Dewdrop dry particles, glaze ink with dewdrop effect, preparation method of glaze ink, rock plate and preparation method of rock plate

A dry-grain glaze and dew-drop technology, applied in the fields of slate and preparation, dew-drop dry-grain, dew-drop effect glaze ink and preparation, can solve the problems of user's aesthetic fatigue, uncontrollable unevenness, serious homogenization, etc. The effect of forming temperature, good surface unevenness, and increasing the firing range

Active Publication Date: 2021-09-07
广东兴辉陶瓷集团有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing antique brick slabs have made some progress in appearance, color, hardness, water absorption, wear resistance and other aspects; but the improvement of performance has led to an increase in the production cost of antique bricks; at the same time, the existing antique bricks In the preparation process of rock slabs, the preparation method is complicated, and the concave-convex feeling of the preparation is uncontrollable, and the concave-convex feeling cannot be designed according to the user's needs. Generally, when the brick body has a concave-convex structure, the brick body is not easy to have gloss. That is, the two requirements of bumpiness and gloss cannot be met at the same time
[0003] Moreover, the existing antique brick and rock slab products have a single effect and serious homogeneity, which causes aesthetic fatigue to users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dewdrop dry particles, glaze ink with dewdrop effect, preparation method of glaze ink, rock plate and preparation method of rock plate
  • Dewdrop dry particles, glaze ink with dewdrop effect, preparation method of glaze ink, rock plate and preparation method of rock plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The dewdrop dry granules, applied on the surface of the slate, include the following components by weight:

[0041] 35~40 parts of nepheline syenite, 8-12 parts of burnt talc, 8-15 parts of calcite, 15-20 parts of zircon, 10-15 parts of quartz, 0-6 parts of barium carbonate, 2-5 parts of calcined alumina , 4-8 parts of air knife soil and 1-5 parts of zinc oxide;

[0042] The chemical composition percentages of dewdrop dry granules are as follows:

[0043] ZrO 2 :3-5%, SiO 2 :55-64%, Al 2 o 3 :8-12%, CaO:10-15%, MgO:3-6%, ZnO:1-5%, BaO:0-6%, K 2 O:3-4%, Na 2 O:3-5%, Fe 2 o 3 : 0-0.1%, B 2 o 3 : 2-5%, loss on ignition 3-5%.

[0044] Nepheline syenite is a solid solution of feldspar and nepheline. The zircon is a silicate mineral, and zircon is widely found in acidic igneous rocks and also in metamorphic rocks and other sediments. Zircon is chemically stable, so gem-quality zircon can also be seen in river gravel. There are many kinds of zircons, and differen...

Embodiment 2

[0052] The difference with embodiment 1 is that the dewdrop dry granules are selected as follows:

[0053] 35-38 parts of nepheline syenite, 10-12 parts of burnt talc, 8-10 parts of calcite, 15-17 parts of zircon, 10-12 parts of quartz, 1-2 parts of barium carbonate, 2-3 parts of calcined alumina , 4-5 parts of air knife soil and 1-3 parts of zinc oxide;

[0054] The chemical composition percentages of dewdrop dry granules are as follows:

[0055] ZrO 2 :4-5%, SiO 2 :58-62%, Al 2 o 3 :8-10%, CaO:10-12%, MgO:3-4%, ZnO:3-5%, BaO:2-3%, K 2 O:3-4%, Na 2 O:3-5%, Fe 2 o 3 : 0-0.1%, B 2 o 3 : 2-5%, loss on ignition 3-5%.

[0056] The dewdrop dry crystals in this example belong to the tetragonal crystal system, the crystals are square short columnar, square biconical, high hardness, diamond luster, high refractive index, strong gloss, high birefringence, high density, high dispersion and typical spectral features, etc.

[0057] Tested by a gloss meter model WGG60-E4, the ...

Embodiment 3

[0059] A dewdrop effect glaze ink,

[0060] Dewdrop effect glaze ink, including the following raw materials by weight:

[0061] Dewdrop dry granule glaze powder 35-55 parts, functional resin 4-8 parts, dispersant 25-45 parts, surfactant 2-4 parts, defoamer 0.2-0.5 parts, suspending agent 0.05-0.12 parts;

[0062] The dewdrop dry glaze powder comprises the following components by weight:

[0063] 35-38 parts of nepheline syenite, 10-12 parts of burnt talc, 8-10 parts of calcite, 15-17 parts of zircon, 10-12 parts of quartz, 1-2 parts of barium carbonate, 2-3 parts of calcined alumina , 4-5 parts of air knife soil and 1-3 parts of zinc oxide.

[0064] The functional resin is a mixture of carboxymethyl cellulose and acrylic resin, and the mass mixing ratio of carboxymethyl cellulose and acrylic resin is 1:1-5.

[0065] The dispersant is polymer polyacrylate emulsion.

[0066] The antifoaming agent is at least one of mineral oil and organic silicon; the suspending agent is cas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glossaaaaaaaaaa
timeaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of rock plate application, and discloses dewdrop dry particles, dewdrop effect glaze ink and a preparation method thereof, and a rock plate and a preparation method thereof. The dewdrop dry particles are applied to the surface of a rock plate and comprise the following components in parts by weight: 35-40 parts of nepheline syenite, 8-12 parts of calcined talc, 8-15 parts of calcite, 15-20 parts of zircon, 10-15 parts of quartz, 0-6 parts of barium carbonate, 2-5 parts of calcined aluminum oxide, 4-8 parts of Qidao soil and 1-5 parts of zinc oxide. By arranging the dewdrop dry particles and the dewdrop effect glaze ink, the high-gloss water drop effect is achieved when the glaze is applied to the rock plate, higher transparency, high temperature resistance, wear resistance and good surface concave-convex feeling are achieved, and the glossiness can reach 80 degrees or above; by introducing nepheline syenite and adjusting the components of SiO2 and Al2O3, the crystal clear effect of the dewdrop dry particles is ensured, the particle effect of the dewdrop can be maintained, the firing temperature is reduced, the firing range is increased, the firing range reaches 1,120-1,200 DEG C, and firing is facilitated.

Description

technical field [0001] The invention relates to the application field of ceramic slabs, in particular to dewdrop dry granules, dewdrop effect glaze ink and a preparation method, slate and a preparation method. Background technique [0002] With the improvement of people's living standards, people's requirements for the environment are also improved, such as the requirements for antique brick and rock panels for decoration. The existing antique brick slabs have made some progress in appearance, color, hardness, water absorption, wear resistance and other aspects; but the improvement of performance has led to an increase in the production cost of antique bricks; at the same time, the existing antique bricks In the preparation process of rock slabs, the preparation method is complicated, and the concave-convex feeling of the preparation is uncontrollable, and the concave-convex feeling cannot be designed according to the user's needs. Generally, when the brick body has a concav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/85C04B41/86C04B41/89
CPCC03C8/00C04B41/5022C04B41/52C04B41/89C04B41/50C04B41/85C04B41/86C04B41/0072
Inventor 母军曾军华何春辉姚向阳马会川袁伟沈盼兵文振鹏
Owner 广东兴辉陶瓷集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com