Bamboo joint earthen pot production process

A production process and technology for casserole, which is applied to other household utensils, clay products, household utensils, etc., can solve the problems of cracking and insufficient durability of casserole, and achieve the effect of long life

Pending Publication Date: 2021-10-12
台宜陶瓷(宜兴)有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a bamboo casserole production process that overcomes the above problems or at least partially solves the above problems, so as to solve the problems that the casserole has insufficient human resistance and cracks in open flames

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The production process of a bamboo casserole provided by the embodiment of the present invention includes the molding process of the casserole and the manufacturing process of the glaze, wherein the percentages of the soil components in the casserole molding process are silicon: 68.8%, aluminum: 26.38%, and iron: 1.5% %, titanium: 1%, calcium: 0.5%, magnesium: 0.08%, potassium 0.34%, sodium: 0.01%, lithium: 1.39%; the specific molding process is as follows:

[0024] Ball milling: clean the ball mill jars, clean the ball millstones and alternately place them in the ball mill jars according to different sizes. The different ball millstones can be divided into large, medium and small ball millstones. The ratio of large, medium and small ball millstones is 1:2:3, and then introduce soil components into the ball mill tank, and then inject 60%-80% of the soil weight. Water is ground in a ball mill with a capacity of 1000KG. The grinding time is 10-20 hours until the distribut...

Embodiment 2

[0034]The difference between embodiment 2 and embodiment 1 lies in the difference of soil and glaze composition content and the difference of ball millstone size.

[0035] A bamboo joint casserole production process, including the molding process of the casserole and the manufacturing process of the glaze, wherein the percentages of soil components in the casserole molding process are silicon: 75.52%, aluminum: 19.59%, iron: 0.66%, titanium: 0.09% , calcium: 0.04%, magnesium: 0.5%, potassium 1%, sodium: 0.1%, lithium: 2.5%; the specific molding process is as follows:

[0036] Ball milling: clean the ball mill jars, clean the ball millstones and alternately place them in the ball mill jars according to different sizes. The different ball millstones can be divided into large, medium and small ball millstones. The ratio of large, medium and small ball millstones is 1:2:3, and then introduce soil components into the ball mill tank, and then inject 60%-80% of the soil weight. Wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a bamboo joint earthen pot production process. The product comprises the following components in percentage by weight: 68.8%-75.52% of silicon, 19.59%-26.38% of aluminum, 0.66%-1.5% of iron, 0.09%-1% of titanium, 0.04%-0.5% of calcium, 0.08%-0.5% of magnesium, 0.34%-1% of potassium, 0.01%-0.1% of sodium and 1.39%-2.5% of lithium. The process comprises the steps of grinding, high-pressure forming, turning table forming, glazing, firing and the like. The components of the earthen pot are limited in a more accurate percentage mode, the earthen pot is integrally fired and formed through combination and arrangement of the production process, different colors are presented in cooperation with glaze, the service life of the earthen pot is longer, the earthen pot is more attractive, and especially the earthen pot cannot be broken when fired on fire at 400 DEG C.

Description

technical field [0001] The invention relates to the technical field of production and processing of ceramic products, in particular to a production process of a bamboo casserole. Background technique [0002] Ceramic products are widely used products in our country. With the development of technology, the process of ceramic production has also undergone major changes. From the previous simple treatment and then firing molding to the present, more attention is paid to the use and method of the product, as well as the appearance of the product. More beautiful and other features go hand in hand. In the past, the front line products were used for tea tableware on the one hand, and on the other hand as cooking utensils fired in an open flame. Now the technology is not only to fire ceramic products in an open flame, but also to use Microwave and electromagnetic heating methods, different heating methods adopt different principles and have different effects on ceramics and durabili...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B33/34C04B33/13C04B33/04C04B41/86
CPCC03C8/00C04B33/13C04B33/04C04B33/34C04B41/86C04B41/5022C04B2235/6567
Inventor 陈建宏
Owner 台宜陶瓷(宜兴)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com