PVC wood-plastic low foaming granule material and preparation method thereof

A technology of granular material and low foaming, applied in the field of new wood-plastic low-foaming granular material, can solve the problems of wood fiber or plant fiber easy to absorb moisture, high product density, large quality difference, etc., to achieve stable composition and product quality. Stable, easy to transport and store

Inactive Publication Date: 2009-09-09
翁端华
View PDF0 Cites 48 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. Wood fiber or plant fiber needs special drying equipment for pretreatment before use, which is time-consuming and energy-consuming
[0004] 2. The wood fiber or plant fiber in the mixture is easy to absorb moisture. Although it has been dried, it is still not suitable for storage and can only be mixed and used now.
[0005] 3. Affected by factors such as raw material suppliers and processing technology, the quality of products produced by different manufacturers with the same formula varies greatly
[0006] 4. The density of processed products is relatively high, usually exceeding 1.1-1.4g / cm 3 , the practical application is restricted by

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Example 1: PVC wood-plastic low-foaming pellets consist of the following components and their contents:

[0047] 60 parts wood flour

[0048] Polyvinyl chloride (PVC) 100 parts

[0049] Composite stabilizer 10 parts

[0050] Calcium Carbonate (CaCO 3 ) 30 copies

[0051] Azodicarbonamide (H2NCON) 6 parts

[0052] Foaming aid (ZB-530) 10 parts

[0053] Processing aid (ACR-401) 10 parts

[0054] Lubricants such as paraffin wax 6 parts

[0055] Titanate coupling agent 4 parts

[0056] Pigment 0.5 parts

Embodiment 2

[0057] Example 2: PVC wood-plastic low-foaming pellets consist of the following components and their contents:

[0058] Bamboo powder 40 parts

[0059] Polyvinyl chloride (PVC) 100 parts

[0060] Composite stabilizer 8.5 parts

[0061] Calcium Carbonate (CaCO 3 ) 40 copies

[0062] Azodicarbonamide (H2NCON) 0.6 parts

[0063] Foaming aid (ZB-530) 16 parts

[0064] Processing aid (ACR-401) 6 parts

[0065] Lubricants such as paraffin wax 3.5 parts

[0066] 3.5 parts of titanate coupling agent

[0067] Pigment 0.4 parts

Embodiment 3

[0068] Example 3: PVC wood-plastic low-foaming pellets consist of the following components and their contents:

[0069] 10 parts wood flour

[0070] Bamboo powder 10 parts

[0071] Polyvinyl chloride (PVC) 100 parts

[0072] Composite stabilizer 4 parts

[0073] Calcium Carbonate (CaCO 3 ) 60 copies

[0074] Azodicarbonamide (H2NCON) 3.5 parts

[0075] Foaming aid (ZB-530) 2 parts

[0076] Processing aid (ACR-401) 1 part

[0077] Paraffin and other lubricants 0.6 parts

[0078] Titanate coupling agent 0.6 part

[0079] Pigment 0.2 parts

[0080] The method of the present invention is: buy polyvinyl chloride resin, processing aid (as blowing aid ZB-530; Processing aid ACR-401 is trade name) and wood powder or / and bamboo powder from manufacturer or from market (The particle size should be above 100 mesh) and other raw materials, and then mix according to the above ratio, and add some pigments for matching, so as to obtain wood-plastic mixtures of different colors. Put i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a PVC wood-plastic low foaming granule material and a preparation method thereof, and belongs to the technical field of wood-plastic materials. The PVC wood-plastic low foaming granule material comprises the following substances in portion by weight: 20 to 60 portions of wood powder or / and bamboo powder, 100 portions of polyvinyl chloride, 2 to 12 portions of composite stabilizing agent, 5 to 60 portions of CaCO3, 0.6 to 6 portions of foaming agent, 2 to 16 portions of assistant foaming agent, 1 to 10 portions of processing assistant, 0.6 to 6 portions of lubricating agent, 0.6 to 4 portions of coupling agent, and 0.1 to 0.8 portion of paint. The method for preparing the PVC wood-plastic low foaming granule material comprises the following steps: mixing and heating the substances; plasticizing the substances; extruding the substances into columnar granules; and separating and packing the granules as a product. The PVC wood-plastic low foaming granule material has relatively stable components and lighter texture, and is convenient to transport, store and process. The preparation method is simple and practical, saves energy, and saves investment; and the quality of the product is stable.

Description

technical field [0001] The invention belongs to the technical field of wood-plastic materials, and relates to a new type of wood-plastic low-foaming granular material compounded with wood powder or / and bamboo powder, polyvinyl chloride (PVC) and processing aids; and the new type A preparation method of wood-plastic low-foaming granules. Background technique [0002] Wood-plastic material is a new type of composite material obtained by filling, reinforcing, modifying and blending waste wood fibers or plant fibers and thermoplastics. This mixed modified material can be processed into shaped materials, plates or other products through a special single-screw extruder or twin-screw extruder with corresponding molds and auxiliary molding machines. There are following defects in the currently available wood-plastic granules and their processing methods: [0003] 1. Wood fiber or plant fiber needs special drying equipment for pretreatment before use, which is time-consuming and en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08K13/02C08J9/10C08L97/00
Inventor 翁端华翁端祥
Owner 翁端华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com