Manufacturing process for enterprise logo on brown electro-technical ceramic product

A technology of enterprise logo and production process, which is applied in the direction of signs, instruments, display devices, etc., can solve the problems of logo clarity that needs to be improved, easy to fall off or missing, poor bonding force, etc., to improve trademark clarity, improve adhesion and Lubrication, the effect of improving the binding force

Pending Publication Date: 2022-01-04
CHONGQING PIGEON ELECTRIC PORCELAIN CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When the existing brown glaze trademark glaze is used to glaze the brown glaze porcelain insulator glaze, the bonding force between the brown glaze trademark glaze and the brown glaze is poor, and it is easy to fall off or be missing. The clarity of the logo needs to be improved, and the logo has light color and fusing Phenomenon

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The manufacturing process of the electric porcelain brown product enterprise logo that the present invention proposes comprises the following steps:

[0015] S1. Prepare the following raw materials in proportion: zirconium dioxide 4 / 15, Dongsheng soil 1 / 15, 2% sodium carboxymethyl cellulose solution 5 / 15 and glycerol 5 / 15. Dongsheng soil is a highly plastic clay. The average binding force is about 5.0MPa, which plays a decisive role in improving the dry bending strength of the green body;

[0016] Brown glaze trademark glaze formula ratio table (%):

[0017] zirconium dioxide Dongsheng soil 2% sodium carboxymethylcellulose solution Glycerol 80 20 100 (plus) 100 (plus)

[0018] Dongsheng soil chemical composition table (%):

[0019] SiO 2

Al 2 o 3

Fe 2 o 3

TiO 2

CaO MgO K 2 o

Na 2 o

other 61.90 22.40 1.53 1.20 0.56 0.30 1.58 0.29 10.24

[0020] S2. In the parallel bar bal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of glaze, in particular to a manufacturing process for an enterprise logo on a brown electro-technical ceramic product. The manufacturing process comprises the following steps: S1, preparing raw materials in proportion, namely preparing 4/15 of zirconium dioxide, 1/15 of Dongsheng soil, 5/15 of a sodium carboxymethyl cellulose solution with a concentration of 2% and 5/15 of glycerol; S2, in a parallel-bar ball mill, matching raw materials and water according to a ratio of the raw materials to balls to water of 1: 2: 1.2, conducting ball milling treatment to obtain a semi-finished product of a brown-glaze trademark glaze; S3, carrying out sieving treatment on the ball-milled semi-finished product of the brown-glaze trademark glaze; and S4, drying the sieved semi-finished product of the brown-glaze trademark glaze to obtain a finished brown-glaze trademark glaze product. According to the invention, the Dongsheng soil is adopted, so formula cost is reduced, and the binding force of the brown-glaze trademark glaze is improved. According to the invention, a large amount of zirconium dioxide is adopted, so the brown-glaze trademark glaze has good white color and refractoriness. The binding force between the brown-glaze trademark glaze and a brown glaze is improved, the brown-glaze trademark glaze is not easy to fall off or lose, the logo is clear, and the brown-glaze trademark glaze is white, colorless or edge-fused.

Description

technical field [0001] The invention relates to the field of glazes, in particular to a manufacturing process of an electric porcelain brown product enterprise logo. Background technique [0002] Electrical ceramics are referred to as electrical ceramics, and electrical ceramics cover a variety of electrical ceramic products, including insulating ceramics, semiconductor ceramics, and so on. Porcelain insulators in power industry systems include various line insulators and insulators for power station appliances, as well as other insulation components for isolation or support of charged bodies. The surface of the existing electric porcelain is usually coated with electric enamel, and the electric enamel refers to the glaze applied on the surface of the body of the electric porcelain product. [0003] When the existing brown glaze trademark glaze is used to glaze the brown glaze porcelain insulator glaze, the bonding force between the brown glaze trademark glaze and the brown...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20G09F7/00G09F7/16
CPCC03C8/20G09F7/00G09F7/16
Inventor 姚绍明张正波苏飞邓小玲唐婷婷毕瑞麟
Owner CHONGQING PIGEON ELECTRIC PORCELAIN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap