first time, and then a final product, the environment-friendly high-temperature leveling agent for the fabric, is prepared from the leveling agent mother liquor, urea and sulfamic acid through a one-pot method. Raw materials are green and environmentally friendly, production conditions are simpler and more convenient, and production is facilitated. The prepared environment-friendly high-temperature leveling agent for the fabric is green and environmentally friendly, and is excellent in transfer dyeing performance (the transfer dyeing rate is as high as 42.6%).

Description

technical field [0001] The invention belongs to the technical field of fine chemicals, and more specifically relates to a preparation method of an environment-friendly high-temperature leveling agent for fabrics. Background technique [0002] High-temperature leveling agent is mainly a dyeing auxiliary for polyester fabrics. The basic component of polyester is polyethylene terephthalate. From the molecular structure of polyester, it lacks active groups that can combine with dyes. Therefore It cannot be dyed directly with acid dyes, reactive dyes, etc., only water-insoluble disperse dyes can be used for dyeing. And because the polyester molecules are arranged relatively closely, there are only small gaps in the fiber, and it is difficult for the dye molecules to enter the interior of the fiber under low temperature conditions. The gaps allow the dye molecules to enter the interior of the fiber. Therefore, the dyeing of polyester fibers is carried out under high temperature ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/607D06P1/649D06P1/673
CPCD06P1/6076D06P1/6491D06P1/67316
Inventor 杨晓凤田飞
Owner 江苏文理新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap