Healthcare toothpaste and preparation process thereof

A preparation process and toothpaste technology, applied in the field of toothpaste, can solve problems such as health hazards

Inactive Publication Date: 2021-06-22
优牌智能科技(上海)有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the use of toothpaste made of abrasives such as silicon dioxide, aluminum hydroxide, and calcium carbonate has created a certain contradiction between keeping the oral cavity clean and hygienic and dental safety for people who have the habit of brushing their teeth.
Moreover, calcium carbonate, calcium phosphate, silicon dioxide, etc. are all chemical additives, and some of them will be swallowed after long-term use, which is harmful to human health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Healthcare toothpaste and preparation process thereof
  • Healthcare toothpaste and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A health-enhancing toothpaste, comprising the following components, the percentages by weight of each component are: 12% of mother-of-pearl powder, 12% of pearl powder, 0.5% of clove oil, 0.5% of mint leaf oil, 1.2% of sweet orange oil, polyglycerin -10 Laurate 10%, Sorbitol 25%, Glycerin 20%, Dipotassium Glycyrrhizinate 0.5%, Cellulose Gum 1.3%, Purified Water 17%.

[0016] The mother-of-pearl powder is powder ground with mother-of-pearl, and the particle size of the mother-of-pearl powder and pearl powder is 200-300 mesh.

[0017] The present invention also provides a preparation process of beneficial health toothpaste, the specific steps are as follows:

[0018] S1. Stir and disperse mother-of-pearl powder, pearl powder, and cellulose gum in glycerin to obtain a mixed solution A;

[0019] S2, add water and sorbitol to A solution while stirring and obtain mixed solution B;

[0020] S3. Put the emulsion B in an emulsification pot and raise the temperature to 80°C and...

Embodiment 2

[0024] A health-enhancing toothpaste, comprising the following components, the percentage by weight of each component is: 15% of mother-of-pearl powder, 10% of pearl powder, 0.5% of clove oil, 0.5% of mint leaf oil, 1.2% of sweet orange oil, polyglycerin -10 Laurate 9%, Sorbitol 22%, Glycerin 24%, Dipotassium Glycyrrhizinate 0.5%, Cellulose Gum 1.3%, Purified Water 16%.

[0025] The mother-of-pearl powder is powder ground with mother-of-pearl, and the particle size of the mother-of-pearl powder and pearl powder is 200-300 mesh.

[0026] The present invention also provides a preparation process of beneficial health toothpaste, the specific steps are as follows:

[0027] S1. Stir and disperse mother-of-pearl powder, pearl powder, and cellulose gum in glycerin to obtain a mixed solution A;

[0028] S2, add water and sorbitol to A solution while stirring and obtain mixed solution B;

[0029] S3. Put the emulsion B in an emulsification pot and raise the temperature to 80°C and st...

Embodiment 3

[0033] A health-enhancing toothpaste, comprising the following components, the percentage by weight of each component is: 10% of mother-of-pearl powder, 14% of pearl powder, 0.4% of clove oil, 0.6% of mint leaf oil, 1.3% of sweet orange oil, polyglycerin -10 Laurate 9%, Sorbitol 21%, Glycerin 25%, Dipotassium Glycyrrhizinate 0.5%, Cellulose Gum 1.2%, Purified Water 17%.

[0034] The mother-of-pearl powder is powder ground with mother-of-pearl, and the particle size of the mother-of-pearl powder and pearl powder is 200-300 mesh.

[0035] The present invention also provides a preparation process of beneficial health toothpaste, the specific steps are as follows:

[0036] S1. Stir and disperse mother-of-pearl powder, pearl powder, and cellulose gum in glycerin to obtain a mixed solution A;

[0037] S2, add water and sorbitol to A solution while stirring and obtain mixed solution B;

[0038] S3. Put the emulsion B in an emulsification pot and raise the temperature to 80°C and st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses healthcare toothpaste and a preparation process thereof. The healthcare toothpaste comprises the components in%age by weight: 0.1 to 20% of pearl fritillary bulb powder, 0.01 to 20% of pearl powder, 0.03 to 1% of clove oil, 0.1 to 1% of mint leaf oil, 0.05 to 2% of sweet orange oil, 0.1 to 15% of polyglycerol-10 laurate, 10 to 55% of sorbitol, 10 to 50% of glycerol, 0.1 to 1% of dipotassium glycyrrhizinate, 0.1 to 2% of cellulose gum and the balance being purified water. The pearl fritillary bulb powder and the pearl powder are used as abrasives to replace conventional abrasives such as silicon dioxide, calcium oxide and calcium carbonate, possible harm to the body caused by abrasive residues is reduced; in addition, the pearl fritillary bulb powder contains a large amount of amino acid and microelements beneficial to the human body, and is beneficial to human health; the pearl powder contains a large amount of active calcium, and can supplement the daily calcium intake amount of a human body.

Description

technical field [0001] The invention belongs to the technical field of toothpaste, and more specifically relates to a health-enhancing toothpaste and a preparation process thereof. Background technique [0002] The ingredients of toothpaste mainly include abrasives, foaming agents, humectants, thickeners, preservatives, fragrances, sweeteners and water. Abrasives are an essential ingredient in toothpaste formulations, generally accounting for 20-50%. During the use of toothpaste, the abrasive in toothpaste is used to remove dirt and colored substances attached to the tooth surface. Raw materials used as toothpaste friction agents are generally required to have appropriate hardness and friction value, uniform particle size, no peculiar smell, comfortable taste, safe and non-toxic, low solubility and stable chemical properties, and do not chemically react with other components in toothpaste . At present, the commonly used abrasive raw materials are silicon dioxide, aluminum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/98A61Q11/00
CPCA61K8/987A61Q11/00
Inventor 丰小为
Owner 优牌智能科技(上海)有限公司