A kind of mixed diluent and environment-friendly high-penetration epoxy grouting material prepared by using the same and preparation method thereof

A technology of mixing diluents and epoxy grouting, applied in the direction of adhesive types, epoxy resin glue, adhesive additives, etc., can solve the problems of construction personnel and environmental hazards, and achieve easy to master, simple configuration process, and grouting. strong effect

Active Publication Date: 2022-07-08
CHINA INST OF WATER RESOURCES & HYDROPOWER RES +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the problem that the diluent with furfural-acetone as the system in the widely used epoxy resin grouting material formula is easy to cause harm to construction personnel and the environment, the primary purpose of the present invention is to provide a new diluent combination formula, and then use The diluent prepares an environmentally friendly epoxy chemical grouting material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of mixed diluent and environment-friendly high-penetration epoxy grouting material prepared by using the same and preparation method thereof
  • A kind of mixed diluent and environment-friendly high-penetration epoxy grouting material prepared by using the same and preparation method thereof
  • A kind of mixed diluent and environment-friendly high-penetration epoxy grouting material prepared by using the same and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] (1) 100 parts by weight of epoxy resin E-51, 10 parts by weight of hexanediol diglycidyl ether, 90 parts by weight of acetone are mixed to obtain A liquid;

[0038] (2) 10 parts by weight of polyamide, 5 parts by weight of DMP-30, 25 parts by weight of T-31 are mixed to obtain B liquid;

[0039] (3) When using, mix A liquid and B liquid to obtain a high-permeability epoxy grouting material.

Embodiment 2

[0041] (1) 100 parts by weight of epoxy resin E-51, 20 parts by weight of hexanediol diglycidyl ether, 80 parts by weight of acetone are mixed to obtain A liquid;

[0042] (2) 10 parts by weight of polyamide, 5 parts by weight of DMP-30, 25 parts by weight of T-31 are mixed to obtain B liquid;

[0043] (3) When using, mix A liquid and B liquid to obtain a high-permeability epoxy grouting material.

Embodiment 3

[0045] (1) 100 parts by weight of epoxy resin E-51, 30 parts by weight of hexanediol diglycidyl ether, 70 parts by weight of acetone are mixed to obtain A liquid;

[0046] (2) 10 parts by weight of polyamide, 25 parts by weight of T-31 and 5 parts by weight of DMP-30 are mixed to obtain liquid B;

[0047] (3) When using, mix A liquid and B liquid to obtain a high-permeability epoxy grouting material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a mixed diluent, and further prepares a new environment-friendly high-permeability epoxy grouting material. The mixed diluent includes non-reactive diluent and reactive diluent. The environmentally friendly high-penetration epoxy grouting material consists of 100 parts of epoxy resin, 50 to 90 parts of non-reactive diluent, 10 to 50 parts of active diluent, and 12 to 25 parts of curing agent. parts, 10-18 parts of toughening agent, and 5-8 parts of accelerator. The diluents added to the grouting material of the present invention are all non-toxic components, and the viscosity of the epoxy slurry is regulated by adjusting the proportion of the diluent. The epoxy grouting material has low initial viscosity, strong grouting, and controllable gel time. At the same time, the epoxy grouting material consolidated body has excellent mechanical properties; the slurry configuration process is simple, easy to master, and the source of raw materials is wide.

Description

technical field [0001] The invention relates to the technical field of epoxy resin grouting materials, in particular to a mixed diluent and an environment-friendly high-permeability epoxy grouting material prepared by using the same and a preparation method thereof. Background technique [0002] Epoxy grouting material is referred to as epoxy grouting material. It has the advantages of low slurry viscosity, good permeability, good grouting, and excellent mechanical properties of the consolidated body. It has been widely used in foundation reinforcement treatment and concrete crack treatment. . Epoxy slurry is generally composed of two components, A and B, in which component A is the main agent, mainly composed of epoxy resin and diluent, and component B is curing agent, mainly composed of curing agent, toughening agent and accelerator. composition. [0003] At present, the epoxy grout widely used in China mainly uses the furfural-acetone system as the diluent, which can no...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J11/00C09J163/02C09J11/08
CPCC09J11/00C09J163/00C09J11/08C08L77/00Y02W30/91
Inventor 汪文昭赵卫全张金接万晓红周建华李娜王丽娟路威
Owner CHINA INST OF WATER RESOURCES & HYDROPOWER RES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com