A technology of solder paste and stainless steel, applied in the direction of welding/welding/cutting items, welding medium, welding equipment, etc., can solve the problems that the high-temperature oxidation of the welded parts cannot be effectively prevented, the solder paste does not have the function of heating, and is prone to cracks, etc. To achieve the effect of prolonging the service life, good adhesion and avoiding high temperature oxidation
Pending Publication Date: 2021-10-29
烟台艾邦电子材料有限公司
View PDF1 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] However, the existing special solder paste for welding stainless steel, in the process of use, due to the high hardenability of stainless steel after welding, it is easy to produce cracks, so it is necessary to preheat the welded parts, but the existing solder paste does not have the function of heating , need to use additional equipment for preheating, and at the same time, the existing tin solder paste, in the process of welding, directly cleans the surface of the weldment, and is prone to high-temperature oxidation when welding stainless steel, which cannot effectively prevent the high-temperature oxidation of the weldment
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0046]The solder paste material includes the following raw materials and their weight fractions: 35 parts of alloy powder, 10 parts of flux, 10 parts of silicate solution, 5 parts of ultrafine inorganic metal oxide, 7 parts of tetrachloroethylene solvent, self-heating 20 doses;
[0047] The self-heating agent is composed of the following weight proportions: 40 parts of iron powder, 10 parts of wood powder, 5 parts of activated carbon, 5 parts of table salt and 10 parts of water.
Embodiment 2
[0049] The solder paste material includes the following raw materials and their weight fractions: 36 parts of alloy powder, 12 parts of flux, 14 parts of silicate solution, 6 parts of ultrafine inorganic metal oxide, 9 parts of tetrachloroethylene solvent, self-heating 21 doses;
[0050] The self-heating agent is composed of the following weight proportions: 42 parts of iron powder, 12 parts of wood powder, 6 parts of activated carbon, 7 parts of table salt and 13 parts of water.
Embodiment 3
[0052] The solder paste material includes the following raw materials and their weight fractions: 37 parts of alloy powder, 13 parts of flux, 14 parts of silicate solution, 7 parts of ultrafine inorganic metal oxide, 10 parts of tetrachloroethylene solvent, self-heating 23 doses;
[0053] The self-heating agent is composed of the following weight proportions: 44 parts of iron powder, 14 parts of wood powder, 7 parts of activated carbon, 10 parts of table salt and 15 parts of water.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the technical field of stainless steel welding, and discloses special tin soldering paste for weldable stainless steel. The special tin soldering paste comprises 35-50 parts of alloy powder, 10-20 parts of soldering flux, 10-20 parts of a silicate solution, 5-10 parts of ultramicro inorganic metal oxide, 7-15 parts of tetrachloroethylene solvent and 20-30 parts of a self-heating agent. The self-heating agent is prepared from, by weight, 40-50 parts of iron powder, 10-20 parts of wood flour, 5-10 parts of activated carbon, 5-15 parts of salt and 10-20 parts of water. By adding the self-heating agent, after the tin soldering paste is extruded, the tin soldering paste makes contact with outside air, heat released by rapid reaction of iron powder and oxygen in the air is reduced, the heat release amount is larger than the heat dissipation amount, temperature rise is caused, various solid powder particles are evenly mixed and dispersed through the water and the wood flour, and a contact surface for gas-solid two-phase reaction is provided. The iron powder can react completely, the heat capacity of the formula is improved, the surface of a welding part can be preheated in the using process of the tin soldering paste, and cracks are relieved.
Description
technical field [0001] The invention relates to the technical field of stainless steel welding, in particular to a special solder paste for welding stainless steel. Background technique [0002] Tin solder paste is widely used in high-precision electronic components. On the one hand, tin solder paste can isolate electronic components from the air, thereby preventing the components from being oxidized. On the other hand, it can ensure the soldering performance of electronic components. , to achieve high resistance and prevent the phenomenon of virtual soldering. With the continuous development of electronic technology, people put forward higher and higher requirements for the welding quality of electronic products. The quality of solder paste has a great influence on the quality of soldering. High-quality solder paste can effectively ensure the quality of soldering. In the assembly and welding of electronic industrial products, tin-lead (Sn-Pb) alloy solder has been used all...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more