a mg based 3 teo 6 Violet inorganic pigment of structure and its preparation method and application

An inorganic pigment, purple technology, applied in the direction of inorganic chemistry, chemical instruments and methods, selenium/tellurium compounds, etc., can solve the problems of poor acid and alkali resistance, high temperature resistance, etc., achieve non-toxic raw materials, keep the color unchanged, raw materials parity effect

Active Publication Date: 2022-02-08
SUN YAT SEN UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The primary purpose of the present invention is to overcome the problem of poor acid and alkali resistance and high temperature resistance of purple pigments in the prior art, and to provide a 3 TeO 6 Structured Violet Inorganic Pigments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • a mg based <sub>3</sub> teo <sub>6</sub> Violet inorganic pigment of structure and its preparation method and application
  • a mg based <sub>3</sub> teo <sub>6</sub> Violet inorganic pigment of structure and its preparation method and application
  • a mg based <sub>3</sub> teo <sub>6</sub> Violet inorganic pigment of structure and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The raw material MgO, TeO 2 , MnCO 3 , Li 2 CO 3 According to the molar ratio of elements Mg:Te:Mn:Li=2.8:1:0.1:0.1, weigh them, mix them and grind them evenly, put them into a muffle furnace, raise the temperature from room temperature to 800°C at a rate of 4°C / min, in air Calcined in medium for 6 hours, cooled naturally, and the sample was obtained after grinding.

Embodiment 2

[0030] The raw material MgCO 3 , Te(OH) 6 , MnO, Li 2 CO 3 According to the molar ratio of elements Mg:Te:Mn:Li=2.9:1:0.05:0.05, weigh them, mix them and grind them evenly, put them into a muffle furnace, raise the temperature from room temperature to 750°C at a rate of 2°C / min, in air Calcined in medium for 6 hours, cooled naturally, and the sample was obtained after grinding.

Embodiment 3

[0032] The raw material MgO, TeO 2 , MnCO 3 , Li 2 CO 3 According to the elemental molar ratio Mg:Te:Mn:Li=2.7:1:0.15:0.15, weigh it, mix and grind it evenly, put it into a muffle furnace, raise the temperature from room temperature to 850°C at a heating rate of 4°C / min, in air Calcined in medium for 12 hours, cooled naturally, and the sample was obtained after grinding.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a Mg-based 3 TeO 6 The purple inorganic pigment of structure and its preparation method and application, the molecular formula of described purple inorganic pigment is Mg 3‑2x mn x Li x TeO 6 , wherein 0.02≤x≤0.15; the preparation method of the purple inorganic pigment comprises the following steps: proportioning a compound containing magnesium, a compound containing tellurium, a compound containing manganese, Li 2 CO 3 After mixing and grinding, it is calcined at 750-900°C, and the purple inorganic pigment is obtained after cooling. The purple inorganic pigment of the invention is resistant to acid, alkali and high temperature, the preparation method is environment-friendly, and the raw materials are cheap and non-toxic, and can be used in the chemical production of paints, coatings, paintings, plastics and rubber.

Description

technical field [0001] The present invention relates to the field of preparation of inorganic pigments, more specifically, to a Mg-based 3 TeO 6 Structured purple inorganic pigments and their preparation methods and applications. Background technique [0002] Inorganic pigments are widely used in construction materials, paints, plastics, inks, military camouflage and other industries because of their stable properties, bright colors, and complete and pure color spectrum. However, existing commercial inorganic pigments still have various problems. First, the commercial pigment chrome yellow (PbCrO 3 ), cadmium yellow (CdS), antimony yellow (Sb 2 o 3 2PbO) and molybdenum red [Pb(Cr,Mo,S)O 4 ] and other toxic heavy metal elements such as lead, chromium, cadmium, etc., will endanger human health and pollute the environment, and its application fields are also subject to more and more restrictions. Second, the pigment production process is complex and produces toxic by-pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01B19/00
CPCC01B19/008C01P2002/72C01P2006/63C01P2006/64C01P2006/62C01P2006/66C01P2004/01
Inventor 李满荣周潇
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap