A technology of weather resistance and soft porcelain, applied in the field of soft porcelain materials with high weather resistance, can solve the problems of easy cracking, corrosion of walls, easy penetration of water vapor, etc., and achieve the effect of water resistance improvement and environmental friendliness

Inactive Publication Date: 2021-09-21
HUBEI YAOMEI FLEXIBLE CERAMICS
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies in the prior art, the present invention provides a soft porcelain material with high weather resistance, which solves the defect of "hot stickiness and cold brittleness" in the soft porcelain existing in the prior art, and the low temperature in winter in the north It is easy to crack in dry conditions, and water vapor easily penetrates into the wall and corrodes the wall in the warm and humid environment in the south

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] In this embodiment, a soft porcelain material with high weather resistance is composed of the following components by weight ratio: 5 parts of Portland cement, 20 parts of heavy calcium, 60 parts of quartz sand, 8 parts of water-based polyurethane modified acrylic emulsion, 3 parts of burning agent and 4 parts of curing agent; among them, decabromodiphenylethane is used as flame retardant, and modified amine epoxy resin curing agent is used as curing agent.

[0025] The specific preparation process of a soft porcelain material with high weather resistance of the above formula is as follows:

[0026] First prepare the raw materials with the following weight ratio: 5 parts of Portland cement, 20 parts of heavy calcium, 60 parts of quartz sand, 8 parts of water-based polyurethane modified acrylic emulsion, 3 parts of flame retardant, and 4 parts of curing agent. Add water of 25% of the dry powder weight to the raw materials while stirring with a mixer until the raw materia...

Embodiment 2

[0028] In this embodiment, a soft porcelain material with high weather resistance is composed of the following components by weight ratio: 5 parts of Portland cement, 30 parts of heavy calcium, 57 parts of quartz sand, 4 parts of water-based polyurethane modified acrylic emulsion, barrier 0.5 parts of the flame retardant, 3.5 parts of the curing agent; wherein the flame retardant uses melamine cyanurate, and the curing agent uses polycarbodiimide curing agent.

[0029] The specific preparation process of a soft porcelain material with high weather resistance of the above formula is as follows:

[0030] First prepare the raw materials with the following weight ratio: 5 parts of Portland cement, 30 parts of heavy calcium, 57 parts of quartz sand, 4 parts of water-based polyurethane modified acrylic emulsion, 0.5 parts of flame retardant, and 3.5 parts of curing agent. Add 20% water of dry powder weight to the raw materials while stirring with a mixer until the raw materials are ...

Embodiment 3

[0032] In this embodiment, a soft porcelain material with high weather resistance is composed of the following components by weight ratio: 8 parts of Portland cement, 17 parts of heavy calcium, 70 parts of quartz sand, 2 parts of water-based polyurethane modified acrylic emulsion, barrier 0.5 parts of the flame retardant, 2.5 parts of the curing agent; wherein the flame retardant uses dimethyl methyl phosphate, and the curing agent uses a non-ionic water-emulsifiable isocyanic acid curing agent.

[0033] The specific preparation process of a soft porcelain material with high weather resistance of the above formula is as follows:

[0034] First prepare the raw materials with the following weight ratio: 8 parts of Portland cement, 17 parts of heavy calcium, 70 parts of quartz sand, 2 parts of water-based polyurethane modified acrylic emulsion, 0.5 parts of flame retardant, and 2.5 parts of curing agent. Add 30% of the dry powder weight water to the raw materials while stirring w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a soft porcelain material with high weather resistance and a preparation method thereof, wherein the soft porcelain material comprises the following raw materials by weight: 5-15 parts of Portland cement, 50-70 parts of quartz sand, 10-30 parts of heavy calcium carbonate, 2-8 parts of a modifier, 0.5-6 parts of a flame retardant, and 2-5 parts of a curing agent. The modifier is waterborne polyurethane modified acrylic emulsion, epoxy resin modified acrylic emulsion or a mixture of the waterborne polyurethane modified acrylic emulsion and the epoxy resin modified acrylic emulsion. The invention provides a preparation method of the soft porcelain, wherein the preparation method comprises the three steps of material preparation, mixing and forming. According to the soft porcelain disclosed by the invention, waterborne polyurethane or epoxy resin is introduced into the acrylic emulsion in a chemical copolymerization manner for modification, and through the interaction of the waterborne polyurethane or epoxy resin and the acrylic emulsion, the generated emulsion comprehensively has excellent performances of acrylic acid and waterborne polyurethane / epoxy resin, and the defect that the acrylic emulsion is sticky in hot and crisp in cold is overcome; and the produced soft porcelain is not easy to break, good in elasticity and excellent in weather resistance.

Description

technical field [0001] The invention relates to the technical field of soft porcelain production, in particular to a soft porcelain material with high weather resistance. Background technique [0002] Soft porcelain is a kind of flexible decorative material. It uses non-metallic industrial tailings, construction waste, stone powder, sand and other materials as the main production materials. Molding technology, shaped under the curve temperature, can vividly express various artistic effects such as bricks, wood, stone, leather, ceramics, braided fabrics and three-dimensional reliefs. The thickness is between 2mm-10mm, and it is flexible and not easy to break. A new type of low-carbon and environmentally friendly green lightweight building decoration material. Because of its light weight, good flexibility, diverse shapes, and good weather resistance, it is widely used in the field of architectural decoration. [0003] At present, soft porcelain on the market often uses acryl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B24/28C04B24/26C04B111/20C04B111/50C04B111/27C04B103/60C04B103/65
CPCC04B28/04C04B24/282C04B24/281C04B24/2641C04B2111/20C04B2111/503C04B2111/27C04B2111/29C04B2103/65C04B2103/60C04B14/06C04B14/28C04B24/005C04B24/12C04B24/128C04B24/003
Inventor 郭中华白晶臣郭和力
Owner HUBEI YAOMEI FLEXIBLE CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap