Macromolecular self-adhesive film waterproof coiled material and preparation method thereof

A waterproof membrane and self-adhesive film technology, applied in the direction of polymer adhesive additives, non-polymer adhesive additives, adhesives, etc., can solve the problem of affecting the quality and efficiency of building waterproof construction and restricting the development of building waterproof membranes , unable to meet the waterproof requirements and other problems, to achieve the effect of reducing emissions and fire risks, reducing water channeling, and convenient construction

Pending Publication Date: 2021-12-17
建国伟业防水科技望都有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the commonly used waterproof membrane for construction is SBS waterproof membrane, and the construction of SBS waterproof membrane is also a common waterproof method in current construction projects. The introduction of SBS has given new vitality to the domestic waterproof market, but with the development of the times, SBS waterproof membrane construction has been unable to meet the waterproof needs of current buildings
[0003] As far as the current actual situation of SBS waterproof membrane construction is concerned, when the waterproof layer is damaged, groundwater will flow between the waterproof layer and the building structure layer. The building structure layer is generally made by pouring concrete, because concrete is porous. Inhomogeneous materials, during the pouring process, there will be defects such as honeycomb holes caused by inaccurate vibration, concrete reserved gaps (construction joints, deformation joints, etc.) caused by objective factors, and structural cracks caused by uneven settlement of the foundation. The water channeling between the waterproof layer and the structural layer will enter the structure along the cracks, holes and other defects in the concrete, resulting in water channeling, which will lead to building leakage, which will easily affect the quality and efficiency of building waterproofing construction, and restrict It hinders the development of building waterproof membrane and needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] This application discloses a polymer self-adhesive film waterproof coiled material, which successively includes a base layer, a self-adhesive layer and an anti-bonding layer. The base layer has the following raw materials: linear low-density polyethylene, and the self-adhesive layer has the following materials: SBS Resin, tackifying resin, softener, 4,4-dicarboxydiphenylethylene, antioxidant, initiator, wherein, tackifying resin adopts terpene resin, anti-adhesion layer is PVC film, and the content of each component is as follows Table 1-1 shows.

[0050] The preparation method of polymer self-adhesive film waterproof membrane comprises the following steps:

[0051] S1. Preparation of raw materials for the self-adhesive layer: Stir the SBS resin, 4,4-dicarboxydiphenylethylene and the initiator at 150°C for 1.5h, then cool down to 110°C, add softener and stir to mix, then Add tackifying resin and antioxidant while stirring, and stir at constant temperature for 2 hours t...

Embodiment 2

[0054] This application discloses a polymer self-adhesive film waterproof coiled material, which successively includes a base layer, a self-adhesive layer and an anti-bonding layer. The base layer has the following raw materials: linear low-density polyethylene, and the self-adhesive layer has the following materials: SBS Resin, tackifying resin, softener, 4,4-dicarboxydiphenylethylene, antioxidant, initiator, wherein, tackifying resin adopts terpene resin, anti-adhesion layer is PVC film, and the content of each component is as follows Table 1-1 shows.

[0055] The preparation method of polymer self-adhesive film waterproof membrane comprises the following steps:

[0056] S1. Preparation of raw materials for the self-adhesive layer: Stir the SBS resin, 4,4-dicarboxydiphenylethylene and the initiator at 160°C for 1 hour, then cool down to 120°C, add the softener and stir well, then Add tackifying resin and antioxidant while stirring, and stir at constant temperature for 1 hou...

Embodiment 3

[0059] This application discloses a polymer self-adhesive film waterproof coiled material, which successively includes a base layer, a self-adhesive layer and an anti-bonding layer. The base layer has the following raw materials: linear low-density polyethylene, and the self-adhesive layer has the following materials: SBS Resin, tackifying resin, softener, 4,4-dicarboxydiphenylethylene, antioxidant, initiator, wherein, tackifying resin adopts terpene resin, anti-adhesion layer is PVC film, and the content of each component is as follows Table 1-1 shows.

[0060] The preparation method of polymer self-adhesive film waterproof membrane comprises the following steps:

[0061] S1. Preparation of raw materials for the self-adhesive layer: Stir the SBS resin, 4,4-dicarboxydiphenylethylene and the initiator at 155°C for 1.5h, then lower the temperature to 115°C, add the softener and stir well, then Add tackifying resin and antioxidant while stirring, and stir at constant temperature...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of waterproof materials for buildings, and particularly discloses a macromolecular self-adhesive film waterproof coiled material and a preparation method thereof. The macromolecular self-adhesive film waterproof coiled material sequentially comprises a base layer, a self-adhesive layer and an anti-adhesive layer, wherein the self-adhesive layer comprises the following raw materials: an SBS resin, a tackifying resin, a softener, 4, 4-dicarboxyl diphenylethylene, an antioxidant and an initiator. The preparation method comprises the following steps: S1, preparing raw materials of an self-adhesive layer; and S2, preparing a waterproof coiled material. According to the invention, 4, 4-dicarboxyl diphenylethylene and an initiator are adopted to initiate an SBS resin macromolecular chain to generate chain free radicals, the chain free radicals react with the 4, 4-dicarboxyl diphenylethylene to generate a graft polymer, the carboxyl in the graft polymer can chemically react with calcium hydroxide in building concrete, and the carboxyl and calcium hydroxide are combined through chemical bonds, so that the bonding tightness between the waterproof coiled material and a building is improved, skin type waterproofing is formed, and the water channeling phenomenon can be reduced when the waterproof coiled material is locally damaged.

Description

technical field [0001] The application relates to the field of waterproof materials for construction, more specifically, it relates to a polymer self-adhesive film waterproof roll and a preparation method thereof. Background technique [0002] Since the reform and opening up, my country's construction industry has developed rapidly, and accordingly, the requirements for waterproofing of buildings have become higher and higher. At present, the commonly used waterproof membrane for construction is SBS waterproof membrane, and the construction of SBS waterproof membrane is also a common waterproof method in current construction projects. The introduction of SBS has given new vitality to the domestic waterproof market, but with the development of the times, The construction of SBS waterproof membrane has been unable to meet the waterproof needs of current buildings. [0003] As far as the current actual situation of SBS waterproof membrane construction is concerned, when the wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/24C09J7/30C09J151/00C09J11/04C09J11/06C09J11/08C08F287/00C08F212/32C08L23/08C08L23/06
CPCC09J7/243C09J7/30C09J151/006C09J11/04C09J11/06C09J11/08C08F287/00C08L23/0815C09J2203/346C08L2207/062C09J2423/046C09J2423/04C09J2301/122C08F212/32C08L23/06C08L23/22C08K5/32C08K5/1539C08K3/12
Inventor 李勇范增昌冯庆伟
Owner 建国伟业防水科技望都有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products