Metal phosphide and metal phosphate composite modified ternary positive electrode material precursor
A technology of metal phosphate and metal phosphide, which is applied in the direction of phosphide, phosphorus compound, non-metallic elements, etc., can solve the problems of poor electrical conductivity, achieve low cost, improve structural stability and rate performance, and be easy to realize Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0031] In this example, metal phosphide and metal phosphate compound modified ternary cathode material precursor is ZnP 2 and ZnMn 2 (PO 4 ) 2 Composite Modified Ni 0.5 co 0.2 mn 0.3 O ternary cathode material precursor, the chemical formula can be written as: ZnP 2 / ZnMn 2 (PO 4 ) 2 @Ni 0.5 co 0.2 mn 0.3 O.
[0032] The preparation method of the composite modified ternary precursor of metal phosphide and metal phosphate in this example is as follows:
[0033] Take 0.1mol ternary cathode material precursor Ni 0.5 co 0.2 mn 0.3 (OH) 2 Disperse in 20 mL of water, add 2 mmol Zn(NO 3 ) 2 and 2 mmol Mn(NO 3 ) 2 After dissolving, add 2 mmol diammonium hydrogen phosphate and 0.05 g complexing agent PVP, stir at 30°C for 5 hours, filter, dry, and calcinate at 700°C for 4 hours under nitrogen atmosphere to obtain metal phosphide and metal phosphate compound Modified ternary precursor ZnP 2 / ZnMn 2 (PO 4 ) 2 @Ni 0.5 co 0.2 mn 0.3 O.
[0034] The ternary cath...
Embodiment 2
[0053] In this example, metal phosphide and metal phosphate compound modified ternary cathode material precursor is ZnP 2 and Zn 2 Co(PO 4 ) 2 Composite Modified Ni 0.5 co 0.2 mn 0.3 O ternary cathode material precursor, the chemical formula can be written as: ZnP 2 / Zn 2 Co(PO 4 ) 2 @Ni 0.5 co 0.2 mn 0.3 O.
[0054] The preparation method of the composite modified ternary precursor of metal phosphide and metal phosphate in this example is as follows:
[0055] Take 0.1mol ternary cathode material precursor Ni 0.5 co 0.2 mn 0.3 (OH) 2 Disperse in 20 mL of water, add 2.5 mmol Zn(NO 3 ) 2 and 1 mmol Co(NO 3 ) 2 After dissolving, add 2 mmol of diammonium hydrogen phosphate and 0.05 g of complexing agent PVP, stir at 30°C for 5 hours, filter, dry, and calcinate at 700°C for 4 hours under nitrogen atmosphere to obtain metal phosphide and metal phosphate compound modification Sexual ternary precursor ZnP 2 / Zn 2 Co(PO 4 ) 2 @Ni 0.5 co 0.2 mn 0.3 O.
[005...
Embodiment 3
[0061] In this example, the precursor of the metal phosphide and metal phosphate composite modified ternary positive electrode material is Ca 3 P 2 and Ca 2 Co(PO 4 ) 2 Composite Modified Ni 0.6 co 0.2 mn 0.2 O ternary cathode material precursor, the chemical formula can be written as: Ca 3 P 2 / Ca 2 Co(PO 4 ) 2 @Ni 0.6 co 0.2 mn 0.2 O.
[0062] The preparation method of the composite modified ternary precursor of metal phosphide and metal phosphate in this example is as follows:
[0063] Take 0.1mol ternary cathode material precursor Ni 0.6 co 0.2 mn 0.2 (OH) 2 Disperse in 20 mL of water, add 2.5 mmol Ca(NO 3 ) 2 and 1 mmol Co(NO 3 ) 2 After dissolving, add 2 mmol diammonium hydrogen phosphate and 0.05 g complexing agent PVP, stir at 30°C for 5 hours, filter, dry, and calcinate at 750°C for 6 hours under nitrogen atmosphere to obtain metal phosphide and metal phosphate compound modification sex ternary precursor Ca 3 P 2 / Ca 2 Co(PO 4 ) 2 @Ni 0.6 ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com