High-temperature-resistant powder coating
A technology of powder coating and high temperature resistance, which is applied in the direction of powder coating, anti-corrosion coating, fire-proof coating, etc. It can solve the problems of general heat resistance, difficulty of powder spraying in the preparation process, and poor fluidity of powder coating, so as to achieve the improvement of acid and alkali corrosion resistance , facilitate equipment layout, increase the effect of adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0034] Example 1:
[0035] High temperature resistant powder coating, including the following weight ratio ingredients: modified resin 400-600, cross-linkage curing agent 20-30, mica powder 100-200, talc powder 150-250, hollow fine powder 100-200, defoamer 1 -9, graft 1-9, high temperature pigment 20-30, other auxiliaries 1-3.
[0036] The talc is a fine grade, a particle size of 4.5-5.5 μm, and the mica powder is a white-female powder having a particle diameter of 15-17 μm.
[0037] With the modified resin as the main filler, the mica powder, talc powder is added, and the heat resistance and adhesion performance, while the use of auxiliaries, leveling agents, cross-linkage curing agents can be guaranteed. The reliable production of coatings is carried out to ensure the quality of the preparation. On the basis of the above-mentioned hollow fine powder, the flow performance of the coating is increased, thereby reducing the molten extrusion during the preparation and the difficulty ...
Example Embodiment
[0038] Example 2:
[0039] High temperature resistant powder coating, including the following weight ratio ingredients: modified resin 400-600, cross-linkage curing agent 20-30, mica powder 100-200, talc powder 150-250, hollow fine powder 100-200, defoamer 1 -9, leveling agent 1-9, high temperature pigment 20-30, other auxiliaries 1-3, modified silicon carbide 5-7, modified silica sol 20-30.
[0040] The talc is a fine grade, a particle size of 4.5-5.5 μm, and the mica powder is a white-female powder having a particle diameter of 15-17 μm.
[0041] On the basis of Example 1, the modified silicon carbide and modified silica sol were increased, but also increased significantly on the acid-resistant corrosion resistance of powder coatings, but also increased the adhesion of the powder coating.
Example Embodiment
[0042] Example 3:
[0043] A high temperature resistant powder coating comprising the following weight ratio component: modified resin 450-550, cross-linkage curing agent 22-28, mica powder 120-180, talc powder 180-220, hollow micro powder 120-180, defoamer 3 -7, level 3-7, high temperature pigment 20-30, other auxiliaries 1-3, modified silicon carbide 6, modified silicon sol 15.
[0044] The talc is a fine grade, a particle size of 4.5-5.5 μm, and the mica powder is a white-female powder having a particle diameter of 15-17 μm.
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap