Hidden hollowed-out aluminum plating pattern holographic anti-counterfeiting adhesive tape and manufacturing method thereof
A technology of holographic anti-counterfeiting and production method, which is applied in the field of hidden hollow-out aluminum-plating pattern holographic anti-counterfeiting tape and its production, can solve the problems of design and production troubles, cost loss, weakening of anti-counterfeiting characteristics of refined hollow-aluminum plating technology, etc. The effect of stable quality, improved adhesion and tightness, and improved anti-counterfeiting performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0055] Example 1
[0056] 1) selection of BOPET film as a base film layer;
[0057] 2) coating the back surface of the base film layer a silicone release agent as a release layer 8;
[0058] 3) coated on the base film layer coating the platen 2, and drying;
[0059] Embossed thermoplastic acrylic resin coating 2 is a composite coating, dry coating amount of 1.0g / m 2 , The drying temperature is 100-130 deg.] C (oven five groups, temperature was set to: 100 ℃, 110 ℃, 130 ℃, 120 ℃, 100 ℃), drying time of 8s.
[0060] 4) The holographic information layer 3 is formed on the embossed hologram layer 2 imprint pattern information;
[0061] 5) the information printed on the hologram layer 3 with printing roll perfluoropolyether layer 9 as a shielding layer, the shielding portion 9 covers the aluminum layer holographic information layer 3, and then dried instant shield layer 9, the holographic information layer 3 the non-printed portion of the shielding layer 9 of the first aluminum layer...
Example Embodiment
[0073] Example 2
[0074] 1) selection of a BOPP film as a base film layer;
[0075] 2) a non-silicone-coated back surface of the base film 1 as a release agent from the layer 8;
[0076] 3) on the base film layer is coated in a coating nip 2, and drying;
[0077] Embossed thermoplastic acrylic resin coating 2 is a composite coating, dry coating amount of 1.2g / m 2 , The drying temperature is 100-130 deg.] C (oven five groups, temperature was set to: 100 ℃, 110 ℃, 130 ℃, 120 ℃, 100 ℃), drying time was 10s.
[0078] 4) The holographic information layer 3 is formed on the embossed hologram layer 2 imprint pattern information;
[0079] 5) the information printed on the hologram layer 3 with printing roll perfluoropolyether layer 9 as a shielding layer, the shielding portion 9 covers the aluminum layer holographic information layer 3, and then dried instant shield layer 9, the holographic information layer 3 the non-printed portion of the shielding layer 9 of the first aluminum layer...
Example Embodiment
[0088] Example 3
[0089] 1) selection of a BOPP film as a base film layer;
[0090] 2) a non-silicone-coated back surface of the base film 1 as a release agent from the layer 8;
[0091] 3) on the base film layer is coated in a coating nip 2, and drying;
[0092] 2 is a platen cellulose acetate coating impression transfer coating, dry coating amount of 1.0g / m 2 Drying temperature of 80-110 deg.] C (oven five groups, temperature was set to: 80 ℃, 90 ℃, 110 ℃, 100 ℃, 90 ℃), drying time of 8s.
[0093] 4) The holographic information layer 3 is formed on the embossed hologram layer 2 imprint pattern information;
[0094] 5) the information printed on the hologram layer 3 with printing roll perfluoropolyether layer 9 as a shielding layer, the shielding portion 9 covers the aluminum layer holographic information layer 3, and then dried instant shield layer 9, the holographic information layer 3 the non-printed portion of the shielding layer 9 of the first aluminum layer 4 is formed o...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap