A kind of technology of chrome tanning agent and low-carbon alcohol
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0026] Raw materials and ratio:
[0027] Sodium red alum (solid state) 100 parts
[0028] Sulfuric acid (98%) 100 parts
[0029] Butanediol-[1,4] 27 parts
[0030] 181 parts of water
[0031] step:
[0032] 1. Add 100 parts of sodium rubylum to an acid-resistant reaction kettle, and add 100 parts of water to dissolve;
[0033] 2. Slowly add 100 parts of sulfuric acid into the red alum solution;
[0034] 3. Dilute butanediol with 81 parts of water;
[0035] 4. Slowly add diluted butanediol into the reaction kettle, and keep the kettle boiling until the reaction is complete;
[0036] 5. Leave it to mature in the reactor for 24 hours;
[0037] 6. adjust the alkalinity B=33% of chrome liquid with sulfuric acid;
[0038] 7. Spray drying into chrome tanning agent.
[0039] Product performance index of this embodiment: Cr 2 o 3 24%, alkalinity B33%, sodium succinate 5%, all are percentages by weight.
Embodiment 2
[0040] Embodiment 2. As described in embodiment 1, difference is that raw material and proportioning are as follows:
[0041] Sodium red alum (solid state) 100 parts
[0042] Sulfuric acid (98%) 100 parts
[0043] 50 parts of n-propanol
[0044] 200 parts of water
[0045] Product performance index of this embodiment: Cr 2 o 3 24%, alkalinity B33%, sodium propionate 5%, all are percentages by weight.
Embodiment 3
[0046] Embodiment 3. As described in Example 1, the difference is to replace butanediol with methyl alcohol and n-amyl alcohol, and the proportioning is: 20 parts of methyl alcohol, 5 parts of n-amyl alcohol.
[0047] Product performance index: Cr 2 o 3 24%, B3 3%, sodium formate 4%, sodium valerate 1%.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap