Mercury adsorption material, and preparation method and application thereof

A technology of adsorbing materials and bonding materials, applied in chemical instruments and methods, adsorbed water/sewage treatment, other chemical processes, etc., can solve the problems of unsatisfactory repeated adsorption performance, limited adsorption capacity, unstable mercury removal efficiency, etc.

Pending Publication Date: 2021-05-18
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] For this reason, the technical problem to be solved by the present invention is to provide a mercury adsorbent material to solve the problems of unstable mercury removal efficiency, limited adsorption capacity and unsatisfactory repeated adsorption performance after regeneration in mercury adsorbent materials in the prior art;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] The preparation method of mercury adsorption material described in the present embodiment, comprises the steps:

[0055] (1) Preparation of hydrotalcite

[0056] Prepare 2L Mg(NO 3 ) 2 ·6H 2 O and Fe(NO 3 ) 3 9H 2 Mixed magnesium-iron salt solution of O, control Mg in the solution 2+ The concentration is 0.6mol / L, Fe 3+ The concentration is 0.15mol / L;

[0057] Prepare 2LNaOH and Na 2 CO 3 The mixed alkali solution, control the Na in the solution 2 CO 3 The concentration of NaOH is 0.3mol / L, and the concentration of NaOH is 1.5mol / L;

[0058] After adding 4L of deionized water into the 10L reactor, add the mixed magnesium-iron salt solution and the mixed alkali solution dropwise into the reactor at a rate of 400ml / h, while vigorously stirring to control the pH value of the mixed stirring solution in the reactor 9; after the titration, the slurry was stirred at 60°C and aged for 12 hours; after aging, the formed hydrotalcite was filtered, washed and filtered ...

Embodiment 2

[0072] The preparation method of mercury adsorption material described in the present embodiment, comprises the steps:

[0073] (1) Preparation of hydrotalcite

[0074] Prepare 2L Mg(NO 3 ) 2 ·6H 2 O and Fe(NO 3 ) 3 9H 2 Mixed magnesium-iron salt solution of O, control Mg in the solution 2+ The concentration is 0.8mol / L, Fe 3+ The concentration is 0.2mol / L;

[0075] Prepare 2L NaOH and NaOH 2 CO 3 The mixed alkali solution, control the Na in the solution 2 CO 3 The concentration of NaOH is 0.4mol / L, and the concentration of NaOH is 2.0mol / L;

[0076] After adding 5L of deionized water into the 10L reactor, add the mixed magnesium-iron salt solution and the mixed alkali solution dropwise into the reactor at a rate of 600ml / h, and stir vigorously at the same time to control the pH value of the mixed stirring solution in the reactor After the titration, the slurry was kept at 60°C for 12 hours and aged for 12 hours; after aging, the formed hydrotalcite was filtered, ...

Embodiment 3

[0090] The preparation method of mercury adsorption material described in the present embodiment, comprises the steps:

[0091] (1) Preparation of hydrotalcite

[0092] Prepare 2L Mg(NO 3 ) 2 ·6H 2 O and Fe(NO 3 ) 3 9H 2 Mixed magnesium-iron salt solution of O, control Mg in the solution 2+ The concentration is 0.7mol / L, Fe 3+ The concentration is 0.18mol / L;

[0093] Prepare 2LNaOH and Na 2 CO 3 The mixed alkali solution, control the Na in the solution 2 CO 3 The concentration of NaOH is 0.35mol / L, and the concentration of NaOH is 1.8mol / L;

[0094] After adding 5L of deionized water into the 10L reactor, add the mixed magnesium-iron salt solution and the mixed alkali solution dropwise into the reactor at a rate of 500ml / h, while vigorously stirring to control the pH value of the mixed stirring solution in the reactor 9.5; after the titration, the slurry was kept at 60°C and stirred for 12 hours; after aging, the formed hydrotalcite was filtered, washed and filter...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Adsorption capacityaaaaaaaaaa
Adsorption capacityaaaaaaaaaa
Adsorption capacityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of sewage treatment materials, and particularly relates to a mercury adsorption material, and a preparation method and application thereof. According to the preparation method of the mercury adsorption material, hydrotalcite with an adjustable and controllable interlayer structure and polypyrrole modified montmorillonite are prepared as raw materials, and the hydrotalcite and the montmorillonite are subjected to compound bonding and intercalation to further form a polyhydroxy layered structure composite material with a spatial domain effect; and sulfydryl modification is carried out by utilizing a specific polyhydroxy layered structure of the material to prepare the modified adsorption material which can be applied to adsorbing Hg<2+> in mercury-containing wastewater. The mercury adsorption material is applied to the mercury adsorption process of mercury-containing wastewater, the content of mercury in adsorbed water is stably lower than 5 [mu]g / L, and the mercury adsorption material has better adsorption efficiency and adsorption capacity, can realize stable regeneration and is suitable for industrial popularization.

Description

technical field [0001] The invention belongs to the technical field of sewage treatment materials, and in particular relates to a mercury adsorption material and its preparation method and application. Background technique [0002] Mercury, commonly known as mercury, has attracted widespread attention due to its characteristics of being highly toxic, bioaccumulative, volatile, easy to migrate and transform, and difficult to biodegrade. Mercury can accumulate in organisms and is easily absorbed by the skin, respiratory tract and digestive tract. Listed as a global pollutant. Currently, China's discharge standards for mercury-containing wastewater require that the concentration of mercury in the effluent is not higher than 5 μg / L. Therefore, how to effectively remove mercury contained in wastewater is a difficult problem in the field of sewage and wastewater treatment. Traditional mercury treatment processes in the prior art include chemical precipitation, activated carbon a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/26B01J20/30C02F1/28C02F101/20
CPCB01J20/12B01J20/041B01J20/22B01J20/262C02F1/281C02F1/285C02F2101/20B01J2220/46B01J2220/4806B01J2220/4812Y02P10/20
Inventor 李波刘婷婷潘咸峰黄斌解洪梅
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com