High-quality low-oxygen copper rod and preparation method thereof

A low-oxygen copper, high-quality technology, applied in the direction of cable/conductor manufacturing, process efficiency improvement, root rod/rod/wire/strip conductor, etc., can solve the problem that the copper rod cannot be connected stably and effectively, and affects the normal use of the copper rod , poor performance of copper rods, etc., to achieve the effect of increased connection surface, improved stability, and improved recycling rate

Pending Publication Date: 2022-01-14
天大铜业(天长)有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is aimed at the problems existing in the background technology: the contact surface of the connecting end of the existing copper rod is single, and the copper rod cannot be connected stably and effectively, so there will be a situation where the joint is detached, which will affect the normal use of the copper rod; The quality of waste miscellaneous copper treatment is low, so the performance of the prepared copper rod is also relatively poor. A high-quality low-oxygen copper rod and its preparation method are proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-quality low-oxygen copper rod and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] like figure 1 As shown, a high-quality low-oxygen copper rod proposed by the present invention includes a copper rod body 1, a connecting groove 11 is provided on the central axis of one end of the copper rod body 1, and a connecting column 12 is provided at one end of the copper rod body 1; 12 is a quarter arc groove; the diameter of the copper rod body 1 is 8mm, and the diameter of the connecting column 12 is 3mm.

[0032] In this embodiment, a method for preparing a high-quality low-oxygen copper rod is also proposed, comprising the following steps:

[0033] Step 1: raw material processing;

[0034] Selection of raw materials: Raw materials include 20 parts of first-class scrap copper with copper content above 99.8%, 15 parts of second-class scrap copper with copper content of 98.8%-99.8%, 65 parts of third-class scrap copper with copper content of 95%-98.8% share;

[0035] Feeding and melting: Add the selected raw materials into the reverberatory furnace, heat up...

Embodiment 2

[0045] like figure 1 As shown, a high-quality low-oxygen copper rod proposed by the present invention, compared with Embodiment 1, this embodiment also includes a copper rod body 1, a connecting groove 11 is provided on the central axis of one end of the copper rod body 1, and the copper rod body One end of 1 is provided with a connecting column 12; the connecting column 12 is a quarter arc groove; the diameter of the copper rod body 1 is 8mm, and the diameter of the connecting column 12 is 3mm.

[0046] In this embodiment, a method for preparing a high-quality low-oxygen copper rod is also proposed, comprising the following steps:

[0047] Step 1: raw material processing;

[0048] Selection of raw materials: raw materials include 30 parts of first-class scrap copper with copper content above 99.8%, 20 parts of second-class scrap copper with copper content of 98.8%-99.8%, and 50 parts of third-class scrap copper with copper content of 95%-98.8% share;

[0049]Feeding and me...

Embodiment 3

[0059] like figure 1 As shown, a high-quality low-oxygen copper rod proposed by the present invention, compared with Embodiment 1 or Embodiment 2, this embodiment also includes a copper rod body 1, and the central axis of one end of the copper rod body 1 is provided with a connecting groove 11 One end of the copper rod body 1 is provided with a connecting column 12; the connecting column 12 is a quarter circular groove; the diameter of the copper rod body 1 is 8mm, and the diameter of the connecting column 12 is 3mm.

[0060] In this embodiment, a method for preparing a high-quality low-oxygen copper rod is also proposed, comprising the following steps:

[0061] Step 1: raw material processing;

[0062] Selection of raw materials: raw materials include 40 parts of first-class scrap copper with copper content above 99.8%, 25 parts of second-class scrap copper with copper content of 98.8%-99.8%, 35 parts of third-class scrap copper with copper content of 95%-98.8% share;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of copper rod preparation and relates to a high-quality low-oxygen copper rod and a preparation method thereof. The invention mainly aims at the problems that an existing copper rod is poor in connection stability, complex in preparation process, high in cost, low in quality and the like. According to the technical schemes, the high-quality low-oxygen copper rod includes a copper rod body, a connecting groove is formed in a center shaft at one end of the copper rod body, and a connecting column is arranged at one end of the copper rod body. The invention further provides a preparation method of the high-quality low-oxygen copper rod. The preparation method comprises the following steps that: 1, raw materials are treated; 2, c copper liquid is casted and crystallized; 3,machining a copper casting blank; and 4, a low-oxygen copper rod is obtained. According to the prepared low-oxygen copper rod connector, the connecting face is enlarged, the connecting stability of the copper rod is improved, the conductivity and tensile strength of the low-oxygen copper rod are improved, the oxygen content in the copper rod is reduced, the tensile strength and the conductivity of the low-oxygen copper rod are improved, waste copper is utilized, the production cost is reduced, resources are saved, and the low-oxygen copper rod is suitable for application and popularization.

Description

technical field [0001] The invention relates to the technical field of copper rod preparation, in particular to a high-quality low-oxygen copper rod and a preparation method thereof. Background technique [0002] Low-oxygen copper rods refer to copper rods with an oxygen content of 200 (175)-400 (450) ppm. Generally, when drawing copper wires with a diameter > 1mm, the advantages of low-oxygen copper rods are more obvious. With the development of the electrical industry, the demand for materials such as cables and wires and the purity requirements are getting higher and higher. Low-oxygen / oxygen-free copper rods are widely used to guide electrical cables, especially low-oxygen copper rods with a diameter of 8mm. Its high purity, low oxygen content, and less impurities are favored by the market. The production of existing low-oxygen copper rods mainly adopts the continuous casting and rolling process. After the raw copper is melted, oxidized, reduced, and copper is produc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01B5/02H01B13/00C22B15/04C22B15/00
CPCH01B5/02H01B13/00C22B15/0036C22B15/0056C22B15/006Y02P10/20
Inventor 李长江吕诗伟陈东
Owner 天大铜业(天长)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap