Processing method of spunlace non-woven fabric

A technology of spunlace non-woven fabrics and processing methods, which can be used in non-woven fabrics, textiles, and papermaking, and can solve problems such as rough hand feeling and poor water absorption of spunlace non-woven fabrics

Inactive Publication Date: 2021-05-04
应城市天润产业用布有限责任公司
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing spunlace non-woven fabrics h

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for processing spunlace non-woven fabrics, comprising the following components in parts by weight: 20-30 parts of polyester, 20-30 parts of wood pulp fibers, 5-10 parts of antistatic fibers, and 10-20 parts of viscose fibers 10-20 parts of seaweed fiber, the wood pulp fiber is coniferous wood fiber, and the antistatic fiber is antistatic agent type antistatic fiber.

[0021] The processing method of described spunlace nonwoven fabric, comprises the steps:

[0022] (1) choose 20 parts of polyester, 20 parts of wood pulp fiber of coniferous wood fiber, 5 parts of antistatic fiber, 10 parts of viscose fiber and 10 parts of seaweed fiber;

[0023] (2) Feed the selected raw materials into the opener for opening and mixing to loosen various fibers, and at the same time fully mix different types of fibers to make the ratio of each component fiber in the fiber web correct , stable and evenly distributed;

[0024] (3) Feed the fully opened and mixed mixed fibers into ...

Embodiment 2

[0028] A method for processing spunlace non-woven fabrics, comprising the following components in parts by weight: 20-30 parts of polyester, 20-30 parts of wood pulp fibers, 5-10 parts of antistatic fibers, and 10-20 parts of viscose fibers 10-20 parts of seaweed fiber, the wood pulp fiber is coniferous wood fiber, and the antistatic fiber is antistatic agent type antistatic fiber.

[0029] The processing method of described spunlace nonwoven fabric, comprises the steps:

[0030] (1) choose 30 parts of polyester, 30 parts of wood pulp fiber of coniferous wood fiber, 10 parts of antistatic fiber, 20 parts of viscose fiber and 20 parts of seaweed fiber;

[0031] (2) Feed the selected raw materials into the opener for opening and mixing to loosen various fibers, and at the same time fully mix different types of fibers to make the ratio of each component fiber in the fiber web correct , stable and evenly distributed;

[0032] (3) Feed the fully opened and mixed mixed fibers into...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a processing method of spunlace non-woven fabric. The spunlace non-woven fabric comprises the following components in parts by weight of 20-30 parts of polyester, 20-30 parts of wood pulp fibers, 5-10 parts of antistatic fibers, 10-20 parts of viscose fibers and 10-20 parts of alginate fibers. A fiber web is soaked in a water solution with hydrogen peroxide content of 30%, washing and dewatering are conducted after soaking, and the antibacterial effect of the non-woven fabric can be effectively improved; meanwhile, a certain bleaching effect can be achieved, the wood pulp fibers of coniferous wood fibers are added, the overall texture of the non-woven fabric can be effectively improved, and the use hand feeling is improved; and the alginate fibers are added, so that the water absorption performance of the non-woven fabric can be effectively improved, and the use is convenient.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a processing method of a spunlace nonwoven fabric. Background technique [0002] Spunlace non-woven fabric is to spray high-pressure fine water onto one or more layers of fiber webs to entangle the fibers with each other, so that the fiber webs can be reinforced and have a certain strength. The obtained fabric is spunlace non-woven fabric. Its fiber raw materials come from a wide range of sources, such as polyester, nylon, polypropylene, viscose fiber, chitin fiber, microfiber, tencel, silk, bamboo fiber, wood pulp fiber, seaweed fiber, etc. [0003] The existing spunlace non-woven fabric has poor water absorption and rough hand feeling. Contents of the invention [0004] In view of this, the present invention aims to propose a processing method of spunlace nonwoven fabric. [0005] In order to achieve the above object, technical solution of the present invention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H1/4382D04H1/492
CPCD04H1/4382D04H1/492
Inventor 丁青
Owner 应城市天润产业用布有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap