A CV-LF-RH-CC, nitrogen content technology, applied in the direction of manufacturing converters, etc., can solve the problems of brittle zone change, weakened grain boundary strength, difficult to stably control nitrogen content and alloy composition, etc.

Active Publication Date: 2022-04-05
MAANSHAN IRON & STEEL CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Nitrogen has a great influence on the performance of steel, which is mainly reflected in the following aspects: 1) Nitrogen precipitates at the grain boundary, causing blue brittleness of steel; 2) The existence of nitrogen in steel reduces the impact toughness and welding performance of steel , the toughness of the thermal stress zone, which increases the brittleness of the steel; 3) Nitrogen combines with Ti or Al in the steel to form TiN or AlN, which weakens the grain boundary strength, changes the brittle zone of the steel, and easily causes cracks on the surface of the slab; 4) Continuous The nitrides precipitated in solid solution during the casting process have a more serious impact on the fatigue life of the steel than the deoxidized products of the same size
[0003] Therefore, some high-grade steels have strict requirements on nitrogen content, and changes in nitrogen content will affect the structure and properties of HCM2S steel. When the nitrogen content in HCM2S steel is greater than 71×10 -6 Sometimes it will react with boron to form BN inclusions, which will reduce the amount of "effective boron" in the steel, reduce the hardenability of the steel, and finally affect the structure and performance of the steel, reduce the forming and cold bending properties of the steel, and reduce the toughness and plasticity of the steel
[0004] The stable control of nitrogen content is a difficult problem for steel types that have passed the LF refining process. The refining process is the most serious link in the production process of nitrogen increase. To achieve stable control of nitrogen content and ultra-low nitrogen content, strict control is required from all aspects , and there is no control method for steel types in the CV-LF-RH-CC process route on the market, it is difficult to stably control the nitrogen content and alloy composition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for controlling the nitrogen content of steel grades in the cv-lf-rh-cc process path

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0071] In order to further illustrate the idea of ​​the present invention, the present invention will be further described by taking 300T converter, refining and continuous casting production as examples below.

[0072] (1) Steel type: QStE600TM;

[0073] (2) The composition requirements of QStE600TM steel RH hollow-breaking molten steel, see Table 1 for details:

[0074] Table 1: QStE600TM steel RH broken steel composition requirements

[0075]

[0076] (3) Oxygen blowing volume 0-15% stage, bottom blowing flow rate 0.03Nm 3 / t.min; During the oxygen blowing period of 16-45%, the bottom blowing flow rate is 0.04Nm 3 / t.min; During the oxygen blowing period of 46-70%, the bottom blowing flow rate is 0.06Nm 3 / t.min; Oxygen blowing volume 71-85% stage, bottom blowing flow rate 0.08Nm 3 / t.min; Oxygen blowing volume 86-100% stage, bottom blowing flow rate 0.14Nm 3 / t.min, gas type argon;

[0077] (4) The principle of temperature control at the end of the converter is to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for controlling the nitrogen content of a CV-LF-RH-CC process path steel grade, relates to the technical field of iron and steel metallurgy, and aims to realize the control of the nitrogen content and alloy composition of the CV-LF-RH-CC process path steel grade Stable control; the present invention includes strict control of converter bottom blowing process, tapping alloying process, slag material type and amount added, LF temperature rise, slagging and alloying process bottom blowing, RH refining vacuum degree and time, line feeding speed and In order to realize the stable control of nitrogen content and alloy composition; the present invention can stabilize Make each alloy element reach the target value, and keep the nitrogen content stably controlled below 30ppm.

Description

technical field [0001] The invention relates to the technical field of iron and steel metallurgy, in particular to a method for controlling the nitrogen content of steel grades in a CV-LF-RH-CC process path. Background technique [0002] Nitrogen has a great influence on the performance of steel, which is mainly reflected in the following aspects: 1) Nitrogen precipitates at the grain boundary, causing blue brittleness of steel; 2) The existence of nitrogen in steel reduces the impact toughness and welding performance of steel , the toughness of the thermal stress zone, which increases the brittleness of the steel; 3) Nitrogen combines with Ti or Al in the steel to form TiN or AlN, which weakens the grain boundary strength, changes the brittle zone of the steel, and easily causes cracks on the surface of the slab; 4) Continuous The nitrides precipitated in solid solution during casting have a more serious impact on the fatigue life of steel than the deoxidized products of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C21C5/34C21C7/00C21C7/06C21C7/10C22C33/06
CPCC21C5/34C21C7/0006C21C7/0025C21C7/06C21C7/10C21C7/0056C22C33/06C21C2007/0093
Inventor 胡晓光付尚红李应江邓勇冯胤明熊华报罗霄杨明吴亚男
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products